High-flow EPDM material and preparation method thereof

A high-flow, raw material technology, used in the field of high-flow EPDM materials and their preparation, can solve the problems of poor EPDM fluidity, unsuitable for direct injection molding, and dissatisfaction

Inactive Publication Date: 2012-05-30
SHANGHAI SUNNY
View PDF0 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] Due to its poor fluidity, the usual EPDM will have defects such as insufficient filling and a large number of shrinkage marks when it is directly injected, so it is not suitable for direct injection molding
However, the EPDM oil-extended glue on the market often exists in blocks. When using it, the glue must be cut into small particles to facilitate processing, which wastes a lot of manpower and material resources.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1~2

[0025] Embodiment 1~2 proportioning (weight %) sees Table 1.

[0026] Table 1

[0027] raw material name

Example 1

Example 2

Polypropylene

-

20

EPDM

78.7

58.7

SEBS

5

5

white oil

16

16

1010 / 168(1∶1)

0.3

0.3

[0028] Put all the components into the high mixer and mix them for 3-5 minutes, then add other raw materials and mix them for 3-5 minutes. The processing temperature is 190, 195, 215, 215, 215, 215, 215 ,, 210, 210 ° C, screw rotation at 300 rpm.

[0029] A kind of high flow EPDM material material obtained in the embodiment is compared in performance test, and the mechanical property is tested by ASTM.

Embodiment 1

[0030] Example 1 sample and Example 2 sample performance comparison table 2.

[0031] Table 2

[0032] Test items

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
melt flow indexaaaaaaaaaa
melt flow indexaaaaaaaaaa
melt flow indexaaaaaaaaaa
Login to View More

Abstract

The invention relates to a high-flow EPDM material and a preparation method thereof. The material is prepared from the following raw materials in percentage by weight: 0 to 30 percent of polypropylene; 40 to 80 percent of EPDM; 1 to 5 percent of compatilizer; 5 to 15 percent of SEBS; 5 to 30 percent of white oil; and 0.1 to 0.5 percent of antioxidant. The preparation method comprises the following steps: weighing the raw materials in percentage by weight; putting the SEBS and the white oil in a high mixing machine for uniformly mixing, then adding other raw materials into the mixture for mixing for 2 to 5 minutes, discharging the obtained product; and putting the raw materials which are uniformly mixed in a screw machine to carry out extrusion granulation. The method and the material are characterized in that: the prepared EPDM material is granules; not only the hardness can be adjusted, but also the fluidness is obviously superior to that of the common EPDM material; and the EPDM material prepared by the method has almost the same appearance and handfeel as the commercial grade EPDM material and can be directly injected into the finished product.

Description

technical field [0001] The invention relates to a high-fluidity EPDM material and a preparation method thereof. The material is a pellet, which can be directly injected into a product, and can be used for functional parts of tools, instruments, meters and the like. Background technique [0002] Due to its poor fluidity, ordinary EPDM will have defects such as insufficient filling and a large number of shrinkage marks when it is directly injected, so it is not suitable for direct injection molding. However, the EPDM oil-extended glue on the market often exists in blocks. When using it, the glue must be cut into small particles to facilitate processing, which wastes a lot of manpower and material resources. Therefore, the preparation of EPDM pellets with good fluidity has great market value. Contents of the invention [0003] The object of the present invention is to provide a high-flow EPDM material and a preparation method thereof in order to overcome the above-mentioned ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08L23/16C08K5/01C08K5/134C08K5/526B29B9/00B29C47/92C08L23/10C08L53/02B29C48/92
CPCB29C48/04B29C48/92B29C2948/9259B29C2948/92704B29C2948/92885B29C2948/92895
Inventor 杨涛郭建鹏陈晓东肖健
Owner SHANGHAI SUNNY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products