Novel ventilated slow-resilience sponge

A slow-rebound sponge and a new technology, applied in the field of slow-rebound sponge, can solve the problems of low air permeability and poor comfort, and achieve the effect of better comfort and improved air permeability.

Inactive Publication Date: 2010-05-19
JIANGSU HEALTHCARE TECH CO LTD
View PDF0 Cites 28 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Pore ​​opener or open cell silicone oil is used in the production process, the product has low air permeability and poor comfort

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0015] Based on 100 parts by weight of the mixture of polyether polyol and polymer polyol, add 33.5 parts of toluene diisocyanate, 0.8 part of polysiloxane polyether copolymer, 0.2 part of triethylene diamine solution, and 0.06 part of stannous octoate , 1.9 parts of foaming agent water. Among them, the above-mentioned polyether polyols are two kinds of Mn700 polyether polyols and Mn3000 polyether polyols, and the material ratios in 100 parts are respectively: 60 parts of Mn700 polyether polyols, 20 parts of Mn3000 polyether polyols, and Mn6000 polymers 20 parts of polyols.

[0016] The air-permeable slow-rebound sponge made from the above raw materials has a porosity of 95%. Press the sponge with your hands, and you can obviously feel the air circulation; blowing air from one side of the 40cm thick sponge, you can feel the airflow immediately on the other side.

Embodiment 2

[0018] Based on 100 parts of the mixture of two polyether polyols and polymer polyols, add 35.8 parts of toluene diisocyanate, 1 part of polysiloxane polyether copolymer, 0.16 parts of triethylenediamine solution, 0.08 parts of stannous octoate, and foam 2.2 parts of agent water. Among them, the above-mentioned polyether polyols are two kinds of Mn700 polyether polyols and Mn3000 polyether polyols, and the material ratios in 100 parts are respectively: 60 parts of Mn700 polyether polyols, 15 parts of Mn3000 polyether polyols, and Mn6000 polymer 25 parts of polyols.

[0019] The air-permeable slow-rebound sponge made from the above raw materials has a porosity of 97%. Press the sponge with your hands, you can obviously feel the air flow quickly, and you can hear the sound of air flow; blow air from one side of the 50cm thick sponge, and you can feel the air flow through the other side immediately; the human body lies flat on the sponge, No stuffy feeling.

Embodiment 3

[0021] Based on 100 parts of the mixture of two polyether polyols and polymer polyols, add 35.8 parts of toluene diisocyanate, 0.8 parts of polysiloxane polyether copolymer, 0.2 parts of triethylenediamine solution, 0.06 parts of stannous octoate, and foam 2.05 parts of potion water. Among them, the above-mentioned polyether polyols are two kinds of Mn700 polyether polyols and Mn3000 polyether polyols, and the material ratios in 100 parts are respectively: 65 parts of Mn700 polyether polyols, 30 parts of Mn3000 polyether polyols, and Mn6000 polymers 5 parts polyol.

[0022] The air-permeable slow-rebound sponge made of the above raw materials has a porosity of 98%. Press the sponge with your hands, you can obviously feel the air flow quickly, and you can hear the sound of air flow; blow air from one side of the 50cm thick sponge, and you can feel the air flow through the other side immediately; the human body is wrapped in the sponge, can Breathe freely.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention mainly discloses a novel ventilated slow-resilience sponge, in particular relates to a ventilated slow-resilience sponge which ensures the aperture ratio of a product by adjusting raw materials and the proportioning of a product, so that the aperture ratio of the product is improved to over 95 percent without using a pore-forming agent or pore-forming silicone oil, and the ventilation property of the product is improved. When the ventilated slow-resilience sponge is used, a human body contacts the product and obviously feels that the product is floppy; and the product is more comfortable after being used for a long time, particularly in muggy summer.

Description

technical field [0001] The invention relates to a slow-rebound sponge, in particular to an air-permeable slow-rebound sponge synthesized without using a pore-opening agent or silicone oil with an opening ratio greater than 70%. Background technique [0002] Since the slow rebound sponge was developed by the United States Space Development Agency in the 1950s, most of the products produced have a low opening rate, generally less than 70%. In the production process, cell opener or open cell silicone oil is used, and the product has low air permeability and poor comfort. Contents of the invention [0003] The main task of the present invention is to provide a novel air-permeable slow-rebound sponge, in particular to a product that does not use a cell-opening agent or silicone oil to increase the porosity of the product so as to improve the gas permeability of the product. [0004] In order to solve the above technical problems, the components and proportions of a novel breat...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C08L75/08C08L83/12C08G18/48C08G18/24C08G101/00
Inventor 倪张根林涛
Owner JIANGSU HEALTHCARE TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com