Solder wire material for stainless steel

A technology of stainless steel and welding wire, applied in welding/cutting medium/material, welding medium, welding equipment, etc., can solve the problems of poor weldability of stainless steel, uneven welding seam, difficulty in slag removal, etc., to achieve low cost, improve finish, reduce Effects of Stomatal Sensitivity

Inactive Publication Date: 2008-12-10
JIANGSU XINGHAI SPECIAL STEEL
View PDF0 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, due to the use of traditional welding wire materials such as ER308 after welding, the weld seam is not smooth, and there is a serious problem of difficult slag removal in the welding process, commonly known as "black skin", and the cost is high
Therefore, when traditional welding wire is used for welding, it is difficult to obtain the result of matching the properties of the weld metal and the base metal. It is still difficult to have welding wire materials that meet this requirement in the welding materials of the prior art, and are widely used in the industry. Stainless steel generally has the disadvantage of poor weldability

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0009] Embodiment 1: A welding wire material for stainless steel, the specific chemical composition weight % of the welding wire material is: C0.07; Si0.65; Mn6.7; P0.01; S0.005; Cr18.5; Ni8.0; Mo0.1; Re0.01; the balance is Fe and unavoidable impurities.

Embodiment 2

[0010] Embodiment 2: A welding wire material for stainless steel, the specific chemical composition weight % of the welding wire material is: C0.075; Si0.70; Mn6.9; P0.015; S0.01; Cr18.8; Ni8.3; Mo0.2; Re0.02; the balance is Fe and unavoidable impurities.

Embodiment 3

[0011] Embodiment 3: A kind of welding wire material for stainless steel, the specific chemical composition weight % of this welding wire material is: C0.08; Si0.8; Mn7.0; P0.015; S0.01; Cr19; Ni8.5; Mo0. 3; Re0.03; the balance is Fe and unavoidable impurities.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
Login to View More

Abstract

The invention discloses a welding wire material for stainless steels and the weight percentage of the concrete chemical compositions of the welding wire material is as follows: C, 0.07 to 0.09; Si, 0.65 to 0.95; Mn, 6.7 to 7.2; P, less than or equal to 0.02; S, less than or equal to 0.015; Cr, 18.5 to 19.5; Ni, 8.0 to 9.5; Mo, less than or equal to 0.4; the remaining is Fe and inevitable impurities. The welding wire material is used for 304 austenitic stainless steels, and welding seams are smooth after the welding is performed and metals at the welding seams have the similar performance as mother metal, no black skin exists and the cost is low.

Description

technical field [0001] The invention belongs to the material field of welding wire for metal material welding. In particular, it relates to welding wire materials for welding 304 austenitic stainless steel. Background technique [0002] Stainless steel is an alloy steel that adds chromium to steel to significantly improve corrosion resistance. According to its composition, it can be roughly divided into chromium series and chromium-nickel series. According to the metal structure, it can be divided into martensite, ferrite, austenite, There are 5 types of austenite-ferrite and precipitation hardening. Austenitic stainless steel (hereinafter referred to as "stainless steel") is a chromium-nickel system in terms of composition, and various steels developed by improving it. In the welding process of 304 austenitic stainless steel, in order to obtain the result of matching the strength of the weld metal with the strength of the base metal, it is necessary to add the necessary a...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): B23K35/30
Inventor 刘庄明黄明义刘庄庚邱爱华计建康
Owner JIANGSU XINGHAI SPECIAL STEEL
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com