Mineral composite capable of removing mycotoxin as well as preparation method and application thereof

A mycotoxin and compound technology, applied in the field of mineral compounds, can solve the problems of cumbersome preparation methods, high cost, and poor effect of removing mycotoxins, achieve good adsorption effect, reduce feed cost, improve production performance and feed conversion rate effect

Active Publication Date: 2011-09-14
INST OF ANIMAL SCI OF CHINESE ACAD OF AGRI SCI
View PDF3 Cites 20 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] There are many kinds of mycotoxin removal agents available for removing mycotoxins in feed. Most of them have a certain effect on the removal of mycotoxins in feed, but they all have poor mycotoxin removal effects to varying degrees, Defects such as tedious preparation method or high cost need to be improved

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Mineral composite capable of removing mycotoxin as well as preparation method and application thereof
  • Mineral composite capable of removing mycotoxin as well as preparation method and application thereof
  • Mineral composite capable of removing mycotoxin as well as preparation method and application thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0027] Preparation of Preliminary Example 1 High Purity Montmorillonite

[0028] 1. After the montmorillonite raw ore is crushed, take 50g sample and add 1L water (5% slurry concentration), mechanically stir for 15min, let it stand for 2min, and extract the supernatant by siphon method;

[0029] 2. Discard the coarse slag (impurities insoluble in water), add 4% sodium pyrophosphate dispersant (promote dispersion and suspension) to the upper liquid, stir, and draw out the upper slurry after standing and settling, and discard the middle slag;

[0030] 3. Centrifuge the upper slurry at high speed for 10 minutes, dry the upper high-purity slurry, and obtain high-purity montmorillonite after crushing.

Embodiment 2

[0031] Preliminary Example 2 Preparation of High Purity Attapulgite

[0032] 1. After the attapulgite raw ore is crushed, take 50g sample and add 1L water (5% pulp concentration), stir mechanically for 15min, let it stand for 2min, and extract the supernatant by siphon method;

[0033] 2. Discard the coarse slag (impurities insoluble in water), add 4% sodium pyrophosphate dispersant (promote dispersion and suspension) to the upper liquid, stir for a certain period of time, take out the upper slurry after standing and settling, and discard the middle slag;

[0034] 3. Centrifuge the upper slurry at high speed for 10 minutes, dry the upper high-purity slurry, and obtain high-purity attapulgite after crushing.

[0035] The preparation of embodiment 1 mineral complex

[0036] Get the high-purity montmorillonite and attapulgite prepared in preliminary examples 1 and 2, and make the two into suspensions with a concentration of 2% (g / ml) respectively, after soaking for 2 hours, acco...

Embodiment 3

[0039] Example 3 Preparation of mineral complex

[0040]Get the high-purity montmorillonite and attapulgite prepared in preparatory examples 1 and 2, and make the two into suspensions with a concentration of 10% (g / ml) respectively. After soaking for 2 hours, follow the montmorillonite: attapulgite= The two suspensions were mixed at a mass ratio of 9:1, stirred magnetically for 2 hours, centrifuged at 2000 r / min for 10 minutes, dried, and the prepared compound was passed through a 200-mesh sieve to obtain the product.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a mineral composite capable of removing mycotoxin as well as a preparation method and application thereof. In the preparation method, by utilizing the characteristics of stable structure, strong adsorption and the like of high-purity montmorillonite and attapulgite, and the high-purity montmorillonite and the attapulgite are mixed in an aqueous solution and stirred, interact and intercalate to obtain the mineral composite. The mineral composite can be used for effectively removing the mycotoxin in a feed, and especially has a cooperative and synergistic adsorption effect on T-2 toxin. The mineral composite can be used as a mildew removing agent or feed additive, and the dosage of the mineral composite in the feed can be 0.3-1.5wt%; and the mineral composite can effectively adsorb various mycotoxins in the feed, and has the functions of improving the feed conversion rate, reducing the feed cost, reducing diarrhea and the like.

Description

technical field [0001] The present invention relates to a mineral compound, in particular to a mineral compound capable of effectively adsorbing mycotoxins and a preparation method thereof. The present invention also relates to the application of the mineral compound as a mildew remover or feed additive, belonging to the field of mineral compounds . Background technique [0002] Montmorillonite, also known as bentonite, is a silicate with a layered chain structure, which has various properties such as thixotropy, adsorption, and suspension. Attapulgite, also known as palygorskite, has an intermediate structure between a chain structure and a layered structure. Montmorillonite and attapulgite have been widely used in the feed industry. As feed additives, they can promote the metabolism of animal organisms, improve feed conversion rate, make animals have strong appetite, thick fur, fast weight gain, early slaughter, and reduce feeding costs. Montmorillonite and attapulgite a...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): A23L1/015A23K1/175A23K20/28A23L5/20
Inventor 张军民马悦培李超孟艳莉
Owner INST OF ANIMAL SCI OF CHINESE ACAD OF AGRI SCI
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com