Solid water ball silicon composite fertilizer and preparation process

A compound fertilizer and solid water technology, applied in fertilization devices, fertilizer mixtures, applications, etc., can solve the problems that the alkalinity of silicon compound fertilizers affects crop growth, etc., and achieve the effects of solving the problem of solidification, improving the emergence rate, and being easy to use

Inactive Publication Date: 2012-08-29
中国冶金矿业长春矿产资源开发有限公司
View PDF10 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The invention discloses a solid water polo silicon compound fertilizer, which solves the problem of the solidification of the silicon compound fertilizer and the defect that the traditional liquid silicon fertilizer is too alkaline to affect the growth of crops

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0020] 1) Will contain SiO 2 25%, K 2 After diluting 10L of O10% (M3.9) potassium silicate with four times of water, add 20L of urea solution containing 1000g and 10L of 5% glucose solution, stir, mix and dissolve to form a silicon composite sol.

[0021] 2) Put the specific gravity to 1.7g / cm 3 600mL of phosphoric acid was diluted 3 times; the silicon composite solution and dilute phosphoric acid were pumped into two low-pressure cylinders respectively, and compressed air was introduced respectively, and the internal pressure of the cylinder was maintained at 0.1-0.2MPa, and the valve was opened to make the phosphoric acid and silicon composite sol Enter the nozzle, quickly mix and neutralize to form a mixed sol, and drop into pellets in the air through the nozzle. Because the nozzle and the receiving tank have a drop of more than 3m, the pellets will gel within 3m of falling time to form solid water polo. Silicon compound fertilizer falls into the Receiving tank, the react...

Embodiment 2

[0026] 1) Will contain SiO 2 20%, K 2 After diluting 10L of O10% potassium silicate with four times of water, add 20L of urea solution containing 1000g and 10L of 5% glucose solution, stir, mix and dissolve to form a silicon composite sol.

[0027] 2) Put the specific gravity to 1.7g / cm 3 600mL of phosphoric acid was diluted 3 times; the silicon composite solution and dilute phosphoric acid were pumped into two low-pressure cylinders respectively, and compressed air was introduced respectively, and the internal pressure of the cylinder was maintained at 0.1-0.2MPa, and the valve was opened to make phosphoric acid and silicon composite sol Enter the nozzle, quickly mix and neutralize to form a mixed sol, and drop into pellets in the air through the nozzle. Because the nozzle and the receiving tank have a drop of more than 3m, the pellets will gel within 3m of falling time to form solid water polo. Silicon compound fertilizer falls into the Receiving tank, the reaction conditi...

Embodiment 3

[0032] Example 3:

[0033] 1) Will contain SiO 2 15%, K 2 After diluting 10L of O10% potassium silicate with four times of water, add 20L of urea solution containing 1000g and 10L of 5% glucose solution, stir, mix and dissolve to form a silicon composite sol.

[0034] 2) Put the specific gravity to 1.7g / cm 3 600mL of phosphoric acid was diluted 3 times; the silicon composite solution and dilute phosphoric acid were pumped into two low-pressure cylinders respectively, and compressed air was introduced respectively, and the internal pressure of the cylinder was maintained at 0.1-0.2MPa, and the valve was opened to make phosphoric acid and silicon composite sol Enter the nozzle, quickly mix and neutralize to form a mixed sol, and drop into pellets in the air through the nozzle. Because the nozzle and the receiving tank have a drop of more than 3m, the pellets will gel within 3m of falling time to form solid water polo. Silicon compound fertilizer falls into the Receiving tan...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides a solid water ball silicon composite fertilizer, and also discloses a preparation process of the composite fertilizer. Potash water glass of potassium silicate is used as a base material, urea and sugar are mixed and added to be dissolved into solution dilutedly, and then the mixture and diluted phosphoric acid are prepared into the fertilizer through a nozzle by using an air granulation method. The fertilizer is a neutral slow release fertilizer; the solid water ball contains more than 80 percent of water; the fertilizer can be fed together with seeds during mechanical seeding; the effects of resisting against drought in spring and improving the rate of emergence can be achieved, and the fertilizer is convenient to use; and the problem of solidification of the silicon composite fertilizer is solved and the defect of influence on crop growth due to over high alkalinity of the conventional liquid silicon fertilizer is overcome.

Description

[0001] technical field [0002] The invention provides a solid water polo silicon compound fertilizer, and also discloses a preparation process of the compound fertilizer, which belongs to the technical field of solid water-based liquid fertilizer. technical background [0003] In the field of agricultural technology, silicon is an indispensable nutrient for the normal growth and development of rice, wheat, corn, soybeans, peanuts and other crops, and is the fourth element required by plants after nitrogen, phosphorus and potassium. Therefore, increasing the application of silicon fertilizer has a significant effect on increasing the yield of crops. However, for a long time, farmers have lacked awareness of the importance of silicon fertilizers and neglected the input of silicon fertilizers, resulting in a lack of silicon in the soil. Therefore, silicon has become a limiting factor affecting high and stable yields of crops. We must see that silicon is an important nutrient ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C05G1/00C05D9/00
Inventor 崔湘浩刘畅刘润华冯文龙王天龙王贺群
Owner 中国冶金矿业长春矿产资源开发有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com