Method for preparing three-dimensional macroporous metal phosphide

A metal phosphide, three-dimensional macroporous technology, applied in the direction of phosphide and so on

Inactive Publication Date: 2013-12-25
TIANJIN POLYTECHNIC UNIV
View PDF0 Cites 23 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Metal phosphides have attracted the attention of scholars due to their excellent physical and chemical properties such as superconductivity, ferromagnetism, and catalytic activity. However, the controlled synthesis and application research of phosphides with special structures has always been a huge challenge.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment approach 1

[0009] Take a piece of nickel foam of 5×2 square centimeters, disperse 5g of red phosphorus powder on the upper surface of the nickel foam, then place it in a quartz boat, put it into a tube furnace, and feed argon gas at a flow rate of 20mL / min, then Directly raise the temperature to 700°C, react at this temperature for 30 minutes, and then lower it to room temperature under the protection of argon. The product is soaked in 6mol / L hydrochloric acid in a water bath at 80°C for 5 hours, then washed to neutrality, and dried in vacuum at 60°C for 3 hours. A three-dimensional macroporous nickel phosphide is obtained.

Embodiment approach 2

[0011] The reaction temperature in Embodiment 1 is changed from 700°C to 750°C, and other conditions remain unchanged, to obtain three-dimensional macroporous nickel phosphide.

Embodiment approach 3

[0013] The reaction time in embodiment 1 is changed from 30min to 60min, and other conditions are unchanged, and three-dimensional macroporous nickel phosphide is obtained.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a method for preparing a three-dimensional macroporous metal phosphide by heat treatment of foam metal, and belongs to the technical field of preparation processes of inorganic materials. According to the method disclosed by the invention, a mechanical mixture of red phosphorus and the foam metal is taken as a precursor, and the three-dimensional macroporous metal phosphide is prepared by utilizing the reaction of the red phosphorus and metal particles. The method has the advantages of simplicity in operation, good process repeatability, stable product quality, and suitability for large-scale production.

Description

technical field [0001] The invention belongs to the technical field of inorganic material preparation technology, and relates to a preparation method of inorganic materials, in particular to a synthesis method of a three-dimensional macroporous metal phosphide. It can be applied to battery materials, superconducting materials and catalytic materials, etc. Background technique [0002] The three-dimensional macroporous structure possesses optimized chemical and physical properties due to its hollow feature, thus holding promising application prospects. Due to the smaller material density, larger specific surface area, and loadable space, three-dimensional macroporous particles can be used as assembly units for lightweight materials and catalysts with high surface activity. Metal phosphides have attracted the attention of scholars due to their excellent physical and chemical properties such as superconductivity, ferromagnetism, and catalytic activity. However, the controlled ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C01B25/08
Inventor 宋立民韦庆梧叶佳义王艳兵
Owner TIANJIN POLYTECHNIC UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com