A processing method and technology of imitating ceramics, applied in the field of imitating ceramics, can solve problems such as uneven product quality, complex ceramic sculpture process, and inability to reproduce large quantities of production, and achieve low processing cost, good product quality uniformity, and high simulation degree Effect

Inactive Publication Date: 2013-04-10
SHENZHEN POLYTECHNIC
View PDF5 Cites 8 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] In view of the above-mentioned deficiencies in the prior art, the purpose of the present invention is to provide a processing method for imitating ceramic sculptures, aiming to solve the problems of complex ceramic sculpture process, uneven product quality, and incapable of mass production

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Processing method for ceramic-imitated sculpture

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0031] Prepare art sculpture molding mud: mix component A and component B of art sculpture clay in a weight ratio of 1:1, the component A is epoxy resin, and the component B is a curing agent; after mixing evenly, Add filler to the mixture, wherein the weight ratio between the mixture of component A and component B and the filler is 1:2.5; and according to the color requirements, add 1% of the total weight of art molding clay , to obtain brightly colored art molding clay. Making a skeleton of a sculpture sample, adhering the art sculpture molding clay to the skeleton to form a green body; carving the green body to form a sculpture sample; drying the sculpture sample; grinding and polishing. The sculpture sample is sprayed with transparent glossy varnish and kept at 30°C.

Embodiment 2

[0033] Prepare art sculpture molding clay: mix component A and component B of art sculpture clay in a weight ratio of 1:1, the component A is epoxy resin, and the component B is a curing agent; after mixing evenly, Add filler to the mixture, wherein the weight ratio between the mixture of component A and component B and the filler is 1:1.5; and according to the color requirements, add 5% of the total weight of art molding clay , to obtain brightly colored art molding clay. Making a skeleton of a sculpture sample, adhering the art sculpture molding clay to the skeleton to form a green body; carving the green body to form a sculpture sample; drying the sculpture sample; grinding and polishing. The sculpture samples were sprayed with transparent varnish and kept at 25°C.

Embodiment 3

[0035] Prepare art sculpture molding clay: mix component A and component B of art sculpture clay in a weight ratio of 1:1, the component A is epoxy resin, and the component B is a curing agent; after mixing evenly, Add fillers to the mixture, wherein the weight ratio between the mixture of component A and component B and the filler is 1:1; and according to the color requirements, add 10% of the coloring material accounting for the total weight of art molding clay , to obtain brightly colored art molding clay. Making a skeleton of a sculpture sample, adhering the art sculpture molding clay to the skeleton to form a green body; carving the green body to form a sculpture sample; drying the sculpture sample; grinding and polishing. The sculpture sample is sprayed with transparent glossy varnish and kept at 35°C.

[0036] The preparation of existing ceramics takes a long time, and defects such as cracks are prone to occur in the process of shaping and firing, and the yield of fini...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a processing method for a ceramic-imitated sculpture, which is characterized in that the ceramic-imitated sculpture is manufactured with artistic sculpture forming clay. The processing method comprises the following steps: 1, preparing artistic sculpture forming clay; 2, processing a sculpture sample with the artistic sculpture forming clay and drying; and 3, spraying transparent bright paint onto the sculpture sample and drying to obtain a finished product. According to the invention, the sculpture is manufactured and processed with the artistic sculpture forming clay, so that sun crack does not occur easily in the manufacturing process, the degree of simulation to ceramic of the obtained sculpture product is high, the processing technique is simple, the processing cost is low, and the quality uniformity of the product is good; and besides, industrial mass production of the product can be realized by manufacturing silicone rubber dies, and the processing method has very high application values.

Description

technical field [0001] The invention relates to the technical field of imitation ceramics, in particular to a processing method for imitation ceramic sculptures. Background technique [0002] The traditional ceramic craft has captivated countless collectors at home and abroad with its unique charm, and it has been passed down to the present for its practical application value. However, the ceramic process is complicated, the energy consumption is large, and the price is relatively high. These shortcomings affect the application of ceramics. The process for ceramic sculpture is more complicated, and due to certain conditions in the processing process, the sculpture is easy to dry and crack, and the product quality is uneven, which further increases the production cost of ceramic sculpture and hinders the development of ceramic sculpture technology. [0003] Therefore, the prior art still needs to be improved and developed. Contents of the invention [0004] In view of...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): B44C3/06
Inventor 张时光陈琳琳罗参
Owner SHENZHEN POLYTECHNIC
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka