A glass insulator material

A glass insulator, glass technology, applied in inorganic insulators, quartz/glass/glass enamel, metal oxides, etc., can solve the problems of difficulty in meeting the characteristics of high-voltage insulators, poor insulation performance of high-alkali glass, and low volume resistivity, etc. Achieve the effect of large-scale popularization and application, meeting characteristic requirements and high volume resistivity

Inactive Publication Date: 2015-08-05
佛山市昌越玻璃有限公司
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the insulation performance of high-alkali glass is poor, mainly manifested in low volume resistivity and high dielectric loss, which makes it difficult to meet the characteristic requirements of high-voltage insulators

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0011] Using waste CRT screen glass as raw material, adjust the mass percentage of each component in the waste CRT screen glass to obtain 65﹪SiO 2 , 3.1﹪PbO, 2﹪Al 2 O 3 , 6﹪MgO, 12﹪Na 2 O, 8﹪K 2 O, 2﹪BaO, 0.4﹪Li 2 O, 1.5﹪SrO glass insulator material.

[0012] The volume resistivity of the glass insulator material prepared in Example 1 at 18°C =5.5×10 14 ,Volume resistivity at 90℃ =2.3×10 10 , The dielectric loss D=1.38% at 18℃, and the dielectric loss D=1.97% at 40℃.

Embodiment 2

[0014] Using waste CRT cone glass as raw material, adjust the mass percentage of each component in the waste CRT cone glass to obtain 72% SiO 2 , 4﹪PbO, 8﹪Al 2 O 3 , 2﹪MgO, 6﹪Na 2 O, 7﹪K 2 O, 0.5% BaO, 0.5% SrO glass insulator materials.

[0015] The volume resistivity of the glass insulator material prepared in Example 2 at 18°C =5.7×10 14 Ω·cm, volume resistivity at 90℃ =2.5×10 10 Ω·cm, dielectric loss D=1.35% at 18℃, and D=1.94% at 40℃.

Embodiment 3

[0017] Using waste CRT screen glass as raw material, adjust the mass percentage of each component in the waste CRT screen glass to obtain 69% SiO 2 , 0.05﹪PbO, 7.5﹪Al 2 O 3 , 6﹪MgO, 11﹪Na 2 O, 3﹪K 2 O, 1.8﹪BaO, 0.35﹪Li 2 O, 1.3% SrO glass insulator material.

[0018] The volume resistivity of the glass insulator material prepared in Example 3 at 18°C =5.45×10 14 Ω·cm, volume resistivity at 90℃ =2.37×10 10 Ω·cm, dielectric loss D=1.33% at 18℃, and D=1.92% at 40℃.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
electrical resistivityaaaaaaaaaa
electrical resistivityaaaaaaaaaa
electrical resistivityaaaaaaaaaa
Login to View More

Abstract

The invention relates to a glass insulator material. An existing insulator is poor in insulation performance of high-alkali glass. The glass insulator material comprises components by weight of 65-72% of SiO2, 0.05-4% of PbO, 2-8% of Al2O3, 2-6% of MgO, 6-12% of Na2O, 3-8% of K2O, 0.5-2% of BaO, 0-0.4% of Li2O and 0.5-1.5% of SrO. When the glass insulator material is 18 DEG C, the volume resistivity is larger than 5*1014. When the glass insulator material is 90 DEG C, the volume resistivity is larger than 2*1010. When the glass insulator material is 18 DEG C, the dielectric loss D is smaller than 1.4%. When the glass insulator material is 40 DEG C, the dielectric loss is smaller than 2.0%. The glass insulator material uses waste leaded glass as main raw materials, changes waste into wealth, and achieves resource utilization of leaded glass. Furthermore, the glass insulator material is high in volume resistivity, low in dielectric loss and excellent in sealing performance and processing performance.

Description

Technical field [0001] The invention relates to a glass insulator material, in particular to an insulator glass piece prepared by using waste lead-containing glass as a raw material. Background technique [0002] An insulator is a device mainly used to support and insulate the wires of overhead transmission lines. The insulators currently used mainly include porcelain insulators, glass insulators and organic composite insulators. Traditional porcelain insulators have complex manufacturing processes, high energy consumption, bulky and fragile products, and poor tensile and bending strength. In addition, the porcelain surface is hydrophilic and therefore has poor resistance to pollution flashover. Organic composite insulators are light in weight, have good anti-fouling performance, and have high strength. The disadvantage is that the production cost is relatively high. Compared with ceramic and organic composite insulators, glass insulators have extremely obvious advantages and h...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): H01B3/08H01B3/10
Inventor 姚志通黄进刚
Owner 佛山市昌越玻璃有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products