Ceramic proppant added with aluminium dihydrogen phosphate and preparation method of ceramic proppant

A technology of aluminum dihydrogen phosphate and proppant, which is applied in chemical instruments and methods, earthwork drilling, drilling composition, etc. The effect of powder removal and crack generation, product quality improvement, and simple preparation method

Inactive Publication Date: 2014-01-15
ZIBO JIAFENG MINING
View PDF6 Cites 7 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] There is a common problem in the production of ceramsite proppant, that is, the strength of green ball is low, which leads to easy de-powdering in the production process, resulting in micro-cracks, turbidity, acid solubility exceeding the standard, etc., affecting the quality of its products, ceramsite proppant Manufacturers of ceramsite proppant often add some binders such as bauxite or clay raw material, starch, dextrin, etc. to the formula to improve the strength of ceramsite proppant balls, but these binders are generally organic binders or contain organic binders. For materials with binder components, the green ball can maintain a certain strength under normal temperature conditions, but under medium temperature conditions, these organic binders will fail, resulting in reduced strength of the green ball, easy powder removal and cracks, so during calcination The preheating section is prone to powder removal and cracks, which seriously affects the quality of the product

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Ceramic proppant added with aluminium dihydrogen phosphate and preparation method of ceramic proppant

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0021] Prepare 5kg of granulation powder, make aluminum dihydrogen phosphate into a solution with a concentration of 12%, use a disc granulator to granulate, add 1.5kg of granulation powder to the granulator, start the turntable, and the turntable rotates clockwise, keeping the speed at 30rpm Keep the same, make the granulated powder do parabolic motion in the disc granulator; add 2g of the prepared aluminum dihydrogen phosphate aqueous solution into the atomized watering can, and spray evenly on the thrown granulated powder until the granulated powder appears For small particles with clear particle size, add 50g of granulation powder at this time, and continue spraying at the same time, repeat adding every 11 seconds, until the remaining 3.5g of granulation powder is added, and the small particles continue to grow to 0.6-0.9mm, stop adding granulation powder and spraying, the disc granulator continued to rotate for 40 minutes to form ceramsite green balls, and then calcined at...

Embodiment 2

[0023] Prepare 5kg of granulation powder, make aluminum dihydrogen phosphate into a solution with a concentration of 20%, use a disc granulator to granulate, add 1.1kg of granulation powder to the granulator, start the turntable, and the turntable rotates clockwise, keeping the speed at 50rpm Keep the same, make the granulated powder do parabolic motion in the disc granulator; add 0.88g of the prepared aluminum dihydrogen phosphate aqueous solution into the atomized watering can, and spray evenly on the thrown granulated powder until the granulated powder When small particles with clear particle size appear, add 80g of granulation powder at this time, continue spraying at the same time, repeat the addition every 10 seconds, until the remaining 3.9g of granulation powder is added, and the small particles continue to grow to 0.6-0.9mm, stop adding granulation Powder and spray, and the disc granulator continues to rotate for 50 minutes to form ceramsite green balls, and then calci...

Embodiment 3

[0025] Prepare 5kg of granulation powder, make aluminum dihydrogen phosphate into a solution with a concentration of 8%, use a disc granulator to granulate, add 1kg of granulation powder to the granulator, start the turntable, and the turntable rotates clockwise, keeping the speed at 40rpm. Change, make the granulated powder do parabolic motion in the disc granulator; add 1.25g of the prepared aluminum dihydrogen phosphate aqueous solution into the atomized watering pot, and spray evenly on the thrown granulated powder until the granulated powder appears For small particles with clear particle size, add 100g of granulation powder at this time, and continue spraying at the same time, repeat adding every 8 seconds until the remaining 4g of granulation powder is added, and the small particles continue to grow to 0.6-0.9mm, stop adding granulation powder and Spray, and the disc granulator continues to rotate for 30 minutes to form ceramsite green balls, and then calcined at 1400°C ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a ceramic proppant added with aluminium dihydrogen phosphate and a preparation method of the ceramic proppant. The ceramic proppant is prepared by adding aluminium dihydrogen phosphate into granulation powder. The preparation method comprises the following steps: firstly, adding part of granulation powder into a granulator, then adding aluminium dihydrogen phosphate and finally adding the rest of granulation powder one or more times to prepare ceramsite blank balls; finally, calcining the ceramsite blank balls to obtain the ceramic proppant. The ceramic proppant has lower turbidity, acid solubility and breakage rate; the intensity of the blank balls in the preparation process is improved; the breakage rate of the finished product is reduced by 1 to 2 percent; powder fall-off and cracks are reduced; product quality is improved. Moreover, the preparation method is simple and is easy to operate.

Description

technical field [0001] The invention relates to a ceramsite proppant added with aluminum dihydrogen phosphate and a preparation method thereof. Background technique [0002] There is a common problem in the production of ceramsite proppant, that is, the strength of green ball is low, which leads to easy de-powdering in the production process, resulting in micro-cracks, turbidity, acid solubility exceeding the standard, etc., affecting the quality of its products, ceramsite proppant Manufacturers of ceramsite proppant often add some binders such as bauxite or clay raw material, starch, dextrin, etc. to the formula to improve the strength of ceramsite proppant balls, but these binders are generally organic binders or contain organic binders. For materials with binder components, the green ball can maintain a certain strength under normal temperature conditions, but under medium temperature conditions, these organic binders will fail, resulting in reduced strength of the green ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C09K8/80
CPCC09K8/80
Inventor 唐珂孙洪巍金宝文高光辉
Owner ZIBO JIAFENG MINING
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com