Gray coated glass and preparation method
A technology of coated glass and a manufacturing method, applied in the field of gray coated glass and its on-line manufacturing, can solve the problems of affecting the life of a melting furnace, large losses, and no online gray coating formula found.
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0033] Dissolve 5 grams of copper chloride in 500 grams of water to form an aqueous solution; add the surfactant used in the aqueous system; then dissolve a mixture of 95 grams of dipropionylmethylcobalt and manganese formylacetonate into 400 grams of dichloromethane , forming an organic solution; adding the organic solution to the above aqueous solution to form a spray solution.
[0034] Cut a 300mm×300mm white glass sample, wash it with detergent and deionized water in sequence, dry it, and put it in a high-temperature furnace. With the dry and purified compressed air as the carrier gas, driven by the carrier gas, the above-mentioned spraying solution is delivered to the hand-held Binks spray gun through the pipeline, and the spraying solution is sprayed onto the surface of the moving hot glass plate through the spray gun, and the moving hot glass The surface temperature of the plate was 580°C. The distance from the spray gun nozzle to the glass plate is 20cm, the delivery ...
Embodiment 2
[0043] The mixture of 15 grams of chromium formate and iron dipropionyl acetonate, the mixture of 135 grams of cobalt ammonium oxalate and manganese propionyl acetonate were dissolved in 850 grams of methylene chloride to form an organic solution, which was used as spray solution one.
[0044] A mixture of 13 grams of silicon tetrachloride and calcium chloride was dissolved in 87 grams of water to form an aqueous solution, which was used as spray solution two.
[0045] Cut a 300mm×300mm white glass sample, wash it with detergent and deionized water in sequence, and dry it, then put it in a high-temperature furnace, heat the glass plate to 530°C, and take it out. With the dry and purified compressed air as the carrier gas, driven by the carrier gas, the above-mentioned spraying solution 2 is transported to the hand-held Binks spray gun through the pipeline, and the spraying solution is sprayed onto the surface of the moving hot glass plate through the spray gun to form a dense l...
PUM
Property | Measurement | Unit |
---|---|---|
thickness | aaaaa | aaaaa |
thickness | aaaaa | aaaaa |
thickness | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com