Flame-resistant polycarbonate resin composition

A technology of resin composition and flame retardant, which is applied in the field of flame retardant polycarbonate resin composition, and can solve the problems of difficulty in coloring transparent colors, lower light transmittance, lower transparency, etc.

Inactive Publication Date: 2012-05-02
TEIJIN KASEK KK
View PDF17 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Therefore, the reduction of transparency, that is, the reduction of light transmittance will make it difficult to color the transparent color, so that the overall design space including the part of feeling and the coloring that imparts light diffusing property becomes smaller.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Flame-resistant polycarbonate resin composition
  • Flame-resistant polycarbonate resin composition
  • Flame-resistant polycarbonate resin composition

Examples

Experimental program
Comparison scheme
Effect test

Embodiment approach

[0166] Hereinafter, the present invention will be described in detail through examples. In addition, evaluation was performed by the following method.

[0167] (1) Flame retardancy: The pellets obtained by the following method were dried at 120° C. for 6 hours with a hot air dryer. Then, by an injection molding machine (IS150EN-5Y, manufactured by Toshiba Machinery Co., Ltd.), under the condition that the cylinder temperature is 280°C and the mold temperature is 60°C, a test piece for the UL94 combustion test with a thickness of 2mm is molded, and the test piece is carried out. UL Specification 94 vertical burning test for evaluation. For the test pieces that do not meet any of the grades of V-0, V-1 and V-2, record it as not V.

[0168] (2) Total light transmittance: The pellets obtained by the following method were dried at 120° C. for 6 hours with a hot air dryer. Then, using an injection molding machine (SG-150U, manufactured by Sumitomo Heavy Industries, Ltd.), under t...

Embodiment 1～22 and comparative example 1～5

[0171]In the polycarbonate resin powder produced by the interfacial polycondensation method from bisphenol A and phosgene, various additives were blended in the amounts recorded in the table, mixed with a mixer, and then extruded with a vented twin-screw extruder ( TEX30α (complete teeth, same direction of rotation, two-flight screw), manufactured by Nippon Steel Works, Ltd.) was melt-kneaded to obtain pellets. The additives were pre-mixed with the polycarbonate resin powder in advance using a Henschel mixer at a concentration 10 times the compounding amount, and then overall mixed with the mixer. Extrusion conditions were as follows: extrusion rate: 20 kg / h; screw rotation speed: 150 rpm; vacuum degree of the exhaust part: 3 KPa; extrusion temperature: 260° C. from the first supply port to the extrusion die.

[0172] The content of each component represented by the symbol in a table|surface is as follows.

[0173] (A component)

[0174] PC-1: linear aromatic polycarbonate r...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
glass transition temperatureaaaaaaaaaa
thicknessaaaaaaaaaa
water absorptionaaaaaaaaaa
Login to View More

Abstract

To provide a flame-resistant polycarbonate resin composition having prescribed-range transparency and having excellent flame resistance. This flame-resistant polycarbonate resin composition contains 0.1-0.2 pt.wt. of polytetrafluoroethylene (B component) having fibril-forming capability and 0.001-20 pts.wt. of a flame retardant (C component) based on 100 pts.wt. of an aromatic polycarbonate-based resin (A component).

Description

[0001] This application is a divisional application of the application dated May 26, 2008, the application number is 200810098983.1, and the invention name is "flame-retardant polycarbonate resin composition". technical field [0002] The invention relates to a flame-retardant polycarbonate resin composition. More specifically, it relates to a flame-retardant polycarbonate resin composition excellent in transparency and flame retardancy. Background technique [0003] Since the aromatic polycarbonate resin not only has transparency or excellent heat resistance and strength but also has a certain flame retardancy, it is widely used in various fields. However, it cannot be said that the flame retardancy of aromatic polycarbonate resins is not as good as that of flame retardancy due to the improvement of flame retardancy requirements for electronic and electrical equipment parts, OA related parts, etc., or the improvement of flame retardancy caused by the thinning of products in...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L69/00C08L27/18C08K5/00C08K5/42
Inventor 大平洋二友田琢也品川佳久
Owner TEIJIN KASEK KK
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More