Fire-retardant polyolefin based wood plastic composite material and preparation method thereof

A wood-plastic composite material and polyolefin-based technology, applied in the field of wood-plastic composite materials and their preparation, can solve the problems of high heat release rate and large smoke production, and achieve a wide range of applications, strong wood feeling, and excellent smoke suppression. performance effect

Active Publication Date: 2012-12-12
NORTHEAST FORESTRY UNIVERSITY
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The present invention aims to solve the problems of high heat release rate, large smoke production, and easy generation of CO harmful gas when the existing flame-retardant wood-plastic composite material burns, and provides a flame-retardant polyolefin-based wood-plastic composite material and its preparation method

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

specific Embodiment approach 1

[0013] Specific Embodiment 1: In this embodiment, the flame-retardant polyolefin-based wood-plastic composite material consists of 30-70 parts by weight of wood fiber material, 2-8 parts of coupling agent, 0.5-4 parts of lubricant, 20-50 parts of plastic, 0.01-1 part of antioxidant, 8-30 parts of nano-inorganic flame retardant and 0-5 parts of mineral filler; the lignocellulosic materials are wood powder, rice husk powder, One or a mixture of bamboo chips, straw powder, fruit shell powder, bagasse; the coupling agent is a silane coupling agent, an aluminate coupling agent, a titanate coupling agent, polymethylene Polyphenylisocyanate, maleic anhydride, maleic anhydride graft-modified polyethylene, maleic anhydride graft-modified polypropylene, or a mixture of isocyanates; the lubricant is polyethylene wax, polypropylene Wax, paraffin, stearic acid, zinc stearate, calcium stearate or a mixture of several; plastics are one or more of polyethylene, polypropylene, recycled polyeth...

specific Embodiment approach 2

[0015] Embodiment 2: The difference between this embodiment and Embodiment 1 is that the flame-retardant polyolefin-based wood-plastic composite material consists of 30 parts by weight of wood fiber material, 2 parts of coupling agent, and 0.5 parts of lubricant, 20 parts of plastic, 0.01 part of antioxidant and 8 parts of nano inorganic flame retardant. Others are the same as in the first embodiment.

specific Embodiment approach 3

[0016] Embodiment 3: The difference between this embodiment and Embodiment 1 is that the flame-retardant polyolefin-based wood-plastic composite material consists of 70 parts by weight of wood fiber material, 8 parts of coupling agent, and 4 parts of lubricant, 50 parts of plastic, 1 part of antioxidant, 30 parts of nano inorganic flame retardant and 5 parts of mineral filler. Others are the same as in the first embodiment.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
bending strengthaaaaaaaaaa
flexural modulusaaaaaaaaaa
heat release rateaaaaaaaaaa
Login to View More

Abstract

The invention discloses a fire-retardant polyolefin based wood plastic composite material and a preparation method thereof, and relates to a wood plastic composite material and a preparation method thereof, and the composite material and method provided by the invention can be used for solving problems that the existing fire-retardant wood plastic composite material has high heat release efficiency in burning and high smoke production, and can generate CO harmful gas easily. The flame-retardant polyolefin based wood plastic composite material is prepared from wood fiber materials, plastics, acoupling agent, a lubricant, an antioxidant, a nano inorganic fire retardant and a mineral filler. The method comprises the following steps: putting the wood fiber materials, the coupling agent and the lubricant into a high-speed mixing machine for hot mixing; then putting into a cold mixing machine for cold mixing, sending the plastics, the antioxidant, the nano inorganic fire retardant and the mineral filler into the cold mixing machine and then mixing; and then carrying out fusing and extruding for granulation by adopting extruding, injection, hot compressing or mold compression for molding, thus the fire-retardant polyolefin based wood plastic composite material is obtained. The wood plastic composite material provided by the invention has low heat release rate in burning and less smoke production, and is healthy and environmentally-friendly, and can be widely applied to the fields of indoor construction, decoration and furnishing materials and the like.

Description

technical field [0001] The invention relates to a wood-plastic composite material and a preparation method thereof. Background technique [0002] Wood-plastic composite materials are made by adding lignocellulosic materials such as wood, rice husk, bamboo chips, hemp, straw, nut shells, etc. in the form of powder, fiber, or shavings as reinforcements or fillers to thermoplastics through melting and compounding. A new class of composite materials obtained. Compared with traditional wooden materials, it has the advantages of not being afraid of insects, water resistance, corrosion resistance, not easy to crack and not easy to absorb moisture and deform, etc. It can be widely used in doors, windows, floors, ceilings and various construction and decoration fields. and automotive lining materials. In addition, polyolefin-based wood-plastic composite materials can be reused and recycled, which is environmentally friendly and has low maintenance costs. [0003] However, as a woo...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08L97/02C08L23/00C08L23/06C08L23/12C08K13/02C08K3/22C08K3/34C08K3/38B29B9/06B29C47/92B29C48/92
CPCB29C48/04
Inventor 宋永明王清文杨伟军王伟宏隋淑娟
Owner NORTHEAST FORESTRY UNIVERSITY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com