Polyether polyamine, preparation method of polyether polyamine, polyether polyamine block silicone oil and preparation method of polyether polyamine block silicone oil

A technology of amino polyether and block silicone oil, which is applied in textiles, papermaking, fiber treatment, etc., and can solve the problems of high bulkiness, easy yellowing, sticking to rollers and cylinders, etc.

Active Publication Date: 2014-01-01
上海硅普化学品有限公司
View PDF3 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] (1) Under the action of light and heat, it is easy to turn yellow;
[0004] (2) Natural fiber will make it lose hydrophilicity and affect its effect;
[0005] (3) It is difficult to meet special needs such as high resilience, washability, and high fluffiness;
[0006] (4) Amino silicone oil cannot be self-emulsified, and an emulsifier needs to be added, which affects the color fastness of the fabric and the fabric is easy to fade;
[0008] (6) Fabrics containing this kind of softener are prone to sticking to rollers and cylinders during the production process

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Polyether polyamine, preparation method of polyether polyamine, polyether polyamine block silicone oil and preparation method of polyether polyamine block silicone oil
  • Polyether polyamine, preparation method of polyether polyamine, polyether polyamine block silicone oil and preparation method of polyether polyamine block silicone oil
  • Polyether polyamine, preparation method of polyether polyamine, polyether polyamine block silicone oil and preparation method of polyether polyamine block silicone oil

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0045] The present invention is described in detail below in conjunction with embodiment:

[0046] Mix the first double-ended amino polyether A, the second double-ended amino polyether B and the double-ended epoxy polyether C according to the weight ratio in Table 1, and an addition reaction occurs.

[0047] h 2 NC 3 h 6 (OC 3 h 6 ) a (OC 2 h 4 ) b (OC 3 h 6 ) a NH 2 (A)

[0048] h 2 NC 3 h 6 (OC 3 h 6 ) d NH 2 (B)

[0049]

[0050] h 2 NC 3 h 6 (OC 3 h 6 ) a (OC 2 h 4 ) b (OC 3 h 6 ) a NHCH 2 CH(OH)CH 2 (OC 2 h 4 ) c OCH 2 CH(OH)CH 2 NHC 3 h 6 (OC 3 h 6 ) d NH 2 (D)

[0051] The values ​​of a, b, c, and d and the temperature and time of the addition reaction are shown in Table 1.

[0052] Table 1

[0053] Wherein the unit of measurement of each substance is parts by weight, the unit of temperature is ℃, and the unit of reaction time is hour, embodiment 1

[0054] The reactio...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses polyether polyamine which is characterized by having a following general formula: H2NC3H6(OC3H6)a(OC2H4)b(OC3H6)aNHCH2CH(OH)CH2(OC2H4)cOCH2CH(OH)CH2NHC3H6(OC3H6)dNH2, wherein the a, b, c and d are all integers from 2-40. The polyether polyamine provided by the invention contains amino groups at chain ends, has amino groups in the chain middle part, and has the improved content of the amino groups in comparison with that of the amino groups of the conventional polyether polyamine, and the flexibility of polyether polyamine block silicone oil prepared by using the polyether polyamine as one of raw materials is greatly improved.

Description

technical field [0001] The invention relates to an amino polyether and a preparation method thereof, an amino polyether block silicone oil and a preparation method thereof. Background technique [0002] At present, amino silicone oil is mostly used as textile softener in the market, so it is also known as the king of softeners. Amino silicone oil is formed by bulk polymerization of N-2-aminoethyl-3-aminopropylmethyldimethoxysilane coupling agent (ie KBM-602) and octamethylcyclotetrasilane (ie D4). The chain contains amino groups, so it can play a softening role. But this kind softener has the following disadvantages simultaneously: [0003] (1) Under the action of light and heat, it is easy to turn yellow; [0004] (2) Natural fiber will make it lose hydrophilicity and affect its effect; [0005] (3) It is difficult to meet special needs such as high resilience, washability, and high fluffiness; [0006] (4) Amino silicone oil cannot be self-emulsified, and an emulsifie...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C08G81/00D06M15/647
Inventor 田慧芬王健伟陈敬然
Owner 上海硅普化学品有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products