Water-based PU bright surface brush clear varnish for synthetic leather

A synthetic leather, water-based technology, used in fiber processing, textiles and papermaking, etc., can solve the problems of poor viscosity, stability, hand feel and other comprehensive effects, synthetic leather feel bad, easy to pollute the environment, etc. Color effect, low cost, strong operability effect

Inactive Publication Date: 2010-05-12
JIANGSU BAOZE POLYMER MATERIAL
View PDF0 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] 1. The organic solvent contained in the solvent-based oil mist surface treatment agent will cause the bottom layer of synthetic leather or artificial leather to dissolve, and the treated synthetic leather has a bad hand feeling and a single effect;
[0005] 2. The organic solvent contained in the solvent-based matte surface treatment agent not only has high cost, strong smell, and is easy to pollute the environment, but also has safety hazards such as flammability and explosion;
[0006] 3. Synthetic leather products prepared by solvent-based matte surface treatment agents have poor comprehensive effects such as viscosity, stability, and hand feel.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0024] 1. Water-based PU glossy varnish for synthetic leather consists of the following raw materials in parts by weight: 100 parts of water-based polyurethane resin (30% solid content), 150 parts of ordinary tap water, 2 parts of silicone defoamer, silicone leveling 2 doses.

[0025] 2. The preparation method of the water-based PU greasy feeling treatment agent for synthetic leather of the present invention is as follows:

[0026] ① Proportionally select 100 parts of water-based polyurethane resin, 2 parts of silicone defoamer, 2 parts of silicone leveling agent and 150 parts of ordinary tap water, mix and stir for 2 to 3 hours, and mix thoroughly;

[0027] ② Take the reaction mixture obtained in step ① and filter it through 200 meshes to obtain the water-based PU glossy varnish for synthetic leather.

[0028] 3. Experimentally detect the technical performance indicators of the PU glossy varnish prepared by 2. The specific experimental results are shown in Table 1:

[0029]...

Embodiment 2

[0032] 1. The water-based PU glossy varnish for synthetic leather is composed of the following raw materials in parts by weight: 90 parts of water-based polyurethane resin (30% solid content), 150 parts of ordinary tap water, 2 parts of silicone defoamer, silicone leveling 2 doses.

[0033] 2. The preparation method of the water-based PU bright surface varnish for synthetic leather of the present invention is as follows:

[0034] ① Proportionally select 90 parts of water-based polyurethane resin, 2 parts of silicone defoamer, 2 parts of silicone leveling agent and 150 parts of ordinary tap water, mix and stir for 2 to 3 hours, and mix thoroughly;

[0035] ② Take the reaction mixture obtained in step ① and filter it through 200 meshes to obtain the water-based PU glossy varnish for synthetic leather.

[0036] 3. Experimentally detect the technical performance indicators of the PU glossy varnish prepared by 2. The specific experimental results are shown in Table 2:

[0037] Ta...

Embodiment 3

[0040] 1. The water-based PU glossy varnish for synthetic leather is composed of the following raw materials in parts by weight: 80 parts of water-based polyurethane resin (30% solid content), 105 parts of ordinary tap water, 2 parts of silicone defoamer, and silicone leveling agent 2 doses.

[0041] 2. The preparation method of the water-based PU bright surface varnish for synthetic leather of the present invention is as follows:

[0042] ① Proportionally select 80 parts of water-based polyurethane resin, 2 parts of silicone defoamer, 2 parts of silicone leveling agent and 105 parts of ordinary tap water, mix and stir for 2 to 3 hours, and mix thoroughly;

[0043] ② Take the reaction mixture obtained in step ① and filter it through 200 meshes to obtain the water-based PU glossy varnish for synthetic leather.

[0044] 3. Experimentally detect the technical performance indicators of the PU glossy varnish prepared by 2. The specific experimental results are shown in Table 3:

...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a water-based PU bright surface brush clear varnish for synthetic leather, which comprises the following materials in parts by weight: 35 to 45 parts of water-based polyurethane resin, 50 to 65 parts of water, 0.5 to 1 part of organic silicon flatting agent, and 2 to 5 parts of organic silicon foam killer. The water-based PU bright surface brush clear varnish has the advantages that the mixture ratio of the component is scientific and reasonable, and the components are coordinated with each other and act together; the bright surface brush clear varnish has the advantages of good film reforming property, firm bonding, solvent resistance, hydrolysis resistance and thermosenescence resistance of coating; the finished product made of the synthetic leather, the surface of which is treated by the bright surface brush clear varnish, has the advantages that the original effect of the leather surface is not affected, the treated leather surface has unique slippery effect, and the synthetic leather has good comprehensive effects of good air permeability, good hand feel, water resistance, cohesiveness and the like.

Description

technical field [0001] The invention relates to a water-based PU glossy surface varnish for synthetic leather, in particular to a water-based PU glossy varnish for synthetic leather used in the post-process of synthetic leather. Background technique [0002] With the improvement of people's living standards, people are gradually pursuing high-quality daily products, and the demand for leather products is increasing. With the enhancement of animal protection awareness, animal leather can no longer meet people's needs. At present, synthetic leather products have gradually become a popular trend in the future. Synthetic leather has been widely used in the production of luggage, clothing, footwear and other products. The base fabric of PU leather is canvas PU material with good tensile strength. In addition to being coated on the base fabric In addition to the upper surface, the base fabric can also be included in the middle, so that the existence of the base fabric cannot be se...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): D06M15/564D06M13/50D06N3/14
Inventor 时云刚
Owner JIANGSU BAOZE POLYMER MATERIAL
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com