Straight conveyor belt finger-model connector and preparation method thereof

A finger joint and conveyor belt technology, which is applied in the field of straight conveyor belt finger joints and its preparation, can solve the problems of the strength of the conveyor belt joint being difficult to solve, and achieve the effects of reducing capital investment, reducing maintenance and improving joint quality.

Active Publication Date: 2013-05-01
YANKUANG GRP CO LTD +1
View PDF5 Cites 11 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] However, the problem of the joint strength of the straight conveyor belt has been difficult to solve
This means that under such ideal conditions, the strength of the existing straight conveyor belt finger joints can only reach 80% of the strength of the straight conveyor belt itself.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Straight conveyor belt finger-model connector and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0028] From figure 1 It can be seen that a straight conveyor belt finger joint of the present invention includes a straight finger skeleton structure 4, which includes a straight canvas layer; There is an adhesive layer 2 on the surface; on the adhesive layer 2 there is a reinforcing fabric layer 3; on the fabric layer 3 there is a covering adhesive layer 1.

[0029] The fabric layer 3 is made of steel screen or aramid mesh cloth. It has high warp strength, small warp density, and obvious gaps between warp threads.

[0030] The length of the fabric layer 3 is 1000mm-3000mm. The strength of the fabric layer 3 is 10%-20% of the strength of the straight conveyor belt.

[0031] The warp direction of the fabric layer 3 is parallel to the warp direction of the straight conveyor belt.

[0032] The thickness of the adhesive layer 2 is 1-2mm.

[0033] The preparation method of described straight through conveyer belt finger joint, comprises the following steps:

[0034] (1) Strip...

Embodiment 2

[0042] From figure 1 It can be seen that a straight conveyor belt finger joint of the present invention includes a straight finger skeleton structure 4, which includes a straight canvas layer; There is an adhesive layer 2 on the surface; on the adhesive layer 2 there is a reinforcing fabric layer 3; on the fabric layer 3 there is a covering adhesive layer 1.

[0043] The fabric layer 3 is made of steel screen or aramid mesh cloth. It has high warp strength, small warp density, and obvious gaps between warp threads.

[0044] The length of the fabric layer 3 is 1500mm-2000mm. The strength of the fabric layer 3 is 10%-20% of the strength of the straight conveyor belt.

[0045] The warp direction of the fabric layer 3 is parallel to the warp direction of the straight conveyor belt.

[0046] The thickness of the adhesive layer 2 is 1-2mm.

[0047] The preparation method of described straight through conveyer belt finger joint, comprises the following steps:

[0048] (1) Strippi...

Embodiment 3

[0056] [0040] From figure 1 It can be seen that a straight conveyor belt finger joint of the present invention includes a straight finger skeleton structure 4, which includes a straight canvas layer; There is an adhesive layer 2 on the surface; on the adhesive layer 2 there is a reinforcing fabric layer 3; on the fabric layer 3 there is a covering adhesive layer 1.

[0057] The fabric layer 3 is made of steel screen or aramid mesh cloth. It has high warp strength, small warp density, and obvious gaps between warp threads.

[0058] The length of the fabric layer 3 is 2500mm. The strength of the fabric layer 3 is 10%-20% of the strength of the straight conveyor belt.

[0059] The warp direction of the fabric layer 3 is parallel to the warp direction of the straight conveyor belt.

[0060] The thickness of the adhesive layer 2 is 1-2mm.

[0061] The preparation method of described straight through conveyer belt finger joint, comprises the following steps:

[0062] (1) St...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
lengthaaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention belongs to the technical field of a rubber conveyor belt product, and particularly relates to a straight conveyor belt finger-model connector and a preparation method thereof. The straight conveyor belt finger-model connector comprises a straight finger-model skeleton structure, wherein the straight finger-model skeleton structure comprises a straight canvas layer; a rubberizing layer is arranged on the surface of the straight finger-model skeleton structure; a textile layer playing a reinforcement effect is arranged on the rubberizing layer; and a coverage rubber layer is arranged on the textile layer. The preparation method of the straight conveyor belt finger-model connector comprises the following steps of (1) stripping coverage adhesive; (2) removing residual adhesive; (3) cutting a finger model; (4) coating adhesive cement; (5) splicing the finger model; (6) forming a finger-model connector; and (7) vulcanizing the finger-model connector. Due to the adoption of the straight conveyor belt finger-model connector, the strength of the connector is improved; and the preparation method is simple and easy to operate.

Description

technical field [0001] The invention belongs to the technical field of rubber conveyor belt products, and in particular relates to a straight conveyor belt finger joint and a preparation method thereof. Background technique [0002] At present, more and more ports, coal, steel, cement and other enterprises have increased the use of conveyor belts in order to improve production efficiency. At the same time, customers have higher and higher requirements for the strength specifications of conveyor belts. Ordinary plain weave canvas is bent up and down due to the warp. When the force is applied vertically and horizontally, part of the force is decomposed to the vertical direction. The higher the strength, the greater the bending degree of the warp and the greater the strength loss. Generally below 630N / mm. [0003] When customers need higher-strength belts, they can only increase the strength by lamination. When the multi-layer skeleton passes through the driving roller, due to...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): B65G15/34B29C65/70B29C35/02B29C37/02B29L29/00
Inventor 王飞汪光亮马洪亮孙桂美张鹏飞杨静吴旗赵连云
Owner YANKUANG GRP CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products