High whiteness and strength adhesive short fiber and process for making same

A viscose staple fiber, strong technology, applied in the field of high white strength fine denier viscose staple fiber and its production technology, can solve the problem of poor wear resistance and repeated deformation resistance, ordinary yarn count, strength, whiteness Low and other problems, to achieve the effect of high cleanliness, high whiteness and comfortable wearing

Active Publication Date: 2008-01-02
唐山三友集团兴达化纤有限公司
View PDF7 Cites 14 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

It has 12 quality indicators, low strength and whiteness, poor cleanliness, low yarn strength, average yarn count, average quality, poor wear resistance and multiple deformation resistance, and can only be used for ordinary products. Production

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0022] A. Example of product raw materials

[0023] The cellulosic fibers of the present invention are the main substance of the present invention and are intended to be processed by spinning. The raw material components and weight percentage are: 86.7-92% of cellulose fiber, 7.7-13% of water and 0.15-0.30% of oil agent.

[0024] Raw material components and weight percent content embodiment:

[0025] 1. Cellulose fiber 86.7, water 13, oil agent 0.3.

[0026] 2. Cellulose fiber 92, water 7.7, oil agent 0.3.

[0027] 3. Cellulose fiber 88, water 11.85, oil agent 0.15.

[0028] 4. Cellulose fiber 90, water 9.8, oil 0.2.

[0029] The role of the three raw materials is:

[0030] Water, the fiber is naturally placed to regain moisture naturally, and it is impossible to be completely dry. When the fiber product is produced, it contains a certain amount of water to prevent static electricity.

[0031] Oil agent, textile processing has lubricating and antistatic effects, and make...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
whitenessaaaaaaaaaa
whitenessaaaaaaaaaa
elongation at breakaaaaaaaaaa
Login to View More

Abstract

A high whiteness and strength adhesive short fiber and a process for producing same belong to an adhesive short fiber of spinning industry but not a weaving industry, and a producing process thereof. Materials and respective percent content are: cellulose fiber 86.7-92%, water 7.7-13%, oil solution 0.15-0.30%. The material is produced to a product by dipping, pressing, etiolation, spinning, drafting, beaming, refining, oxydol secondary albifaction and drying. The product of the invention has fine denier, high strength, yarns of the product have high counts and high strength, thereby cloth face fabric has advantages of high strength, strong abradability, exquisite hand feeling, and pleat resistance and multi-deformation resistance higher than that of cloth face fabric machined by common adhesive short fiber and by a same process. The high counts product has thin cloth face fabric, light weight, area of a same weight mateiral machining face fabric in creased and cost is reduced.

Description

technical field [0001] The invention relates to a viscose staple fiber and a production method of the textile spinning industry and the non-woven fabric industry, in particular to a high white strength fine denier viscose staple fiber and a production process thereof. Background technique [0002] The development of ordinary viscose staple fiber has a history of about 100 years, and its quality index requirements and inspection methods can be found in GB / T14463-1993 "Viscose staple fiber" standard. Due to its quality index, it can only be mainly used in traditional textile spinning. It has 12 quality indicators, low strength and whiteness, poor cleanliness, low yarn strength, average yarn count, average quality, poor wear resistance and multiple deformation resistance, and can only be used for ordinary products. Production. Contents of the invention [0003] The object of the present invention is to provide a kind of viscose staple fiber with high white strength and fine...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): D01D1/02D01D5/06D01D10/06D01F2/06
Inventor 么志义李晓明张会平于捍江李方荣高孝义孙林东郑晓晨关绍宏
Owner 唐山三友集团兴达化纤有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com