Low-bounce ice-cold breathable sponge and preparing process thereof

A low-rebound, cold technology, applied in the field of sponge processing and preparation, can solve problems such as temperature rise, affecting human comfort, and sponges are easy to absorb heat, etc., to achieve good low resilience, facilitate large-scale production, and simple and efficient preparation process Effect

Active Publication Date: 2014-11-12
良眠家居科技江苏有限公司
View PDF1 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] Aiming at the deficiencies in the above-mentioned prior art, the present invention provides a low-rebound ice-cold breathable sponge, which has good low-rebound elasticity, breathable moisture permeability and excellent mechanical properties, and also has a cold effect, overcoming Solve the problem that the existing sponge is easy to absorb heat and cause the temperature to rise and affect the comfort of the human body

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Low-bounce ice-cold breathable sponge and preparing process thereof
  • Low-bounce ice-cold breathable sponge and preparing process thereof
  • Low-bounce ice-cold breathable sponge and preparing process thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0030] Take the following components by weight, and use raw material tanks for batching: 90 parts of polyether polyol with a hydroxyl value of 230-306, 50 parts of isocyanate TDI80, 0.1 part of amine catalyst A33, and 0.3 parts of tin catalyst T9 1 part of silicone oil, 3 parts of sodium tetraborate, and 1 part of zinc oxide powder. The above-mentioned components are prepared in a raw material tank and then sent to the reaction kettle for mixing. The stirring speed is 3000r / min and the temperature is 21°C. Then the stirred mixture is sent to the foaming box for aging and film removal. 100s, process and cut the sponge obtained after aging and stripping into finished products.

Embodiment 2

[0032] Take the following components by weight, and use raw material tanks for batching: 110 parts of polyether polyols with a hydroxyl value of 230-306, 30 parts of isocyanate TDI80, 0.3 parts of amine catalyst A33, and 0.1 parts of tin catalyst T9 3 parts of silicone oil, 1 part of sodium tetraborate, and 3 parts of zinc oxide powder. The above-mentioned components are prepared in a raw material tank and then sent to the reaction kettle for mixing. The stirring speed is 5000r / min and the temperature is 23°C. Then the stirred mixture is sent to the foaming box for aging and stripping. The aging time is 150s, process and cut the sponge obtained after aging and stripping into finished products.

Embodiment 3

[0034] Take the following components by weight, and use raw material tanks for batching: 100 parts of polyether polyol with a hydroxyl value of 230-306, 40 parts of isocyanate TDI80, 0.2 parts of amine catalyst A33, and 0.2 parts of tin catalyst T9 2 parts, silicone oil 2 parts, sodium tetraborate 2 parts, zinc oxide powder 2 parts. The above-mentioned components are prepared in a raw material tank and then sent to the reactor for mixing. The stirring speed is 4000r / min and the temperature is 22°C. Then the stirred mixture is sent to the foaming box for aging and stripping. The aging time is 120s, process and cut the sponge obtained after aging and stripping into finished products.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses low-bounce ice-cold breathable sponge. The low-bounce ice-cold breathable sponge comprises the following components, by weight part, of 90-110 parts of polyether polyol, 30-50 parts of isocyanate, 0.1-0.3 part of amine catalyst, 0.1-0.3 part of tin catalyst, 1 part to 3 parts of stabilizers, 1 part to 3 parts of sodium tetraborate and 1 part to 3 parts of zinc oxide powder. The hydroxyl value of the polyether polyol is 230 to 306. The invention further correspondingly provides preparing process of the sponge. The preparing process comprises the steps of adding raw materials into a reaction kettle in proportion to be evenly mixed and stirred, sending the stirred and mixed raw materials into a foaming box to be cured and demoulded, cooling the cured and demoulded sponge for 24 hours and cutting the sponge into finished products. The sponge has good bounce, breathability and moisture penetrability and excellent mechanical property and also has the ice-cold effect.

Description

technical field [0001] The invention relates to the field of sponge processing and preparation, in particular to a low-rebound ice-cold breathable sponge and a preparation process thereof. Background technique [0002] Sponge is a type of polyurethane foam that falls specifically within flexible polyurethane foam. It has a porous honeycomb structure, so it has excellent softness, elasticity, water absorption, and water resistance. It is currently widely used in various industries such as sofas, mattresses, clothing, and flexible packaging. [0003] Low-rebound foam has excellent resilience and memory properties, so low-rebound pillows and mattresses made of it allow the body to rest in a natural, stress-free position. However, when the human body is in direct or indirect contact with the low-rebound sponge for a long time, the sponge will absorb heat and the temperature will rise accordingly, especially in hot weather, sitting on a sofa made of low-rebound sponge for a long...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C08G18/76C08G18/48C08G18/24C08G18/20C08K3/38C08K3/22C08G101/00
CPCC08G18/165C08G18/1808C08G18/24C08G18/48C08G18/7621C08G2101/00C08K3/22C08K3/38C08K2003/2296
Inventor 蔡佛丰
Owner 良眠家居科技江苏有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com