Method for preparing ZSM-5 zeolite by in situ crystallization

A ZSM-5, in-situ crystallization technology, applied in chemical instruments and methods, crystalline aluminosilicate zeolite, borocarbane silicone crystalline aluminum silicate zeolite, etc., can solve the problem of low content of ZSM-5 zeolite, method Complicated, small pore area and micropore volume, etc., to achieve the effect of high zeolite content, increased micropore volume, and rich mesopores

Active Publication Date: 2010-12-22
CHINA PETROLEUM & CHEM CORP +1
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The method of preparing ZSM-5 zeolite by this method is relatively complicated, and the crystallization time is as long as 72 hours, and the content of ZSM-5 zeolite in the crystallized microspheres is low, and the micropore area and micropore volume are small

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method for preparing ZSM-5 zeolite by in situ crystallization
  • Method for preparing ZSM-5 zeolite by in situ crystallization
  • Method for preparing ZSM-5 zeolite by in situ crystallization

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0039] 1. Preparation of kaolin microspheres

[0040] Add kaolin, silica sol and water into a gel tank and mix homogeneously to obtain a kaolin slurry with a solid content of 30% by weight. The kaolin slurry is spray-dried to obtain kaolin microspheres with an average particle diameter of 50 μm. The kaolin microspheres are washed twice with decationized water of pH=2-4 at a mass ratio of 10:1 to the kaolin microspheres. The properties of raw materials are shown in Table 1, and the composition content of each component in the slurry is calculated on a dry basis in Table 2.

[0041] Table 1

[0042]

[0043] Table 2

[0044]

[0045] 2. Preparation of silica-rich clay microspheres

[0046] The silicon-rich clay is diatomaceous earth. In addition, diatomite, silica sol and water were added to another gel-forming tank and mixed homogeneously to obtain a silicon-rich clay slurry with a solid content of 60% by weight. The silicon-rich clay slurry was spray-dried to obtain ...

Embodiment 2

[0054] 1. Preparation of kaolin microspheres

[0055] Add kaolin, ZSM-5 zeolite seed crystals, silica sol and water into a gel tank and mix homogeneously to obtain a kaolin slurry with a solid content of 40% by weight. The kaolin slurry is spray-dried to obtain kaolin microspheres with an average particle diameter of 60 μm. The kaolin microspheres are washed twice with decationized water of pH=2-4 at a mass ratio of 10:1 to the kaolin microspheres. The properties of raw materials are shown in Table 1, and the composition content of each component in the slurry is calculated on a dry basis in Table 2.

[0056] 2. Preparation of silica-rich clay microspheres

[0057] The silicon-rich clay uses diatomaceous earth and pyrophyllite. In addition, diatomite, pyrophyllite, silica sol and water were added into another gel-forming tank and mixed homogeneously to obtain a silicon-rich clay slurry with a solid content of 50% by weight. The silicon-rich clay slurry was spray-dried to obt...

Embodiment 3

[0065] 1. Preparation of kaolin microspheres

[0066] Add kaolin, Y-type zeolite seed crystals, silica sol and water into a gel tank and mix homogeneously to obtain a kaolin slurry with a solid content of 30% by weight. The kaolin slurry is spray-dried to obtain kaolin microspheres with an average particle diameter of 80 μm. The kaolin microspheres are washed twice with decationized water of pH=2-4 at a mass ratio of 10:1 to the kaolin microspheres. The properties of raw materials are shown in Table 1, and the composition content of each component in the slurry is calculated on a dry basis in Table 2.

[0067] 2. Preparation of silica-rich clay microspheres

[0068] The silicon-rich clay is bentonite. Add bentonite, water glass and water to another gel-forming tank and mix homogeneously to obtain a silicon-rich clay slurry with a solid content of 30% by weight. Spray-dry the silicon-rich clay slurry to obtain a silicon-rich clay microparticle with an average particle diameter ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
diameteraaaaaaaaaa
diameteraaaaaaaaaa
Login to View More

Abstract

The invention relates to a method for preparing ZSM-5 zeolite through in-situ crystallization, which comprises that: kaolin slurry containing kaolin, adhesive and water is prepared into kaolin microspheres through spray drying, and the prepared kaolin microspheres are baked; silicon-enriched clay slurry containing silicon-enriched clay, adhesive and water is prepared into silicon-enriched clay microspheres through spray drying, and the prepared silicon-enriched clay microspheres are baked; and the respectively baked kaolin microspheres and silicon-enriched clay microspheres are mixed with a water solution containing alkali, and the mixture is subjected to in-situ hydrothermal crystallization to obtain crystallization product, wherein the mol ratio of SiO2 to Al2O3 in the silicon-enriched clay is more than 2. The ZSM-5 zeolite prepared by the method has high content of zeolite and rich middle holes, so the ZSM-5 zeolite can be used as a catalyst in the field of petrochemical industry.

Description

technical field [0001] The invention relates to a method for preparing ZSM-5 zeolite by in-situ crystallization. Background technique [0002] Since ZSM-5 zeolite was first reported by the Mobil Company of the United States (USP3702886) in 1972, due to the unique three-dimensional pore structure and shape-selective catalysis of ZSM-5 zeolite, it has high silicon-aluminum ratio and lipophilic and hydrophobic characteristics. Characterized by high stability and high catalytic activity, it is widely used as a catalyst in various methods. [0003] ZSM-5 zeolites have been shown to be particularly useful catalysts in reactions involving aromatic compounds, especially aromatic compounds having a single carbocyclic ring. Therefore, in the conversion reaction of olefins, naphthalene, alcohols, ethers and alkanes to aromatic compounds and in reactions such as isomerization, alkylation, dealkylation and transalkylation of aromatic compounds, ZSM-5 zeolite All exhibit unique selectiv...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B01J29/40C01B39/38C01B39/40
Inventor 潘晖华罗一斌王殿中慕旭宏蒋文斌舒兴田
Owner CHINA PETROLEUM & CHEM CORP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com