HT-02 type ship dressing coat

A HT-02, 1.HT-02 technology, applied in the field of HT-O2 marine dressing coating, can solve the problems of shortened service life, rust, etc., and achieve the effect of comfortable walking, soft surface and changeable colors

Inactive Publication Date: 2010-02-17
HUZHOU CITY HUICHENG MARINE COVERING
View PDF2 Cites 7 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] The deck of the cabin of the ship is made of steel, if it is not treated, it will lead to rust and other phenomena and shorten the service life

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • HT-02 type ship dressing coat

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0017] HT-O2 marine dressing coating is composed of epoxy resin, curing agent, wear-resistant filler and thinner. The ratio of each component is as follows in terms of weight ratio:

[0018] Specific dosage ratio

[0019] material name

Packing Specifications

Laying weight

Laying consumption

epoxy resin

13.5kg / drum

1116g

0.0827 barrels

Hardener

4.5kg / drum

372g

0.0827 barrels

[0020] Wear-resistant filler

20kg / bag

988g

0.0494 packs

Thinner

10kg / barrel

100g

0.01 barrel

[0021] In the above technical solution, the epoxy resin is produced by Shanghai Shengxing Resin Coating Co., Ltd.

[0022] The specific product models and technical indicators are as follows:

[0023] Product model name: H80-03 bright green epoxy floor paint (package)

[0024] Production batch number: 03092307, 2308 Executive standard: SXJS-03-009-052

[0025] Packing specification: A 13....

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
densityaaaaaaaaaa
Login to View More

Abstract

The invention discloses an HT-02 type ship dressing coat comprising the components of epoxide resin, a solidified agent, wearproof filler and a diluting agent, wherein the component proportion of theepoxide resin, the solidified agent and the wearproof filler is 2-4:1:2-5, and the proportion of the wearproof filler and the diluting agent is 8-10: 1. The HT-02 type ship dressing coat has the formula of the epoxide resin and the auxiliary materials of the wearproof filler and various addition agents, and the components are reasonably matched into a high-efficiency chemosetting self-leveling terrace coat. The HT-02 type ship dressing coat is coated on the surfaces of cement concrete, steel plates and wood to form a bright or honed terrace. The terrace is comfortable for walking, has soft surfaces, various colors and good adhesive force and resists skid, wear, water, acid and alkali and is suitable for industrial terraces, various ship desks, building floors and test locations with higherrequirements.

Description

technical field [0001] The invention relates to a HT-O2 type marine dressing coating. Background technique [0002] The deck of the cabin of the ship is made of steel, if it is not treated, it will lead to rust and other phenomena and shorten the service life. Contents of the invention [0003] The purpose of the present invention is to overcome the deficiencies in the prior art and provide a HT-O2 type marine dressing coating. Apply the marine dressing coating of the present invention on the surface of cement concrete, steel plate, and wood to form a bright or matte floor, which has the characteristics of comfortable walking, soft surface, changeable color, non-slip and wear-resistant, water-resistant, acid-alkali, and adhesion Good and other advantages. [0004] To achieve the above object, the present invention has taken the following technical solutions: [0005] HT-O2 marine dressing coating is composed of epoxy resin, curing agent, wear-resistant filler and thinne...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D163/00C09D7/12
Inventor 朱培新
Owner HUZHOU CITY HUICHENG MARINE COVERING
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com