Light and thin roving high-count flat-coated tweed and production process
A woolen tweed and high-count technology, applied in the textile field, can solve problems such as unsatisfactory evenness of woolen high-count wool yarn, fiber cohesion, antistatic property, poor hand feeling, overall thick fabric, etc., to achieve full hand feeling, fiber Good cohesion and antistatic properties, light and soft fabric
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0021] The tweed is a twill weave fabric with 2 / 2 as the basic weave.
[0022] In this embodiment, it is necessary to change the heavy feeling of the traditional roving fabric to make the roving fabric light, thin and supple, and the yarn count of the roving yarn must be increased. Single weft production process.
[0023] In this embodiment, the warp and weft raw materials are selected by mixing fine wool fibers and polyester fibers, and their weight percentages are respectively 70% of fine wool fibers and 30% of polyester fibers.
[0024] The production process of woolen high-count, light, thin, and smooth woolen tweed includes the following process steps:
[0025] The first step: preparation of raw materials, including the raw materials for spinning woolen high-count, light and thin tweed fabrics: the warp and weft raw materials are the same, including 70% fine wool fiber, 30% polyester fiber, after weighing the above fibers All dyed.
[0026] The dyeing adopts loose wool...
Embodiment 2
[0048] The difference between embodiment 2 and the process parameters of the embodiment is: the selection of raw materials for warp and weft yarns is formed by mixing fine wool fibers and polyester fibers, and the weight percentages are respectively 75% of fine wool fibers and 25% of polyester fibers; wool dyeing Temperature 90℃, time 55min, polyester fiber dyeing temperature 130℃, time 55min; control relative humidity 55%~60% in spinning process, temperature 25℃~30℃; shredder working solution temperature 35~40℃, time 80min. The needle roller is fluffed 6 times, the thorn fruit is fluffed with a humidity of 90%, and the front is 8 times.
Embodiment 3
[0050] The difference between the process parameters of Example 3 and Example 3 is that the raw materials of warp and weft are mixed with fine wool fiber and polyester fiber, and the weight percentages are respectively 65% of fine wool fiber and 35% of polyester fiber. The wool dyeing temperature is 100℃, the time is 60min, the polyester fiber dyeing temperature is 140℃, and the time is 60min; in the spinning process, the relative humidity is controlled at 60%~65%, and the temperature is 25℃~30℃; , time 100min. The needle roller is fluffed 10 times, the thorn fruit is fluffed with a humidity of 80%, and the front is 10 times.
PUM
Property | Measurement | Unit |
---|---|---|
Breaking strength | aaaaa | aaaaa |
Tear strength | aaaaa | aaaaa |
Breaking strength | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information

- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com