Strong permeability waterproof agent and preparation method thereof

A technology of waterproofing agent and penetrating agent, which is applied in the direction of textiles and papermaking, fiber treatment, coating, etc. It can solve the problems of poor waterproofness, poor permeability, and complicated preparation methods, and achieves strong temperature resistance, simple production methods, and broad application prospects. Effect

Active Publication Date: 2014-10-22
WUHAN PANTHERS LEAKPROOF TECH DEV CO LTD
View PDF6 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0008] (3) The Si-O bond length is longer, and the Si-O-Si bond angle is large
[0047] So far, all kinds of waterproofing agents have been sold in the market, but they all have their defec

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Strong permeability waterproof agent and preparation method thereof
  • Strong permeability waterproof agent and preparation method thereof
  • Strong permeability waterproof agent and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0070] 1. Proportion (mass ratio) of strong penetrating waterproofing agent for interior and exterior walls of buildings

[0071]

[0072] 2. Preparation method

[0073] (1) Take 2.0 kg of silicone polymer, add 97.6 kg of co-solvent under stirring, and react at a temperature of 30°C for 1 hour;

[0074] (2) When the reactant is clear, add 0.11kg of penetrant under stirring, and react at a temperature of 30°C for 0.5 hours;

[0075](3) When the reactant is clear, add 0.11 kg of leveling agent under stirring, and react at a temperature of 30°C for 0.5 hours;

[0076] (4) When the reactant is clear, add 0.11kg of defoamer under stirring, and react at a temperature of 30°C for 0.5 hours;

[0077] (5) When the reactant is clear, add 0.11 kg of dispersant under stirring, and react at a temperature of 30°C for 0.5 hours;

[0078] (6) Filter through 300-mesh stainless steel mesh, pack and store.

Embodiment 2

[0080] 1. Proportion of strong penetrating waterproofing agent for ancient buildings (mass ratio)

[0081]

[0082]

[0083] 2. Preparation method

[0084] (1) Take 1.9kg of silicone polymer, add 97.5kg of co-solvent under stirring, and react at 25°C for 1 hour; (2) When the reactant is clear, add 0.2kg of penetrant under stirring, and react at 25°C for 0.5 hour ;

[0085] (3) When the reactant is clear, add 0.2kg of leveling agent under stirring, and react at a temperature of 25°C for 0.5 hours;

[0086] (4) When the reactant is clear, add 0.15kg of defoamer under stirring, and react at a temperature of 25°C for 0.5 hours;

[0087] (5) When the reactant is clear, add 0.15kg of dispersant under stirring, and react at a temperature of 25°C for 0.5 hours;

[0088] (6) Filter through 300-mesh stainless steel mesh, pack and store.

[0089] The detection report (see attachment) of the strong penetrating waterproofing agent prepared according to Example 1.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a strong permeability waterproof agent and a preparation method thereof. The strong permeability waterproof agent comprises the following raw materials by following mass fraction: 1.8-2.5 parts of organosilicon polymer, 0.1-0.3 parts of osmotic agent, 0.1-0.3 parts of levelling agent, 0.1-0.3 parts of antifoaming agent, 0.1-0.3 parts of dispersing agent and 96-98 parts of cosolvent. The waterproof agent is prepared by adding the ingredients in a container one by one and then stirring, controlling the temperature and filtering under normal pressure condition. The strong permeability waterproof agent has the advantages of production technology simplification, prevention of high temperature/high pressure synthesis risk, and no three wastes generation of composition; and has the beneficial effects of strong high-temperature resistance, strong permeability, fast drying and no change of color of original product. The strong permeability waterproof agent can be widely used for moisture and mildew resistant treatment before interior decoration, and used for water repellent treatment in stone industry, woodwork and textile industry, and is especially suitable for rapid construction under special environment.

Description

technical field [0001] The invention relates to a waterproofing agent, in particular to a strong penetrating waterproofing agent and a preparation method thereof. Background technique [0002] 1 silicone [0003] Organosilicon, that is, organosilicon compound, refers to a compound that contains Si-O bonds and at least one organic group is directly connected to a silicon atom. Linked compounds are also known as organosilicon compounds. Among them, the polysiloxane composed of silicon-oxygen bond (-Si-0-Si-) as the skeleton is the most numerous, the deepest researched and the most widely used class of organosilicon compounds, accounting for more than 90% of the total amount. . [0004] The basic structural unit of silicone products is composed of silicon-oxygen chain links, and the side chains are connected with various other organic groups through silicon atoms. Therefore, the structure of silicone products contains both "organic groups" and "inorganic structures". This s...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C09D183/04C09D7/12D06M15/643
Inventor 向宗煜胡高平
Owner WUHAN PANTHERS LEAKPROOF TECH DEV CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap