A stainless steel and pickling technology, applied in the field of metal processing, can solve the problems of brittleness and easy breakage, low comprehensive performance of stainless steel fibers, and achieve the effect of overcoming poor drawing and improving comprehensive performance.

Inactive Publication Date: 2013-07-24
JIANGSU YABAO AUTO PARTS
View PDF3 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The comprehensive performance of the stainless steel fiber processed by this process is not high, brittle and easy to break

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0020] A stainless steel wire whose composition includes the following components (expressed in wt.%):

[0021] C: 0.06%, Mn: 0.36%, Si: 0.55%, Ce: 0.02%, Al: 4.8%, Cr: 26%, Cu: 1%, S: 0.04%, P: 0.05%, Fe: balance.

Embodiment 2

[0023] A stainless steel wire consisting of the following components (expressed in wt.%):

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
strengthaaaaaaaaaa
elongationaaaaaaaaaa
Login to view more

Abstract

The invention discloses a stainless steel. The stainless steel is characterized by comprising the following components represented by wt.%: 0.06-0.08% of C, 0.20-0.46% of Mn, 0.40-0.63% of Si, 20-40% of Ni, 40-60% of Cu, 4-10% of Al, 15-26% of Cr, 1-2% of Cu, 0.03-0.04% of S, 0.04-0.05% of P, and 67-81% of Fe. By adopting the technical scheme, the stainless steel wires disclosed by the invention are suitable for being subjected to drawing machining, the diameter of each wire can achieve 6 microns, the strength of each wire is greater than 16 Newton / square millimetre, and the elongation of each wire is 1.40%; the comprehensive performance of the finished products is greatly improved; and the defects that the original stainless steel wires cannot be drawn to be thin, and are brittle and easy to break are completely overcome.

Description

technical field [0001] The invention belongs to the field of metal processing, in particular to stainless steel and its manufacturing process. Background technique [0002] In the production and processing of stainless steel wire, sometimes the stainless steel wire needs to be processed very thin, and its comprehensive performance is required to be still strong and not easy to break. But existing stainless steel wire does not have such condition. According to the search by the inventor, the name is "stainless steel fiber material and processing technology and stainless steel fiber muffler core", the name is "bunch drawn stainless steel fiber", the application number is: 02814697.2, and the composition of its stainless steel fiber includes iron and the following Composition (expressed in wt.%): C<=0.05% , Mn≤5% , Si≤2% , 8%≤Ni≤12% , 15%≤Cr≤20% , Mo≤3% , Cu≤4 % , N≤0.05%, S≤0.03%, and P≤0.05%. Although this kind of stainless steel fiber can be drawn very finely, after be...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C22C38/20C23G1/08C23G3/02
Inventor 赵建林
Owner JIANGSU YABAO AUTO PARTS
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap