A kind of cellulose blend fiber and preparation method thereof

A technology of blending fiber and cellulose, which is applied in the direction of cellulose/protein conjugated artificial filament, fiber chemical characteristics, spinning solution preparation, etc., to achieve high environmental friendliness, simple preparation method, excellent flexibility and strength Effect

Active Publication Date: 2014-10-29
傲丝生态(中国)有限公司
View PDF8 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The advent of ionic liquids has greatly increased the possibility

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of cellulose blend fiber and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0022] Embodiment 1 Preparation of blended fiber of the present invention

[0023] Prepare a polyacrylonitrile solution with a mass concentration of 15% and a polyvinyl alcohol solution with a mass concentration of 15%; prepare a cellulose solution with a mass concentration of 5%, and vacuum-dry chitosan and polylysine (70°C, vacuum under the condition of 100Pa and vacuum drying for 12 hours, the drying temperature is 45), and then added to the cellulose solution at 50°C to obtain the spinning stock solution, and the spinning stock solution was mixed with polyacrylonitrile solution and polyvinyl alcohol solution at 75°C uniform, so that the solution contains 60 parts of natural cellulose, 10 parts of polylysine, 3 parts of polyacrylonitrile, 2 parts of polyvinyl alcohol, and 0.5 part of chitosan, and the mixed mixture is extruded by a twin-screw extruder to obtain Blending the tow; washing the blended tow through a water tank to remove the ionic liquid, stretching, drying, cro...

Embodiment 2

[0024] Embodiment 2 Preparation of blended fiber of the present invention

[0025] Prepare a polyacrylonitrile solution with a mass concentration of 15% and a polyvinyl alcohol solution with a mass concentration of 15%; prepare a cellulose solution with a mass concentration of 5%, and vacuum-dry chitosan and polylysine (70°C, vacuum vacuum drying under the condition of 100 Pa for 12 hours, and the drying temperature is 45), then add it to the cellulose solution at 50°C to obtain the spinning stock solution, and mix the spinning stock solution with polyacrylonitrile solution and polyvinyl alcohol solution at 50°C uniform, so that the solution contains 80 parts of natural cellulose, 15 parts of polylysine, 7 parts of polyacrylonitrile, 8 parts of polyvinyl alcohol, and 3.5 parts of chitosan, and the mixed mixture is extruded by a twin-screw extruder to obtain Blending the tow; washing the blended tow through a water tank to remove the ionic liquid, stretching, drying, cross-link...

Embodiment 3

[0026] Embodiment 3 Preparation of blended fiber of the present invention

[0027] Prepare a polyacrylonitrile solution with a mass concentration of 15% and a polyvinyl alcohol solution with a mass concentration of 15%; prepare a cellulose solution with a mass concentration of 5%, and vacuum-dry chitosan and polylysine (70°C, vacuum vacuum drying under the condition of 100 Pa for 12 hours, and the drying temperature is 45), then add it to the cellulose solution at 50°C to obtain the spinning stock solution, and mix the spinning stock solution with polyacrylonitrile solution and polyvinyl alcohol solution at 50°C uniform, so that the solution contains 70 parts of natural cellulose, 12 parts of polylysine, 5 parts of polyacrylonitrile, 5 parts of polyvinyl alcohol, and 2.5 parts of chitosan, and the mixed mixture is extruded by a twin-screw extruder to obtain Blending the tow; washing the blended tow through a water tank to remove the ionic liquid, stretching, drying, cross-link...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
degree of polymerizationaaaaaaaaaa
degree of polymerizationaaaaaaaaaa
Login to View More

Abstract

The invention relates to blended fibers and a preparation method thereof and belongs to the technical field of blended fibers. In order to overcome the technical defects of low strength and low toughness of cellulose fibers in the prior art, the invention provides blended fibers adopting cellulose as a main component and a preparation method thereof. The blended fibers comprise the following components in parts by weight: 60-80 parts of natural cellulose, 10-15 parts of polylysine, 3-7 parts of polyacrylonitrile, 2-8 parts of polyvinyl alcohol and 0.5-3.5 parts of chitosan. The blended fibers prepared by the formula and the process are excellent in performance, strong in toughness and good in elasticity and can meet the needs of the textile industry.

Description

technical field [0001] The invention relates to a blended fiber and a preparation method thereof, belonging to the technical field of blended fibers. Background technique [0002] With the development and progress of technology and the continuous improvement of people's requirements, fibers of a single material sometimes cannot meet people's needs very well, and various multi-component fibers have emerged as the times require. They have properties that cannot be possessed by fibers of a single material at the same time, and combine the advantages of multiple fibers to provide better performance. The blended fiber can have part of the excellent properties of the two blended components at the same time, and the blended fiber with excellent properties can be obtained by a reasonable combination of properties. The preparation process is simple, and at the same time, the amount of more expensive materials can be reduced and the cost can be saved. [0003] Cellulose is a common n...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): D01F8/02D01F8/12D01F8/08D01F8/10D01F8/18D01D1/02
Inventor 洪朝阳
Owner 傲丝生态(中国)有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com