Bronzing pulp and preparation method thereof

A bronzing paste and emulsion technology, applied in dyeing method, transfer printing method, textile and papermaking, etc., can solve the problems of no bronzing effect, poor washing fastness, hard hand feeling, etc. Soft-touch effect

Active Publication Date: 2013-08-21
GUANGZHOU SHENGQIN IND
View PDF5 Cites 22 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

But for a long time, clothing bronzing has defects such as hard hand feeling, poor washing fastness, and bronzing effect is not as shiny as bronzing on plastic.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0030] Bronzing paste, made from raw materials comprising the following parts by weight:

[0031] Acrylate Emulsion 61,

[0032] deionized water 3,

[0033] Solvent 4,

[0034] Stabilizer 2,

[0035] Hot melt adhesive powder 11,

[0036] Silica 0.6,

[0037] Defoamer 0.3,

[0038] pH regulator 0.2,

[0039] Preservatives 0.12,

[0040] Emulsifying wetting agent 0.4;

[0041] Thickener 0.5.

Embodiment 2

[0043] Bronzing paste, made from raw materials comprising the following parts by weight:

[0044] Acrylate Emulsion 79,

[0045] deionized water 5,

[0046] Solvent 9,

[0047] Stabilizer 4,

[0048] Hot melt adhesive powder 19,

[0049] Silica 2.9,

[0050] Defoamer 0.45,

[0051] pH regulator 0.45,

[0052] Preservatives 0.19,

[0053] Emulsifying wetting agent 0.9

[0054] thickener 1.9.

Embodiment 3

[0056] Bronzing paste, made from raw materials comprising the following parts by weight:

[0057] Acrylate Emulsion 67,

[0058] deionized water 3,

[0059] Solvent 7,

[0060] Stabilizer 2,

[0061] Hot melt adhesive powder 18,

[0062] Silica 1,

[0063] Defoamer 0.4,

[0064] pH regulator 0.3,

[0065] Preservatives 0.15,

[0066] emulsifying wetting agent 0.6,

[0067] Thickener 0.8.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses bronzing pulp. The bronzing pulp is prepared from the following raw materials in parts by weight: 60-80 parts of acrylic ester emulsion, 2-6 parts of deionized water, 3-10 parts of a solvent, 1-5 parts of a stabilizer, 10-20 parts of EVA (Ethylene-Vinyl Acetate) hot melt adhesive powder, 0.5-3 parts of silica, 0.2-0.5 part of a polyurethane defoaming agent, 0.1-0.5 part of a pH regulator, 0.1-0.2 part of a preservative, 0.3-1 part of an emulsion wetting agent and 0.4-2 parts of a thickener. The bronzing pulp has the beneficial effects that the bronzing pulp is water-based pulp, the raw materials are easy to obtain and environment-friendly, the production is convenient, the technology is mature, and substances harmful to the environment can not be produced; and the bronzing pulp is soft in handfeel, firm in fastness, outstanding in resistance to tension fracture and diversified in application mode, enriches the styles of textiles, and endows the textiles with the noble quality.

Description

technical field [0001] The invention relates to the field of textile printing materials, in particular to bronzing paste and a preparation method thereof. Background technique [0002] Prior Art In clothing printing, bronzing has become a fashion symbol because of its brilliance. But for a long time, clothing bronzing has defects such as hard hand feeling, poor washing fastness, and the bronzing effect is not as shiny as bronzing on plastics. As consumers favor bronzing effects, these problems are becoming more and more prominent. Therefore, customers urgently need to solve these problems. Contents of the invention [0003] Aiming at the deficiencies in the above-mentioned prior art, the purpose of the present invention is to provide a bronzing paste with soft hand feeling, firm fastness and outstanding cracking resistance. [0004] Another object of the present invention is to provide a method for preparing the above bronzing paste. [0005] In order to achieve the ab...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): D06P1/52D06P1/673D06P5/24
Inventor 梅立斌
Owner GUANGZHOU SHENGQIN IND
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com