Method of stone-like surface treatment for glass-ceramic surface

A treatment method, the technology of glass-ceramic, applied in the field of architectural ceramics, can solve the problems of monotonous flower shape, poor anti-fouling, unnatural, etc., and achieve a strong decorative effect

Inactive Publication Date: 2011-06-01
骆水根
View PDF0 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At present, the concave-convex feeling on the surface of glass-ceramic is mainly formed by mechanical methods such as manual or computer engraving technology, but the architectural decoration materials made by engraving methods have poor anti-fouling performance, and the flower shape is monotonous and unnatural.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0022] 1. Material selection and pretreatment

[0023] Take a glass-ceramic composite brick that has undergone rough polishing and fine polishing, and use a sandblasting machine to manually sandblast the surface of the glass-ceramic composite brick into a rough surface;

[0024] 2. Cleaning and drying

[0025] Clean the above-mentioned rough-faced glass-ceramic composite bricks, dry them in a drying oven at 50°C, and set them aside;

[0026] 3. Glue

[0027] Add animal glue 1 into hot water at about 90°C at a glue ratio of 0.5:1, place the beaker containing glue in a hot water bath to keep warm, and stir vigorously to become glue evenly;

[0028] 4. Glue

[0029] Apply the prepared glue on the surface of the aforementioned materials, and control the thickness of the glue layer at about 2mm;

[0030] 5. Dry

[0031] Use color-changing silica gel to spread evenly on the adhesive layer, and the moisture in the adhesive layer is quickly absorbed by the color-changing silica g...

Embodiment 2

[0035] 1. Material selection and pretreatment

[0036] Take a glass-ceramic composite brick that has undergone a rough throwing process;

[0037] 2. Cleaning and drying

[0038] Clean the above rough-polished glass-ceramic composite bricks, and then dry them in a drying oven at 60°C for use;

[0039] 3. Glue

[0040] Add animal glue 2 into hot water at about 90°C at a glue ratio of 0.5:1, place the beaker containing glue in a hot water bath to keep warm, and stir vigorously to become glue evenly;

[0041] 4. Glue

[0042] Apply the prepared glue on the surface of the aforementioned materials, and control the thickness of the glue layer at about 1.5mm;

[0043] 5. Dry

[0044] Dry at room temperature for 7.5 hours, then at 50°C for 14 hours, then at 80°C for 24 hours;

[0045] 6. Adhesive cleaning

[0046] After the adhesive layer bursts, it is cleaned up to obtain a stone-faced glass-ceramic composite brick, and the peeled off film is reused as a recycled adhesive.

Embodiment 3

[0048] 1. Material selection and pretreatment

[0049] Take a glass-ceramic composite brick that has not been polished;

[0050] 2. Cleaning and drying

[0051] Clean the above-mentioned unpolished glass-ceramic composite brick, then dry it in a drying oven at 80°C, and set it aside;

[0052] 3. Glue

[0053] Add animal glue 3 into hot water at about 90°C at a glue ratio of 0.5:1, place the beaker containing glue in a hot water bath to keep warm and swell, and stir gently to dissolve it into glue;

[0054] 4. Glue

[0055] Apply the prepared glue on the surface of the aforementioned materials, and control the thickness of the glue layer at about 2.0mm;

[0056] 5. Dry

[0057] Dry at room temperature for 3h, then at 50°C for 2h, then at 80°C for 18.5h;

[0058] 6. Adhesive cleaning

[0059] After the adhesive layer bursts, it is cleaned up to obtain a stone-faced glass-ceramic composite brick, and the peeled off film is reused as a recycled adhesive.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The present invention discloses a method of the stone-like surface treatment for a glass-ceramic surface, which comprises the following steps: 1. cleaning the surface to be treated and drying; 2. putting gelatin into water to be dissolved for later use; 3. coating the obtained glue on the surface to be treated, and controlling the thickness of the glue layer within 0.5-3 millimeters; 4. placing for more than 3 hours at the room temperature, and then placing for more than 4 hours within the temperature range of 50 DEG C-80 DEG C; and 5 cleaning the surface after the layer bursts. The core technology of the method is the control of the drying process and by using different drying curves of several preferred programs to get different styles of surface effects. The glass-ceramic surface has the same random three-dimensional effects as the surface texture of the natural stones like white marble; and besides, compared with the materials without processing the invention, has better functions of decoration, soil resistance and skid resistance.

Description

technical field [0001] The invention belongs to the technical field of architectural ceramics, in particular to a stone surface treatment method for the surface of glass-ceramics. Background technique [0002] Crystalline glass (CRYSTOE and NEOPARIES), also known as microcrystalline jade or ceramic glass, is a relatively new building material, which is sintered at high temperature with a specific formula of frit. Glass-ceramic looks very different from our common glass, it has dual characteristics of glass and ceramics. In the field of architectural ceramics, there are several types of glass-ceramic composite bricks and glass-ceramics for architectural decoration. Among them, the glass-ceramic composite brick is based on ordinary porcelain bricks, and a layer of glass-ceramics is sintered on it, see Chinese patent 031091903, etc.; glass-ceramics for architectural decoration is a complete glass-ceramic material, see China Patent 021179816, 961141085, etc. Their common feat...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C03C17/28
Inventor 余爱民赵明夏昌奎刘新
Owner 骆水根
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com