a permeable brick

A permeable brick and permeable base technology, which is applied to roads, pavements paved with prefabricated blocks, road surfaces, etc., can solve problems such as loose foundations, achieve the effects of prolonging service life, excellent drainage performance, and enhancing water permeability

Active Publication Date: 2016-06-08
RENCHSAND ECO ENVIRONMENT PROTECTION SCI & TECH CO LTD
View PDF7 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The purpose of the present invention is to overcome the defect that the existing permeable bricks are easy to cause the foundation to loosen, and to provide a permeable brick that has excellent drainage capacity and is not easy to cause the foundation to loosen

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • a permeable brick
  • a permeable brick
  • a permeable brick

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0046] This embodiment is used to illustrate the permeable brick provided by the present invention and its preparation.

[0047] (1) Formation of the second aggregate particles:

[0048] Put 10kg of quartz sand into the muffle furnace, bake it at 300°C for 10 minutes, then transfer the baked quartz sand to the sand mixer, and add 0.04 kg of E-44 water-based epoxy resin, 0.01 kg of phthalocyanine blue (purchased from Dainichi Seika Chemical Co., Ltd., 4920 type), continue to stir, and when the temperature drops to 130 ° C, add 0.005 kg of diethylene triethylene to the mixture amine, and stirred for 60 s to obtain coated quartz sand, the average particle diameter of which was measured by a digital stereo microscope (purchased from Beijing Huaqi Information Digital Technology Co., Ltd., brand DLC300) to be 0.1 mm.

[0049] (2) Formation of permeable bricks:

[0050] 1000g perlite (purchased from Xinyuan bentonite factory in Xinyang Industrial City, with an average particle diam...

Embodiment 2

[0052] This embodiment is used to illustrate the permeable brick provided by the present invention and its preparation.

[0053] (1) Formation of the second aggregate particles:

[0054] Put 10kg of quartz sand into the muffle furnace, roast at 300°C for 10min, then transfer the roasted quartz sand to the sand mixer, and add 0.24 kg of ME-2 water-based epoxy resin, 0.05 kg of carbon black (purchased from Dainichi Seika Chemical Co., Ltd., H190), continue to stir, and when the temperature drops to 130 ° C, add 0.6 kg of hexamethylene tetrachloride to the mixture amine, and stirred for 120s to obtain coated quartz sand, the average particle diameter of which was measured by a digital stereo microscope to be 1 mm.

[0055] (2) Formation of permeable bricks:

[0056] Mix 600g of ceramsite (purchased from Anhui Zijin Ceramsite Factory, with an average particle diameter of 7mm), 12g of cement and 10g of water to obtain a mixture that forms a permeable base; lay the mixture to a si...

Embodiment 3

[0058] This embodiment is used to illustrate the permeable brick provided by the present invention and its preparation.

[0059] (1) Formation of the second aggregate particles:

[0060] Put 10kg of raw sand into the muffle furnace, roast at 300°C for 10 minutes, then transfer the roasted raw sand to the sand mixer, and add 0.12 kg of HD-RHA308 water-based acrylic resin, 0.03 kg of carbon black (purchased from Dainichi Seika Chemical Co., Ltd., H190), and continue to stir for 80 s to obtain the coated raw sand. The average particle diameter measured by a digital stereo microscope is 0.5 mm.

[0061] (2) Formation of permeable bricks:

[0062] 1000g expanded vermiculite (purchased from Yatong Mineral Powder Factory in Lingshou County, with an average particle diameter of 5mm), 60g cement and 60g water are mixed uniformly to obtain a mixture forming a permeable base; the mixture is laid to a size of 30 cm × In a steel permeable brick mold of 60 cm x 10 cm, the laying thicknes...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
pore sizeaaaaaaaaaa
pore sizeaaaaaaaaaa
diameteraaaaaaaaaa
Login to View More

Abstract

The present invention provides a water permeable brick, which comprises a water permeable base layer and a water permeable surface layer covering on the water permeable base layer, wherein the water permeable base layer is formed through curing a mixture containing a first aggregate and a first binder, the water permeable surface layer is formed through curing a mixture containing a second aggregate and a second binder, and the second binder contains a hydrophilic binder. The water permeable brick further comprises at least a water flow pore channel positioned inside the water permeable base layer, wherein the water flow pore channel penetrates through both side surfaces of the water permeable base layer. The water permeable brick has excellent water permeability, and can not cause foundation loosing.

Description

technical field [0001] The invention relates to a permeable brick. Background technique [0002] At present, the floors of city squares, commercial streets, sidewalks, community activity sites, parking lots, etc. are mainly paved with impermeable materials such as granite, marble, glazed tiles, cement and asphalt. The impermeable floors are very harmful to the urban environment. When it rains, the impermeable ground completely prevents the rainwater from infiltrating directly into the ground, and the accumulated water makes it very inconvenient for people to travel; the precious water resources eventually flow away with the drainage pipes, which increases the burden on urban drainage facilities; The large loss of rainwater makes it difficult for the groundwater level to rise, which directly affects the health of urban vegetation, makes it difficult for the surface plants in the city to grow normally, and increases the burden of municipal greening; the large loss of rainwater...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): E01C15/00E01C5/04
Inventor 秦升益
Owner RENCHSAND ECO ENVIRONMENT PROTECTION SCI & TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com