Platinum black pulse plating method based on ultrasonic assistance

A pulsed electroplating, ultrasonic-assisted technology, applied in the field of ultrasonic-assisted platinum black pulse electroplating, can solve the problems of poor adhesion between the coating and the substrate, large diameter of platinum black particles, easy to fall off, etc., to achieve increased charge storage, AC impedance Reduced, good binding effect

Inactive Publication Date: 2010-09-01
SHANGHAI JIAO TONG UNIV
View PDF1 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The preparation method of platinum black mentioned in this article is to use direct current electroplating platinum black, the diameter of the platinum black electroplating is larger, the bonding force between the coating and the substrate is not good, and it is easy to fall off and cause failure

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Platinum black pulse plating method based on ultrasonic assistance
  • Platinum black pulse plating method based on ultrasonic assistance

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0019] Such as figure 1 As shown, this embodiment was prepared through the following steps:

[0020] The first step is to clean the platinum electrode and platinum wire auxiliary electrode;

[0021] The cleaning refers to ultrasonic cleaning.

[0022] Step 2: Put the platinum electrode to be electroplated and the platinum wire auxiliary electrode into the electroplating solution vertically, and connect the negative and positive electrodes of the power supply respectively;

[0023] The diameter of the platinum electrode to be electroplated is 60 μm, and the electrode spot width is 60 μm.

[0024] The electroplating solution refers to a solution obtained by dissolving 3 grams of chloroplatinic acid and 0.01 grams of lead acetate in 100 grams of water.

[0025] Step 3: Put the electroplating tank containing the electroplating solution into the ultrasonic generator, turn on the ultrasonic generator and apply pulse current;

[0026] The pulse current refers to a duty cycle of 5μs: 500μs and a ...

Embodiment 2

[0030] Such as figure 2 As shown, this embodiment was prepared through the following steps:

[0031] The first step is to clean the platinum electrode and platinum wire counter electrode to be electroplated;

[0032] The cleaning refers to ultrasonic cleaning.

[0033] Step 2: Put the platinum electrode to be electroplated and the platinum wire auxiliary electrode into the electroplating solution vertically, and connect the negative and positive electrodes of the power supply respectively;

[0034] The diameter of the platinum electrode to be electroplated is 200 μm, and the electrode spot width is 200 μm.

[0035] The electroplating solution refers to a solution obtained by dissolving 3 grams of chloroplatinic acid and 0.01 grams of lead acetate in 100 grams of water.

[0036] Step 3: Put the electroplating tank containing the electroplating solution into the ultrasonic generator, turn on the ultrasonic generator and apply pulse current;

[0037] The pulse current refers to a duty ratio...

Embodiment 3

[0041] Such as image 3 As shown, this embodiment was prepared through the following steps:

[0042] The first step is to clean the platinum electrode and platinum wire auxiliary electrode;

[0043] The cleaning refers to ultrasonic cleaning.

[0044] Step 2: Put the platinum electrode to be electroplated and the platinum wire auxiliary electrode into the electroplating solution vertically, and connect the negative and positive electrodes of the power supply respectively;

[0045] The diameter of the platinum electrode to be electroplated is 400 μm, and the electrode spot width is 400 μm.

[0046] The electroplating solution refers to a solution obtained by dissolving 3 grams of chloroplatinic acid and 0.01 grams of lead acetate in 100 grams of water.

[0047] Step 3: Put the electroplating tank containing the electroplating solution into the ultrasonic generator, turn on the ultrasonic generator and apply pulse current;

[0048] The pulse current refers to a duty cycle of 5μs: 500μs and...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
widthaaaaaaaaaa
diameteraaaaaaaaaa
Login to View More

Abstract

The invention discloses a platinum black pulse plating method based on ultrasonic assistance and belongs to the field of biomedicine engineering technology. The method comprises the steps of: vertically putting an electrode to be platinized and a platinum wire auxiliary electrode into an electroplate liquid and respectively connecting with the positive pole and the negative pole of a power supply; then applying pulse current and starting an ultrasonic device at the same time; and finally turning off the power supply and the ultrasonic device, taking the platinized electrode out and washing with deionized water to obtain a platinum black plating layer attached to the platinized electrode. The platinum black obtained by the invention can obtain greatly reduced particle diameter and better bonding force between the plating layer and a microelectrode substrate and is not easy to fall off to cause failure of the electrode; in addition, the platinized microelectrode obtains greatly reduced AC impedance and greatly increased electrode charge injection capacity and charge storage capacity, which is beneficial to the reduction of embedded system power consumption and the improvement of electric stimulus effect.

Description

Technical field [0001] The invention relates to a platinum black electroplating method in the technical field of biomedical engineering, in particular to a platinum black pulse electroplating method based on ultrasound assistance. Background technique [0002] The various movements of the human body are controlled by the movement of muscles, and the muscles are controlled by nerves through neuroelectricity. When nerves have obstacles such as nerve severance, nerve atrophy, etc., and muscles cannot be controlled, the movement of a certain part of the body cannot be achieved. Due to the piezoelectric properties of muscles, at present, the use of implanted microelectrodes to directly electrically stimulate the nerve-controlled muscles can produce certain deformations of the muscles, thereby controlling the movements of certain parts of the human body. Its applications include orbicularis oculi muscle stimulation to treat inability to close eyes, facial muscle stimulation to treat f...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C25D5/18C25D5/20
Inventor 刘景全芮岳峰杨春生何庆
Owner SHANGHAI JIAO TONG UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com