Expansion type flame-proof smoke-suppressing soft polyvinyl chloride composition and its preparation method

A technology of soft polyvinyl chloride and polyvinyl chloride, which is applied in the field of polymers to achieve remarkable flame retardant effects, smoke suppression effects, and obvious effects

Active Publication Date: 2007-05-16
SHANGHAI RES INST OF CHEM IND
View PDF4 Cites 17 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

And there is no report about the research on intumescent flame-retardant flexible polyvinyl chloride.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0039] Combine 35 parts by weight of flame retardant B, 10 parts by weight of smoke suppressant D, 50 parts by weight of chlorinated polyethylene (CPE), 5 parts by weight of polyethylene wax, 2 parts by weight of silane coupling agent and 0.3 parts by weight Parts of non-ionic antistatic agent, etc. According to the weight ratio of the formula, the above raw materials are fully mixed in a high-speed mixer, extruded and granulated, and then mixed with 100 parts by weight of polyvinyl chloride resin, and extruded on a twin-screw extruder , Injection molding samples, test performance. The results are shown in Table 3.

Embodiment 2

[0041] Except that the ethylene-acrylic acid copolymer is substituted for chlorinated polyethylene, the remaining components and process conditions are the same as in Example 1. The obtained samples were tested, and the results are shown in Table 3.

Embodiment 3

[0043] Except that oxidized polyethylene is used instead of polyethylene wax, the other components and process conditions are the same as in Example 1. The obtained samples were tested, and the results are shown in Table 3.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a bulking-typed flame-proof smoke-resistant flexible-polychloroethylene composition and preparing method, which comprises the following parts: 100% polychloroethylene, 15-50% fire retardant, 3-25% smoke-resistant agent, 30-80% carrier resin, 0.1-20% dispersant, 0.1-10% coupler and 0.05-10% antistatic agent.

Description

Technical field [0001] The invention relates to a flame-retardant and smoke-inhibiting soft polyvinyl chloride composition and a preparation method thereof, belonging to the technical field of polymers, and in particular to an intumescent flame-retardant and smoke-inhibiting soft polyvinyl chloride composition and a preparation method thereof. Background technique [0002] Soft PVC has been widely used in various industries such as electronics, electrical appliances (wire and cable coating and insulation), construction, transportation, furniture and mining. As we all know, polyvinyl chloride resin itself has high flame retardancy, and its oxygen index (OI) can be higher than 45. However, as a soft PVC, a large amount of plasticizer is added in the processing process to improve the softness of the resin, so that the flame retardancy of the resin is greatly reduced, and it becomes a flammable material, which will spread when it catches fire. Chengda fire. In addition, the smoke ass...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C08L27/06C08K9/04C08K3/22C08K5/09C08K5/54C08L23/28C08L31/04C08L23/08
Inventor 郝冬梅刘彦明陈崇伟尹亮
Owner SHANGHAI RES INST OF CHEM IND
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products