Preparation method of polyurethane polymer dispersant for textile pigment printing paste

A polymer dispersant and paint printing technology, applied in textiles, papermaking, dyeing and other directions, can solve the problems such as polyurethane polymer dispersants that have not yet been seen, and achieve the effects of bright color, simple preparation method and high stability

Inactive Publication Date: 2011-12-14
DONGHUA UNIV
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] But so far, there are no related literature reports about polyurethane polymer dispersants for textile pigment printing pastes

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0033] (1) According to the NCO / OH molar ratio of 2, under the protection of nitrogen, add 71.35g HDI and 48.42g BPA (dissolved in 30g DMF) into a three-necked flask equipped with a stirrer, and heat up to 75°C for 60min;

[0034] (2) Cool down to 70°C, ① add 14.23g DMPA (26gDMF dissolved) dropwise, add 0.115g dibutyltin dilaurate after the dropwise addition, and perform chain extension reaction for 60min; heat up to 75°C, ② drop 7.11gDMPA (13gDMF dissolved) , carry out the chain extension reaction for 60min; ③ add 3.56gDMPA (7gDMF solution) dropwise, and carry out the second chain extension reaction for 60min; ) for capping, the reaction time is 120min, and the temperature is 75°C;

[0035] (3) Cool down to 50°C, slowly add 11.87g Na dissolved in 50ml water dropwise 2 CO 3 solution, while neutralizing and emulsifying until Na 2 CO 3 After adding all of it, add 100ml of water, raise the temperature to 60°C and continue stirring and emulsifying for 30min.

Embodiment 2

[0037] (1) According to the NCO / OH molar ratio of 2, under the protection of nitrogen, add 70.51g HDI and 47.85g BPA (dissolved in 30g DMF) into a three-necked flask equipped with a stirrer, and raise the temperature to 75°C for 60min;

[0038] (2) Cool down to 70°C, ① add 14.06g DMPA (dissolved in 26gDMF) dropwise, add 0.115g of dibutyltin dilaurate after the dropwise addition, and perform chain extension reaction for 60min; heat up to 75°C, ② add 7.03gDMPA (dissolved in 13gDMF) dropwise , chain extension reaction for 60 minutes; ③ dropwise adding 3.52g DMPA (7gDMF solution), chain extension reaction 60min; ④ dropwise adding 7.03gDMPA (13gDMF solution), capping reaction 120min, temperature 75°C;

[0039] (3) Cool down to 50°C, slowly add 12.51g Na2CO3 solution dissolved in 50ml of water dropwise, and emulsify while neutralizing, until all Na2CO3 is added, then add 50ml of water, heat up to 60°C and continue to stir and emulsify for 30min.

Embodiment 3

[0041] (1) According to the NCO / OH molar ratio of 2, under the protection of nitrogen, add 68.9g HDI and 46.75g BPA (dissolved in 30gDMF) into a three-necked flask equipped with a stirrer, and heat up to 75°C for 60min;

[0042](2) Cool down to 70°C, ① add 13.74g DMPA (dissolved in 26gDMF) dropwise, add 0.115g of dibutyltin dilaurate after the dropwise addition, and perform the chain extension reaction for 60min; raise the temperature to 75°C, ② add 6.87gDMPA (dissolved in 13gDMF) dropwise , chain extension reaction for 60 minutes; ③ dropwise adding 13.74g DMPA (26gDMF solution), capping reaction for 120min, temperature 75°C;

[0043] (3) Cool down to 50°C, slowly add 13.59g Na2CO3 solution dissolved in 50ml of water dropwise, and emulsify while neutralizing, until all Na2CO3 is added, then add 50ml of water, raise the temperature to 60°C and continue to stir and emulsify for 30min.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a preparation method of a polyurethane polymer dispersant for textile pigment printing paste, comprising: dissolving diisocyanate and hydrophilic carboxyl diol in an organic solvent, raising the temperature to 75°C for 60 minutes, and then dripping in batches Add small molecule dihydric alcohol solution, carry out multiple chain extension reactions, the reaction time is 60min, after the chain extension reaction is completed, carry out capping reaction for 120min; cool down to 50°C, add Na2CO3 solution dropwise, emulsify while neutralizing, dropwise add After completion, add water and heat up to 60°C and continue to stir and dissolve for 30 minutes to prepare a polyurethane polymer dispersant. The polymer dispersant of the present invention has strong affinity to the surface of pigment particles, is not easy to desorb, and has good anti-flocculation; and the preparation method is simple, low in cost, and environmentally friendly; the pigment paste prepared by using the dispersant is stable High, used in textile printing processing, can obtain high dry and wet rubbing fastness of printing.

Description

technical field [0001] The invention belongs to the field of preparation of polymer dispersants, in particular to a preparation method of polyurethane polymer dispersants for textile paint printing paste. Background technique [0002] In the textile pigment printing process, the color paste plays a role in adjusting the color; at the same time, the particle size and uniformity of the pigment play an important role in the fastness of the pigment printing. The production of paint color paste is the pulverization and dispersion process of organic pigments, that is, before the pigments are used, physical or chemical methods must be adopted to make the pigment particles finer, control the pigment particle size within the required particle size range, and achieve stable dispersion the goal of. [0003] The simplest and most effective method of pigment dispersion is ball milling. A dispersant must be added during the ball milling process. The dispersant is a surface active substan...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08G18/34C08L75/04D06P1/52
Inventor 闵洁刁正平葛媛李娜潘建君
Owner DONGHUA UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com