Looking for breakthrough ideas for innovation challenges? Try Patsnap Eureka!

Aqueous ink of white board pen

A pen ink, whiteboard technology, applied in ink, household appliances, applications, etc., can solve the problems of high price of chemical raw materials, irritating odor, high risk, etc., and achieve the effect of light and smooth writing and clear handwriting

Inactive Publication Date: 2006-12-27
张志刚
View PDF0 Cites 15 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] 1. When used, a large amount of volatile gas will be produced, which has a pungent smell and is highly toxic, which is harmful to human health
[0005] 2. The price of chemical raw materials used in solvent-based inks is relatively high, and the volatility of the solvent is extremely strong. The solvent loss in the process of production and use is large, resulting in a waste of energy
[0006] 3. The organic solvents used are highly volatile, flammable, and explosive dangerous chemical raw materials, which require strict management in production, storage, and transportation, and are very dangerous

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0035] Raw material composition:

[0036] NUOSPERSE 2008 9g Silica 20g

[0037] Light calcium carbonate 30g Zinc stearate 20g

[0038] Hectorite clay 1g Polyvinyl alcohol 5g

[0039] Sodium N-N-Oleoyl Methyl Taurate 35g Sodium Alkylbenzene Sulfonate 35g

[0040] Propylene Glycol 40g Lisol Red 10g

[0041] Ethylene glycol 10g SER-ADFA 379 5g

[0042] 780g of water.

[0043] Preparation:

[0044] Add polyvinyl alcohol into 60g of water, raise the temperature to 95°C, stir to dissolve completely; then add hectorite clay into 100g of water, stir to disperse evenly.

[0045] Take NUOSPERSE 2008, white carbon black, light calcium carbonate, and zinc stearate and add them to 620g of water, grind and disperse them for 40 minutes with a blue-type grinder at a speed of 1000-1200 rpm, then add the above-mentioned hectorite clay solution, poly Vinyl alcohol solution, sodium N-N-oleoylmethyl taurate, sodium alkylbenzene sulfonate, Lithor red pigment, ethylene glycol, propylene glyco...

Embodiment 2

[0047] Raw material composition:

[0048] NUOSPERSE FA 115 10g Silica 40g

[0049] Light calcium carbonate 25g Zinc stearate 15g

[0050] Hectorite clay 2g Polyvinyl alcohol 6g

[0051] Sodium N-N-Oleoyl Methyl Taurate 65g Ethylene Glycol 10g

[0052] Propylene Glycol 20g Glycerol 25g

[0053] SER-ADFA 379 5g Phthalocyanine Blue 8g

[0054] Water 769g.

[0055] Preparation:

[0056] Add polyvinyl alcohol into 100g of water, raise the temperature to 95°C, stir to dissolve completely; then add hectorite clay into 150g of water, stir to disperse evenly.

[0057] Take NUOSPERSE FA 115, white carbon black, light calcium carbonate, and zinc stearate and add them into 519g of water, grind and disperse them for 40 minutes at a speed of 1000-1200 rpm with a blue-type grinder, then add the above-mentioned hectorite clay solution, Polyvinyl alcohol solution, sodium N-N-oleoylmethyl taurate, phthalocyanine blue pigment, ethylene glycol, propylene glycol, glycerol, fungicide SER-ADF...

Embodiment 3

[0059] Raw material composition:

[0060] NUOSPERSE FA 607 8g Silica 45g

[0061] Light calcium carbonate 15g Zinc stearate 45g

[0062] Hectorite clay 2g Polyvinyl alcohol 8g

[0063] Sodium alkylbenzene sulfonate 75g Ethylene glycol 10g

[0064] Propylene Glycol 35g Glycerol 25g

[0065] SER-ADFA 379 5g Risol Scarlet 12g

[0066] 715g of water.

[0067] The preparation method is the same as above, and 1000 g of red water-based whiteboard pen ink is obtained.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates the aquosity ink, comprising dispersing agent, white carbon black, light calcium carbonate, detaching agent, colourant, and water. The invention has the advantages of innocuous, energy conservation and safety.

Description

technical field [0001] The invention relates to a water-based ink, in particular to a water-based ink specially used for whiteboard markers. Background technique [0002] Water-based ink has a history of many years, is a mature technology, and has a large number of literature reports. Generally speaking, water-based inks are composed of dyes, water-soluble organic solvents, additives (including stabilizers, wetting agents, color enhancers, water-resistant agents, etc.) The choice of additives varies. These water-based inks are all inks for writing on paper, do not have erasability, and are not suitable for blackboard writing pens. [0003] The whiteboard markers sold and used in the domestic and foreign markets all adopt solvent-based inks, mainly with ethanol, acetone, methyl alcohol or similar chemical raw materials as solvents. Solvent-based inks have the following disadvantages: [0004] 1. When used, it will produce a large amount of volatile gas, which has a pungen...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D11/16
Inventor 张志刚景富根
Owner 张志刚
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More