Spinning oil for fine-denier melt-spun spandex fiber

A technology of spandex fiber and spinning oil, which is applied in the field of textile auxiliaries to achieve the effects of good removability, good temperature adaptability, easy washing and removal

Inactive Publication Date: 2013-05-01
TIANJIN POLYTECHNIC UNIV +1
View PDF4 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Within the scope of the applicant's literature search, the spandex oil agent suitable for the spinning and post-processing production of the fine-denier melt-spun spandex fibers has not been reported yet.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0032] At a temperature of 20°C, add the materials according to the following weight percentage composition into a reaction kettle with a stirrer and stir for 90 minutes to obtain the oil agent:

[0033] Simethicone 40%;

[0034] Amino modified silicone oil 45%;

[0035] Polyether modified silicone oil 5%;

[0036] Fatty alcohol polyoxyethylene ether 9%;

[0037] Alkyl alcohol polyoxyethylene ether phosphate potassium salt Balance.

Embodiment 2

[0039] At a temperature of 25°C, add the materials according to the following weight percentage composition into a reaction kettle with a stirrer and stir for 60 minutes to obtain the oil agent:

[0040] Simethicone 58%;

[0041] Amino modified silicone oil 17%;

[0042] Polyether modified silicone oil 14%;

[0043] Fatty alcohol polyoxypropylene ether 7%;

[0044] Alkyl alcohol polyoxyethylene ether phosphate potassium salt Balance.

Embodiment 3

[0046] At a temperature of 30°C, add the materials according to the following weight percentage composition into a reaction kettle with a stirrer and stir for 30 minutes to prepare the oil agent:

[0047] Simethicone 48%;

[0048] Amino modified silicone oil 27%;

[0049] Polyether modified silicone oil 23%;

[0050] Fatty alcohol polyoxyethylene polyoxypropylene ether 1%;

[0051] Alkyl alcohol polyoxyethylene ether phosphate potassium salt Balance.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses spinning oil for a fine-denier melt-spun spandex fiber. The oil comprises the following components by weight percentage: 30-60% of dimethyl silicon oil, 30-50% of modified silicone oil, 0-10% of nonionic surfactant and the balance of other additive, wherein the modified silicone oil is amino modified silicone oil or polyether modified silicone oil; polysiloxane chain segments m and n in the amino modified silicone oil are equal to 30-120; an adduct number b of polyoxyethylene chain segments in the polyether modified silicone oil is equal to 0-10; an adduct number a of polyoxypropylene chain segments is equal to 0-10; the nonionic surfactant is fatty alcohol polyoxyethylene ether, fatty alcohol polypropylene oxide ether or fatty alcohol polyoxyethylene polyoxypropylene ether; and other additive is phosphate potassium salt of alkyl alcohol polyoxyethylene ether.

Description

technical field [0001] The invention relates to a textile auxiliary agent, in particular to a fine-denier melt-spun spandex fiber spinning oil. Background technique [0002] Spandex fiber is the abbreviation of polyurethane fiber. It is a block copolymer obtained by polymerization of diol and diisocyanate, and then synthesized by dry method, wet method or melt spinning. fiber. Spandex has the characteristics of high elongation and high elasticity, and is a kind of high elastic fiber. It is often made into core-spun yarn with other fibers, and used to make elastic parts of various underwear, swimwear, tights, jeans, sportswear, etc. Although the amount of spandex used in the fabric is small, it can change the stretching effect of the fabric, improve the wearing performance of the product, improve the sense of oppression and freedom of movement of the relevant parts of the human body, and have perfect comfort and good fit. As a result, the grade of the product is greatly im...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): D06M15/643D06M15/647D06M101/38
Inventor 周存郑帼刘燕军徐进云辛丽霞孙玉
Owner TIANJIN POLYTECHNIC UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products