Looking for breakthrough ideas for innovation challenges? Try Patsnap Eureka!

Polyurethane hard bubble composite material for vehicle and preparing method thereof

A polyurethane rigid foam combination material and technology for vehicles, applied in the field of foam materials, can solve the problems of difficult mixing, low temperature resistance, and destruction of the atmosphere, so as to extend the use temperature range and service life, and improve temperature resistance Effect

Inactive Publication Date: 2007-08-08
FUZHOU XIANGRONG POLYURETHANE PROD
View PDF0 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] Existing a kind of polyurethane rigid foam combination material is made up of polyether 4110, silicone oil (foam stabilizer), fluorodichloroethane (foaming agent 141B), catalyst, and this combination material product has the following disadvantages: (1 ) The temperature resistance is not high, and when the temperature is higher than 80 degrees Celsius, the foam body will expand and bubble and deform; (2) Due to the high viscosity of polyether 4110, it is difficult to stir and mix with other substances. Therefore, the existing combination material Only 1-fluorodichloroethane can be used as a blowing agent, and the use of 1-fluorodichloroethane as a blowing agent will not only destroy the atmosphere, but also cause damage to the environment, and the cost is relatively high

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0018] The specific embodiment of the present invention is described as follows:

[0019] (1) Polyurethane rigid foam combination material for vehicles is characterized in that: it comprises the raw material formula of following mass fraction ratio:

[0020] Polyether 4110 60-40 parts,

[0021] Polyether 350 40-60 parts,

[0022] 2 to 3 parts of foam stabilizer,

[0023] Foaming agent 2 to 5 parts,

[0024] Catalyst 6-10 parts.

[0025] The preferred raw materials for the above formula are: silicone oil is preferred as a foam stabilizer; water is preferred as a foaming agent; and the catalyst is an amine catalyst, preferably a triethylenediamine catalyst.

[0026] In the above combination material formula, with the gradual increase of the addition of polyether 350, the high temperature resistance of the product is gradually improved, the viscosity of the product is gradually reduced, and the hardness of the product is also gradually reduced, so it is necessary to ensure th...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a polyurethane hard bubble composite material and making method of car, which comprises the following parts: 40-60% polyether 4110, 40-60% polyether 350, 2-3% foam stabilizer, 2-5% foaming agent and 6-10% catalyst, wherein the materials are put into container to blend evenly to produce the product.

Description

technical field [0001] The invention relates to a foaming material for automobiles, in particular to a polyurethane rigid foam composite material for automobiles and a preparation method thereof, which can play the role of heat insulation and decoration. Background technique [0002] Existing a kind of polyurethane rigid foam combination material is made up of polyether 4110, silicone oil (foam stabilizer), fluorodichloroethane (foaming agent 141B), catalyst, and this combination material product has the following disadvantages: (1 ) The temperature resistance is not high, and when the temperature is higher than 80 degrees Celsius, the foam body will expand and bubble and deform; (2) Due to the high viscosity of polyether 4110, it is difficult to stir and mix with other substances. Therefore, the existing combination material Only 1-fluorodichloroethane can be used as the foaming agent, and the use of 1-fluorodichloroethane as the foaming agent will not only destroy the atmo...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C08G18/48C08G18/18C08L75/08C08G101/00C08L83/04
Inventor 刘增文
Owner FUZHOU XIANGRONG POLYURETHANE PROD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com