Controllable solidifying type technologic clay sculpture material

Abstract

The invention relates to a controllable and cured type technique clay sculpture material, which adopts epoxy resin, PVC paste resin, talc powder and light calcium carbonate as raw materials. The raw materials are mixed evenly and then stirred into putty shape composition 1; curing agent, the PVC paste resin and the talc powder are mixed evenly and stirred into semi-transparent paste, in which the light calcium carbonate is added, thus obtaining composition 2. The two compositions are mixed evenly in accordance with a certain ratio, thus obtaining the controllable and cured type technique clay sculpture material. The invention is characterized in that: the invention not only has the plasticity (being moulded into different shapes randomly) of the traditional technique clay sculpture material (clay), but also has long storing time; besides, the cured time can be controlled (a plurality of hours or a plurality of days) under low temperature (below 0 DEG C); the invention is characterized by constructability, innocuity, adjustable hardness of products and extremely high impact resistance (being uneasy to be broken), etc. The invention is the technique clay sculpture material with excellent comprehensive property.

Description

technical field [0001] The invention relates to a controllable solidification type craft clay plastic material, which belongs to the field of material science. Background technique [0002] There are many kinds of clay sculpture artworks and a long history. It is a popular art form of our people and has strong local characteristics of China. Traditional clay plastic materials use soil as raw material, add additives, and adjust viscosity with water, which has the characteristics of low cost. However, due to the long drying time of traditional clay sculpture materials (usually several days or even longer), it is easy to cause deformation and collapse of the molded handicrafts, especially for large clay sculpture products. Moreover, traditional clay plastic materials use water as the medium and cannot be operated under low temperature conditions (freezing below 0°C), thus limiting their use. [0003] Synthetic materials have the advantages of high strength, strong aging resis...

AI Technical Summary

Problems solved by technology

However, due to the long drying time of traditional clay plastic materials (usually several days or even longer), it is easy to cause deformation and collapse of the molded handicrafts, especially for large clay sculpture products.

Moreover, traditional clay plastic materials use water as the medium and cannot be operated under low temperature conditions (freezing below 0°C), which limits its use.