Preparation method of crystallite glass with low expansion rate

A technology of glass-ceramics and low expansion rate, which is applied in the field of low-expansion glass-ceramic preparation, can solve the problems of complex crystallization process and glass performance damage, and achieve the effect of reducing expansion coefficient and ensuring performance

Inactive Publication Date: 2013-03-27
JIANGSU YITA NEW MATERIAL TECH
View PDF2 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Due to the complex crystallization process of this system, the precipitation of heterogeneous crystal phases will lead to the destruction of glass properties due to phase change

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

specific Embodiment approach

[0010] (1) Weigh glass raw materials, the weight percentage is, MgO15.2kg, Al 2 o 3 22.3kg, SiO 2 48kg, CaO2kg, B 2 o 3 2kg, Sb 2 o 3 0.5kg, ZnO 2 10kg;

[0011] (2) Mix the above raw materials and add them into the crucible, raise the temperature to 1550°C, keep it warm for 4h, then lower it to 1450°C and keep it warm for 1h;

[0012] (3) Then cast into a thin plate and anneal at 680°C for 5 hours to obtain the basic glass;

[0013] (4) The basic glass is then nucleated and crystallized. The nucleation temperature is 750°C, the nucleation time is 1h, the crystallization temperature is 1075°C, and the crystallization time is 1.5h.

[0014] The obtained glass-ceramic with a small expansion coefficient is 23.535×10 / ℃.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a preparation method of crystallite glass, in particular to a preparation method of crystallite glass with a low expansion rate. According to the specific technical scheme, the preparation method comprises the following steps: weighing glass raw material, evenly mixing the raw material and putting into a crucible; heating up to 1550 DEG C, carrying out heat preservation for 4h, cooling to 1450 DEG C and carrying out heat preservation for 1h; carrying out annealing treatment for 5h at the temperature of 680 DEG C to obtain base glass; and then carrying out coring and crystallization, wherein the coring temperature is 750 DEG C, the coring time is 1h, the crystallization temperature is 1075 DEG C, and the crystallization time is 1.5h. The production method provided by the invention is capable of effectively separating out cordierite and reducing the expansion factor, thus guaranteeing the performances of the crystallite glass.

Description

technical field [0001] The invention relates to a method for preparing a glass-ceramic, in particular to a method for preparing a glass-ceramic with a low expansion rate. Background technique [0002] MgO-A1 2 o 3 -SiO 2 The glass-ceramic has excellent high-frequency electrical properties, high mechanical strength, good thermal shock resistance and thermal stability, and has been widely used in electronics, aerospace, machinery and other fields. These superior properties are derived from cordierite (2MgO·2A1 2 o 3 ·5SiO2 2 ) The precipitation of the main crystal phase. The thermal expansion coefficient of cordierite is isotropic. As the temperature increases, it expands in the c-axis direction but contracts in the a-axis direction, resulting in zero volume expansion. Due to the complex crystallization process of this system, the precipitation of heterogeneous crystal phases will lead to the destruction of glass properties due to phase change. Contents of the inventi...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C03C10/08
Inventor 蒋达光顾玉华岳丹
Owner JIANGSU YITA NEW MATERIAL TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com