Preparation method of petroleum resin

A technology of petroleum resin and resin, which is applied in the field of petroleum resin synthesis, can solve the problems of limited use of petroleum resin, dark color of resin products, affecting the application and development of domestic petroleum market, etc., and achieves easy control of properties and performance, high softening point, Effect of Narrow Molecular Weight Distribution

Active Publication Date: 2007-03-07
SINOPEC LANZHOU GASOLINEEUM CHEM IND CORP
View PDF5 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0007] Because the synthesis of existing petroleum resin mainly adopts C 5 、C 9 Distillation is used as raw material for cationic polymerization, and the obtained resin product has a dark color, which limits the use of petroleum resin and seriously affects the application and development of the domestic petroleum market.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0039] Embodiment 1, the ethylene cracking C that will contain diolefins, monoolefins 5 The distillate was subjected to Diels-Alder reaction at a temperature of 140°C and a pressure of 12.0 MPa for 9 hours, then cooled and discharged, and rectified to remove unreacted C 5 component, obtained as C 10 、C 15 、C 20 Be the mixing component of main component (the weight percentage of each composition in this mixing component is: C 10 75-99%, C 15 1~15%, C 20 0~3%, C 5 Fraction 0-1%); then the mixed component is dried to a water content of 100ppm, added to the reactor, heated to 90°C under stirring, and then added with 0.5% anhydrous aluminum chloride by weight of the mixed component, Polymerize at a temperature of 190°C and a pressure of 5 MPa for 24 hours to obtain a crude resin; add mineral oil to dilute the crude resin, wash and settle to obtain a crude resin solution, and distill the crude resin solution under reduced pressure to obtain a resin product. After measurement,...

Embodiment 2

[0040] Embodiment 2, the ethylene cracking C that will contain diolefins, monoolefins 5 The distillate was subjected to Diels-Alder reaction at a temperature of 220°C and a pressure of 6.0 MPa for 12 hours, then cooled and discharged, and rectified to remove unreacted C 5 component, obtained as C 10 、C 15 、C 20 Be the mixing component of main component (the weight percentage of each composition in this mixing component is: C 10 75-99%, C 15 1~15%, C 20 0~3%, C 5 Fraction 0-1%); then the mixed component is dried to a water content of 15ppm, added to the reactor, heated to 60°C under stirring, and then added with anhydrous aluminum trichloride of 2.5% by weight of the mixed component, Polymerize at a temperature of 150°C and a pressure of 3 MPa for 10 hours to obtain a crude resin; add naphtha to dilute the crude resin, wash and settle to obtain a crude resin solution, and distill the crude resin solution under reduced pressure to obtain a resin product. After measurement...

Embodiment 3

[0041] Embodiment 3, the ethylene cracking C that will contain diolefins, monoolefins 5 The distillate was subjected to a Diels-Alder reaction at a temperature of 300°C and a pressure of 1.0 MPa for 3 hours, then cooled and discharged, and rectified to remove unreacted C 5 component, obtained as C 10 、C 15 、C 20 Be the mixing component of main component (the weight percentage of each composition in this mixing component is: C 10 75-99%, C 15 1~15%, C 20 0~3%, C 5 Fraction 0-1%); then dry the mixed components until the water content is 200ppm, add to the reactor, heat to 75°C under stirring, then add anhydrous aluminum trichloride with 1.0% weight of the mixed components, Polymerize at a temperature of 100°C and a pressure of 0 MPa for 35 hours to obtain a crude resin; add n-pentane to dilute the crude resin, wash with water, and settle to obtain a crude resin solution, and distill the crude resin solution under reduced pressure to obtain a resin product. After measureme...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
softening pointaaaaaaaaaa
softening pointaaaaaaaaaa
molecular weight distributionaaaaaaaaaa
Login to view more

Abstract

The invention discloses a synthesizing method of oil resin, which comprises the following steps: adopting C10, C15, C20 as main component; drying; placing in the reactor; stirring; heating to 100-190 deg.c; adding 0.5-2.0% composition of anhydrous aluminium chloride as catalyst; polymerizing under 0-5Mpa for 10-35h to obtain rough resin; neutralizing rough resin; washing; sedimenting; decompressing; distilling.

Description

technical field [0001] The invention belongs to the field of chemical products, relates to a synthetic method of petroleum resin, in particular to a 10 、C 15 、C 20 A method of synthesizing petroleum resin with the mixed component as the main component as the raw material. Background technique [0002] Petroleum resin is produced by ethylene cracking by-product C 5 、C 9 Distillation is a chemical product obtained by polymerization of raw materials. C 5 Petroleum resin has excellent properties such as acid resistance, alkali resistance, and aging resistance, and is cheap, and can be widely used in adhesives, road marking paints, rubber additives, coatings, inks, etc. [0003] Petroleum resin is seldom used alone, usually mixed with other mixtures, it requires petroleum resin to have good compatibility, after being used in conjunction with other substances, it must have good water resistance, acid resistance, low melting point and good viscosity Compatibility. [0004] ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08F240/00
Inventor 毛兵李亮曹耀强王福善潘广勤张耀亨齐永新李光明许翠红杨晓晨
Owner SINOPEC LANZHOU GASOLINEEUM CHEM IND CORP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka