Preparation method of safe anti-puncturing tyre

A tire and safety technology, applied to the reinforcement layer of pneumatic tires, tire parts, transportation and packaging, etc., can solve the problems of low production efficiency, unsatisfactory anti-puncture effect, high cost, etc., and achieve high production efficiency and tire anti-corrosion Good pricking effect and low cost

Inactive Publication Date: 2014-01-08
杭州绿奇科技有限公司
View PDF5 Cites 11 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] Existing radial tires are generally composed of airtight layer 2, carcass layer 3, belt layer 5 and tread 4, and its structure can be referred to figure 1 , the production efficiency of the tire with this structure is low, the cost is high, and its anti-puncture effect is not ideal, and the safety performance needs to be improved

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method of safe anti-puncturing tyre
  • Preparation method of safe anti-puncturing tyre
  • Preparation method of safe anti-puncturing tyre

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0032] refer to figure 2 , a preparation method of a safety puncture-proof tire, the safety puncture-proof tire is provided with a self-sealing layer 1, an airtight layer 2, a carcass layer 3, a belt layer 5 and a tread 4 in sequence from the inside to the outside, and the self-sealing The thickness of the layer is 0.5mm, and the thickness of the airtight layer is 2.5mm; the self-sealing layer 1 is fully covered on the airtight layer 2 . The cord layer is a steel cord layer, and the number of layers of the steel cord layer is 3 layers. The preparation method comprises the steps of:

[0033] (1) Extrude the tread through an extruder;

[0034] (2) The adhesive is sprayed and cooled to form a self-sealing layer;

[0035] (3) Extrude the airtight layer and ply layer respectively through the calender;

[0036] (4) Bond the airtight layer and the self-sealing layer to form an inner lining layer;

[0037] (5) Forming of the belt layer; in the spindle room, the steel wire comes ...

Embodiment 2

[0045] refer to figure 2 , a preparation method of a safety puncture-proof tire, the safety puncture-proof tire is provided with a self-sealing layer 1, an airtight layer 2, a carcass layer 3, a belt layer 5 and a tread 4 in sequence from the inside to the outside, and the self-sealing The thickness of the layer is 1.1 mm, and the thickness of the airtight layer is 1.8 mm; the self-sealing layer 1 is fully covered on the airtight layer 2 . The ply is a steel ply, and the number of layers of the steel ply is one. Described tire is prepared by following method:

[0046] (1) Extrude the tread through an extruder;

[0047] (2) The adhesive is sprayed and cooled to form a self-sealing layer;

[0048] (3) Extrude the airtight layer and ply layer respectively through the calender;

[0049] (4) Bond the airtight layer and the self-sealing layer to form an inner lining layer;

[0050] (5) Belt forming;

[0051] (6) The inner liner, cord layer, belt layer and tread are integrally...

Embodiment 3

[0057] refer to figure 2 , a preparation method of a safety puncture-proof tire, the safety puncture-proof tire is provided with a self-sealing layer 1, an airtight layer 2, a carcass layer 3, a belt layer 5 and a tread 4 in sequence from the inside to the outside, and the self-sealing The thickness of the layer is 1.9 mm, and the thickness of the airtight layer is 1.0 mm; the self-sealing layer 1 is fully covered on the airtight layer 2 . The cord layer is a steel cord layer, and the number of layers of the steel cord layer is 5 layers. Described tire is prepared by following method:

[0058] (1) Extrude the tread through an extruder;

[0059] (2) The adhesive is sprayed and shaped to form a self-sealing layer;

[0060] (3) Extrude the airtight layer and ply layer respectively through the calender;

[0061] (4) Belt forming;

[0062] (5) Self-sealing layer, airtight layer, carcass layer, belt layer, and tread are integrally formed and bonded on the molding machine. The ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a preparation method of a safe anti-puncturing tyre. The safe anti-puncturing tyre is sequentially provided with a self-sealing layer, an air-tight layer, a curtain cloth layer, a belted layer and a tread from inside to outside. The preparation method comprises the following steps: (1) extruding the tread by using an extruding machine; (2) spraying and molding an adhesive to form the self-sealing layer; (3) respectively pressing the air-tight layer and the curtain cloth layer by a calendering machine; (4) molding the belted layer; and (5) fitting the self-sealing layer, the air-tight layer, the curtain cloth layer, the belted layer and the tread on a molding machine and integrally molding and fitting to obtain the safe anti-puncturing tyre. The tyre prepared by the preparation method provided by the invention is simple in structure and reasonable in design and has the characteristics of high production efficiency, low cost, good tyre anti-puncturing effect, high safety performance and the like.

Description

technical field [0001] The invention relates to a tire, in particular to a preparation method of a safe puncture-proof tire. Background technique [0002] With the rapid development of the automobile industry and the improvement of the traffic road network, improving the performance of motor vehicle tires and developing safe, durable, high-speed and low-cost products have become one of the important research projects of the current scientific research and production departments. According to incomplete statistics from relevant professional organizations, more than 95% of automobile tires have potential safety hazards, 60% of tires have abnormal tire pressure, and 70% of traffic accidents on domestic expressways are caused by hidden tire hazards. The death rate of a tire blowout accident is as high as 100%. High-speed tire blowout, speeding driving, fatigue driving, and drunk driving have become the four major culprits of vehicle safety accidents. Traffic accidents are shoc...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): B60C9/04B60C9/20
Inventor 沈仁元王宏海沈乐恩
Owner 杭州绿奇科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com