Internal wall putty and production process thereof

A technology of interior wall putty and heavy calcium powder, which is applied in the field of building materials, can solve the problems of paint film bubbling, falling off, affecting the quality of interior walls of buildings, etc., and achieves the effects of increasing constructability, outstanding durability and strong constructability.

Inactive Publication Date: 2013-05-08
黄明杰
View PDF6 Cites 40 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, in the case of humidity or contact with water, 107 glue and pregelatinized starch will dissolve in water, making the putty on the inner wall soft and pulverized, resulting in bubbling and peeling of the paint film, which seriously affects the quality of the inner wall of the building

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0057] The present embodiment provides a kind of by weight, and interior wall putty comprises the following components:

[0058] 230 parts of white cement;

[0059] Particle size is 680 parts of 325 mesh heavy calcium powder;

[0060] Particle size is 38 parts of ash calcium of 400 meshes;

[0061] 4 parts of methyl hydroxyethyl cellulose ether;

[0062] 18 parts of vinyl acetate-ethylene copolymer;

[0063] 4 parts of sodium methyl siliconate;

[0064] 0.5 part of starch ether;

[0065] Wood fiber 2 parts.

[0066] Its production process is as follows:

[0067] Step 1, weigh 230kg of white cement, 680kg of heavy calcium powder with a particle diameter of 325 mesh, 38kg of ash calcium with a particle diameter of 400 mesh, 4kg of methyl hydroxyethyl cellulose ether, 18kg of vinyl acetate-ethylene copolymer, methyl 4kg of sodium silanolate, 0.5kg of starch ether and 2kg of wood fiber;

[0068] Step 2, put 50% white cement and 50% heavy calcium powder into a conical double-...

Embodiment 2

[0072] The present embodiment provides a kind of by weight, and interior wall putty comprises the following components:

[0073] 200 parts of white cement;

[0074] Particle size is 600 parts of 400 mesh heavy calcium powder;

[0075] Particle size is 20 parts of ash calcium of 300 mesh;

[0076] 2 parts of methyl cellulose ether;

[0077] 10 parts of vinyl acetate homopolymer;

[0078] 3 parts of high boiling sodium silanolate;

[0079] 0.1 part of starch ether;

[0080] 1 part of wood fiber.

[0081] Its production process is as follows:

[0082] Step 1, weigh 200kg of white cement, 600kg of heavy calcium powder with a particle size of 400 mesh, 20kg of ash calcium with a particle size of 300 mesh, 2kg of methyl cellulose ether, 10kg of vinyl acetate homopolymer, and 3kg of high-boiling sodium silanolate , starch ether 0.1kg and wood fiber 1kg;

[0083] Step 2, put 30% white cement and 30% heavy calcium powder into a conical twin-screw mixer and stir evenly, and the ...

Embodiment 3

[0087] The present embodiment provides a kind of by weight, and interior wall putty comprises the following components:

[0088] 250 parts of white cement;

[0089] Particle size is 800 parts of 325 mesh heavy calcium powder;

[0090] Particle size is 45 parts of ash calcium of 400 meshes;

[0091] 6 parts of hydroxyethyl cellulose ether;

[0092] 20 parts of styrene-butadiene copolymer;

[0093] 7 parts of sodium methyl siliconate;

[0094] 1 part starch ether;

[0095] Wood fiber 5 parts.

[0096] Its production process is as follows:

[0097] Step 1, weigh 250 kg of white cement, 800 kg of heavy calcium powder with a particle size of 325 mesh, 45 kg of ash calcium with a particle size of 400 mesh, 6 kg of hydroxyethyl cellulose ether, 20 kg of styrene-butadiene copolymer, methyl silicon Sodium alkoxide 7kg, starch ether 1kg and wood fiber 5kg;

[0098] Step 2, put 40% white cement and 40% heavy calcium powder into a conical twin-screw mixer and stir evenly, and the ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle size (mesh)aaaaaaaaaa
particle size (mesh)aaaaaaaaaa
Login to View More

Abstract

The invention belongs to the technical field of building materials, and particularly relates to an internal wall putty which comprises the following components in parts by weight: 150-300 parts of white cement, 500-900 parts of calcium carbonate powder, 10-50 parts of grey desert soil, 1-8 parts of cellulose ether, 7-30 parts of polymer latex powder, 1-10 parts of water repellent, 0.05-3 parts of starch ether and 0.5-7 parts of wood fiber. Compared with the prior art, the internal wall putty has the advantages that 107 glue water or 801 glue water is not used, thus formaldehyde is not contained, the environment is protected; and pregelatinized starch is not used, and the water repellent is added, thus the internal wall putty has the function of preventing water and moisture. In addition, with the white cement and the calcium carbonate powder as the strength basis and the grey desert soil as an auxiliary strength material, the strength of the internal wall putty is ensured; due to the synergistic effect of the cellulose ether and the starch ether, the water-retaining property and the application property of the internal wall putty are ensured; and because the polymer latex powder is added, the flexibility of the internal wall putty and the adhesion of the polymer latex powder and the wall are improved.

Description

technical field [0001] The invention belongs to the technical field of building materials, and in particular relates to an environment-friendly, water-resistant and moisture-proof interior wall putty and a production process thereof. Background technique [0002] In the current decoration market, interior wall putty is widely used as a leveling material for wall protection. Because it is used on the interior wall, the environment of the interior wall is not as harsh as the outdoor environment, so people generally do not have high requirements for the putty on the interior wall, which leads to the generally poor quality of the putty on the interior wall. [0003] The main component of the current popular interior wall putty is Shuangfei powder (mainly composed of calcium and magnesium). By adding 107 glue (scientific name is polyvinyl formal adhesive, it is an adhesive formed by a solution or emulsion with water as the medium). agent), 801 glue (made by polyvinyl alcohol and...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B28/04C04B24/26C04B24/42C04B24/38
Inventor 张立功
Owner 黄明杰
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More