Composite floor board and production method thereof

A composite flooring and production method technology, applied to layered products, floors, buildings, etc., can solve problems such as floor breakage, reduced service life, and poor quality of composite floors, so as to reduce shrinkage and expansion rates and improve performance and service life, reducing the effect of volume change

Inactive Publication Date: 2013-12-25
ZHEJIANG KINGDOM NEW MATERIAL GRP CO LTD
View PDF5 Cites 16 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] The specifications of calcium carbonate used in the base material layer of the existing composite flooring are all 325 meshes, which makes the shrinkage rate of the composite flooring produced can only reach a minimum of 0.05%, and the expansion rate can only reach a minimum of 0.13%. It is relatively large, and the quality of the composite floor is relatively poor. During use, it is easy to cause gaps between the floors due to thermal expansion and contraction or mutual extrusion between the floors, resulting in floor breakage and other damage, affecting the normal use of the floor. reduce its service life

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0010] The composite floor described in this embodiment comprises a wear-resistant layer, a color film layer and a substrate layer from top to bottom, wherein the substrate layer is made of calcium carbonate, PVC, plasticizer, stabilizer and modifier ACR, The weight ratio of its PVC, calcium carbonate, plasticizer, stabilizer, modifier ACR is: 100:400:30:0.5:5, the specification of described calcium carbonate is 500 mesh; The production method of this composite floor, The first step is to produce the substrate layer first, and then put the raw materials into the compacting and kneading equipment for processing and molding, and the processing temperature is 160°C; the second step is to heat-composite the wear-resistant layer, color film layer and substrate layer, and process The temperature is 125°C; the third step, after thermal compounding treatment, place the wear-resistant layer, color film layer and substrate layer in a constant temperature room for 24 hours and then perfor...

Embodiment 2

[0012] The composite floor described in this embodiment comprises a wear-resistant layer, a color film layer and a substrate layer from top to bottom, wherein the substrate layer is made of calcium carbonate, PVC, plasticizer, stabilizer and modifier ACR, The weight ratio of its PVC, calcium carbonate, plasticizer, stabilizer, modifier ACR is: 100:500:40:5:10, the specification of described calcium carbonate is 600 mesh; The production method of this composite floor, The first step is to produce the base material layer first, and put the raw materials into the compacting and kneading equipment for processing and molding, and the processing temperature is 180°C; the second step is to heat-compound the wear-resistant layer, color film layer and base material layer, and process The temperature is 140°C; the third step, after thermal compounding treatment, place the wear-resistant layer, color film layer and substrate layer in a constant temperature room for 24 hours and then perfo...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Specificationaaaaaaaaaa
Login to View More

Abstract

The invention relates to the field of the production of a floor board, and particularly discloses a composite floor with small expansion rate and contraction rate and a production method thereof. The composite floor board comprises a wearable layer, a color film layer and a base material layer from top to bottom in sequence, wherein the base material layer consists of calcium carbonate, PVC (Polyvinyl Chloride), a plasticizer, a stabilizer and a modifier ACR (Acrylics); the production method comprises the steps of processing for shaping, implementing thermal compounding, implementing surface UV (Ultraviolet) and tempering, cooling and finally implementing slicing and grooving. According to the composite floor board and the production method thereof, the calcium carbonate adopted for the composite floor board has a specification of over 500 meshes; the processing temperature is rationally controlled through the production method, so that the contraction rate and the expansion rate can be effectively lowered; consequently, the lowest contraction rate can reach 0.04% and the lowest expansion rate can reach 0.1%; as the volume change of the composite floor board caused by expansion and contraction is greatly decreased, the use performance and the service life of the composite floor board can be effectively improved.

Description

technical field [0001] The invention relates to the field of floor production, in particular to a composite floor and a production method thereof. Background technique [0002] The specifications of calcium carbonate used in the base material layer of the existing composite flooring are all 325 meshes, which makes the shrinkage rate of the composite flooring produced can only reach a minimum of 0.05%, and the expansion rate can only reach a minimum of 0.13%. It is relatively large, and the quality of the composite floor is relatively poor. During use, it is easy to cause gaps between the floors due to thermal expansion and contraction or mutual extrusion between the floors, resulting in floor breakage and other damage, affecting the normal use of the floor. reduce its service life. Contents of the invention [0003] The object of the present invention is to provide a compound floor with low expansion rate and shrinkage rate and its production method in order to solve the ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): E04F15/10B32B33/00
Inventor 范柳华
Owner ZHEJIANG KINGDOM NEW MATERIAL GRP CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com