Polypropylene-based microcellular foaming wood-plastic composite material and production method thereof

A production method and microcellular foaming technology, which is applied in the field of wood-plastic composite materials, can solve the problems of large wear of extruder barrel and screw, limited application range of materials, and short service life of extruder, so as to prolong the service life , reduce material density, and protect the environment

Active Publication Date: 2013-08-21
SHANDONG UNIV OF TECH
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

This material has a higher density, about 1.3kg / m 3 , the application of the material is limited
This production process has a relatively large wear on the extruder barrel and screw, resulting in a relatively short service life of the extruder

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Polypropylene-based microcellular foaming wood-plastic composite material and production method thereof
  • Polypropylene-based microcellular foaming wood-plastic composite material and production method thereof
  • Polypropylene-based microcellular foaming wood-plastic composite material and production method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1-3

[0024] Embodiment 1-3: formula (unit: weight part)

[0025]

Example 1

Example 2

Example 3

Polypropylene

70

70

70

Low-density polyethylene

30

30

30

Nano calcium carbonate

5

5

5

[0026] biomass powder

50

50

50

Compatibilizer

6

6

6

lubricant

2.5

2.5

2.5

[0027] Preparation method: prepare according to the formula of Example 1-3.

[0028] 1) Add biomass powder and nano-calcium carbonate into a high-mixer and mix in a weight ratio of 10:1, the mixing temperature is 105°C-110°C, and the mixing time is 15-20 minutes;

[0029] 2) Add 70 parts of polypropylene, 30 parts of low-density polyethylene, 50 parts of treated biomass powder, 6 parts of compatibilizer, and 0.5, 1.5, and 2.5 parts of lubricant into a high-speed mixer in proportion by weight. The temperature is 105°C-110°C, and the mixing time is 15-20 minut...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
melt flow indexaaaaaaaaaa
softening pointaaaaaaaaaa
Rockwell hardnessaaaaaaaaaa
Login to View More

Abstract

The invention provides a polypropylene-based microcellular foaming wood-plastic composite material and a production method thereof, belonging to the technical field of a wood-plastic composite material. The polypropylene-based microcellular foaming wood-plastic composite material is characterized by being prepared from the following raw materials in parts by weight: 70 parts of polypropylene, 30 parts of low-density polyethylene, 30-70 parts of biomass powder, 3-7 parts of nanometer calcium carbonate, 2-8 parts of compatilizer, 0.5-2.5 parts of foaming agent and 2-8 parts of lubricant. The problem of severe corrosion of a material cylinder and a screw of an extruder can be effectively solved by adjusting the ingredient formula of the property components and the processing agents, so that the service life of the extruder is prolonged. Furthermore, the continuous and uniform microcellular foaming wood-plastic composite material is obtained, the material density is reduced, and the application range of the material is enlarged. Therefore, the biomass powder is widely recycled, the waste material is recycled, and the environment is protected.

Description

technical field [0001] The invention belongs to the technical field of wood-plastic composite materials, and in particular relates to a polypropylene-based wood-plastic microporous foam composite material and a production method thereof. Background technique [0002] Wood-plastic composite material refers to the use of biomass powder (wood powder, agricultural straw powder, etc.) High-pressure extruded, cooled and processed into a reversible and recycled high-quality material. This type of material has the advantages of acid and alkali resistance, low water absorption, not easy to deform, good mechanical properties, and can be recycled. This material has a higher density, about 1.3kg / m 3 , the scope of application of the material is limited. This production process has relatively large wear and tear on the extruder barrel and screw, resulting in a relatively short service life of the extruder. Contents of the invention [0003] In order to solve the problem of wear and...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08L23/12C08L23/06C08L97/02C08L51/06C08K13/02C08K3/26C08J9/04B29C47/92B29C48/92
CPCB29C48/04B29C48/40B29C48/92B29C2948/92514B29C2948/9259B29C2948/92704B29C2948/92885B29C2948/92895B29C2948/92904
Inventor 蔡红珍柏雪源易维明高巧春
Owner SHANDONG UNIV OF TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com