A kind of oil-resistant and anti-corrosion PVC cable material and preparation method thereof

A cable material and anti-corrosion technology, applied in the direction of plastic/resin/wax insulators, organic insulators, etc., can solve problems such as difficulty in batch use, special processing performance, and high price

Active Publication Date: 2016-03-09
HUNAN WEICHU CABLE POLYMER MATERIAL CO LTD
View PDF2 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, most materials on the market can only meet one or two performance requirements at the same time, and cannot take care of many of them at the same time; while some high-end materials, such as polyurethane, can meet the performance requirements, but they are expensive and have special processing properties, making it difficult to use them in batches.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of oil-resistant and anti-corrosion PVC cable material and preparation method thereof
  • A kind of oil-resistant and anti-corrosion PVC cable material and preparation method thereof
  • A kind of oil-resistant and anti-corrosion PVC cable material and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1～ Embodiment 4

[0029] 1. Experimental materials

[0030] The composition and proportioning of raw materials are shown in Table 1 below.

[0031] PVC resin (polymerization degree 1300) was purchased from Ningbo Formosa Plastics Company; PVC resin (polymerization degree 2500) was purchased from Shanghai Chlor-Alkali Chemical Company; ethylene-propylene rubber was purchased from DuPont; nitrile rubber was purchased from Korea LG Company; , purchased from Japan Denki Chemical Corporation; calcium-zinc composite heat stabilizer, organotin heat stabilizer purchased from Germany Bear brand.

[0032] 2. Experimental method

[0033] Put the PVC resin, heat stabilizer, lubricant, and antioxidant in a high-speed kneader and heat it for low-speed mixing. The speed is 500 rpm. After the plasticizer is completely added, start high-speed mixing, and the high-speed mixing speed is 1500rpm;

[0034] Mix at high speed until the plasticizer is absorbed by the powder, start low speed when the material temper...

Embodiment 5～ Embodiment 8

[0045] 1. Experimental materials

[0046] PVC resin (polymerization degree 1300) was purchased from Ningbo Formosa Plastics Company; PVC resin (polymerization degree 2500) was purchased from Shanghai Chlor-Alkali Chemical Company; ethylene-propylene rubber was purchased from DuPont; nitrile rubber was purchased from Korea LG Company; , purchased from Japan Denki Chemical Corporation; calcium-zinc composite heat stabilizer, organotin heat stabilizer purchased from Germany Bear brand.

[0047] The composition and proportioning of raw materials are shown in Table 3 below.

[0048] 11. Experimental method

[0049] Put the PVC resin, heat stabilizer, lubricant, and antioxidant in a high-speed kneader and heat it for low-speed mixing. The mixing speed is 1000rpm, and the temperature of the high-speed kneader is controlled at about 115°C. At the same time, the plasticizer is added in two times. After the plasticizer is completely added, start high-speed mixing, and the mixing speed...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
degree of polymerizationaaaaaaaaaa
Login to View More

Abstract

The invention relates to the field of a cable material, and in particular discloses an oil-proof and anti-corrosion polyvinyl chloride (PVC) cable material and a preparation method thereof. The oil-proof and anti-corrosion PVC cable material consists of the following components in parts by weight: 100 parts of PVC resin, 15-40 parts of rubber, 40-65 parts of a plasticizer, 30-55 parts of calcium carbonate, 5-12 parts of a heat stabilizer, 1.5-4 parts of a lubricant and 1-2 parts of an antioxidant. The prepared oil-proof and anti-corrosion PVC cable material disclosed by the invention is compatible with temperature resistance, cold resistance, oil resistance and corrosion resistance, and overcomes shortcomings of an existing material; the cable material is suitable for cold region and coastal region.

Description

technical field [0001] The invention relates to the field of cable materials, and specifically discloses an oil-resistant and anti-corrosion PVC cable material and a preparation method thereof. Background technique [0002] In recent years, due to natural internal processes and man-made external damage, the global climate has undergone great changes, frequent extreme weather, and severe weather such as heavy rain, snowstorm, and typhoon have occurred in many areas, and these have caused extremely hot or extremely cold climates , so that the wires and cables in daily use have requirements for heat resistance and cold resistance. In the coastal area, the perennial sea wind and waves erode, the seawater is highly alkaline, and has certain corrosion damage to the cable material, thus putting forward requirements for the corrosion resistance of the cable material. For example, the cables used in wind energy generator sets must meet the strict low-temperature torsion test and at ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08L27/06C08L23/16C08L9/02C08L11/00H01B3/44C08K13/02C08K3/26
Inventor 胡玲
Owner HUNAN WEICHU CABLE POLYMER MATERIAL CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com