Method for producing bird damage resistant silicon fluoride insulated sleeve

A technology for insulating sheaths and production methods, applied in the direction of insulators, insulators, organic insulators, etc., can solve problems such as loss, and achieve the effects of convenient application, excellent insulation performance, and high pollution flashover voltage resistance

Active Publication Date: 2009-12-02
NORTH CHINA ELECTRICAL POWER RES INST +2
View PDF0 Cites 11 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Bird damage tripping accidents in North China Power Grid and Northwest Power Grid have accounted for 8-12% of abnormal power outages, causing huge losses
The currently used technical measures such as anti-bird thorns and bird repellents cannot be completely solved, and potential hazards such as overlapping of foreign objects in complex living areas also require a high-insulation technical measure

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0015] The invention discloses a production method of bird-damaging fluorosilicone insulating sheath, which is composed of: 10-30% of fluorine-containing polydimethylsiloxane, 40-50% of vinyl-containing polydimethylsiloxane, Silica reinforcing filler 20-40%, electric corrosion resistance filler aluminum hydroxide 20-40%, vulcanizing agent 1-3%, anti-aging agent 0.5-1%, pigment 1-5%, and its preparation method is: 10-30% fluorine-containing polydimethylsiloxane, 40-50% vinyl-containing polydimethylsiloxane, 20-40% reinforcing filler silica, anti-corrosion filler hydrogen The mixture of alumina and 1-5% pigment is rolled in an internal mixer at 70-120°C and pressure ≤ 0.2Mpa for 1 hour, and 1-3% vulcanizing agent is added to the mixture rolled by the internal mixer And mix evenly, then put it on the open mill for rolling for 1 hour for mixing, and then re-mill the mixture containing vulcanizing agent mixed by the open mill, calender and extrude through the extrusion molding mach...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
lengthaaaaaaaaaa
dielectric strengthaaaaaaaaaa
mechanical strengthaaaaaaaaaa
Login to View More

Abstract

The invention discloses a method for producing a bird damage resistant silicon fluoride insulated sleeve. The production method comprises the following steps: roller-milling a mixture formed by 10 to 30 percent of fluorine containing dimethyl polysiloxan, 40 to 50 percent of ethylene containing dimethyl polysiloxan, 20 to 40 percent of reinforcing filler silicon dioxide and electrical erosion resistant filler aluminum hydroxide, and 1 to 5 percent of dye in a banbury mixer at a temperature of between 70 and 120 DEG C and under a pressure of less than or equal to 0.2Mpa for 1 hour; adding 1 to 3 percent of vulcanizer in the mixture roller-milled by the banbury mixer and evenly mixing; roller-milling the mixture in a roller mixer for 1 hour, and then milling the mixture; re-milling the vulcanizer containing mixture milled by the roller mixer; rolling-extruding the mixture by an extrusion forming machine for forming; and finally, two-stage vulcanizing the mixture in a vulcanizing furnace at a temperature of 180 DEG C for 2 hours to obtain the silicon fluoride insulated sleeve, cutting the silicon fluoride insulated sleeve into certain length, and sealing the tenon by a bonding agent when the sleeve is used. The invention is a method for producing a highly insulated bird damage resistant silicon fluoride insulated sleeve.

Description

technical field [0001] The invention relates to a fluorosilicone insulating sheath, in particular to a production method for a fluorosilicon insulating sheath used for preventing flashover and tripping of birds in high-voltage transmission lines. Background technique [0002] At present, power transmission and transformation lines have frequent tripping and blackout accidents caused by bird damage. In recent years, with the great development of the national electric power industry, the number of transmission lines has increased significantly. Bird damage tripping accidents in North China Power Grid and Northwest Power Grid have accounted for 8-12% of abnormal power outages, causing huge losses. The currently used technical measures such as anti-bird thorns and bird repellents cannot be completely solved, and potential hazards such as overlapping of foreign objects in complex living areas also require a high-insulation technical measure. Contents of the invention [0003] ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): H01B19/00H01B17/58H01B3/46C08L83/07C08K13/02C08K5/14
Inventor 陈原卢毅陈泓张跃男宋志强宋福如
Owner NORTH CHINA ELECTRICAL POWER RES INST
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products