Art canvas with non-filler polyvinyl built coating and its production process

A technology of polyvinyl alcohol and polyvinyl alcohol solution, applied in the field of painting supplies, can solve problems such as affecting product performance and shelf life, unsatisfactory coating film compactness, easy yellowing of white coating, etc., to improve compactness , The effect of excellent surface performance and mechanical strength improvement

Inactive Publication Date: 2006-11-29
宋健 +2
View PDF0 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The defect of this white-coated art canvas is that the compactness of the coating film is not ideal, and back seepage and oil absorption are often prone to occur during painting; because it contains more solid powder without fillers, it is prone to cracking and cracking of the coating and flaking; white coating tends to yellow
These defects affect the performance and shelf life of the product

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0031] Embodiment one: the production process step of the embodiment of the present invention is as follows:

[0032] 1. Preparation of coating materials for bottom, middle and overcoat coatings:

[0033] Undercoat material: take polyvinyl alcohol solution: 40%, styrene-acrylate copolymer emulsion: 25%, vinyl acetate-ethylene copolymer emulsion: 10%, emulsifying wax: 0.05%, glycerin: 0.2%, sodium benzoate: 0.2%, water: 24.55%; first heat the polyvinyl alcohol solution to 75°C, add emulsifying wax and stir to mix evenly, then add styrene-acrylate copolymer emulsion, vinyl acetate-ethylene copolymer Mix the product emulsion evenly, then add glycerin, sodium benzoate, and water, stir and mix evenly at room temperature, and set aside.

[0034] Coating material for intermediate coating: polyvinyl alcohol solution: 45%, styrene-acrylate copolymer emulsion: 25%, vinyl acetate-ethylene copolymer emulsion: 5%, glycerin: 0.2%, sodium benzoate For: 0.2%, water: 24.6%; mix polyvinyl alc...

Embodiment 2

[0041] The production process step of the embodiment of the present invention is as follows:

[0042] 1. Preparation of coating materials for bottom, middle and overcoat coatings:

[0043] Undercoat material: take polyvinyl alcohol solution: 39.97%, styrene-acrylate copolymer emulsion: 17%, vinyl acetate-ethylene copolymer emulsion: 22%, emulsifying wax: 0.01%, glycerin: 0.01%, sodium benzoate: 0.01%, water: 30%; first heat the polyvinyl alcohol solution to 80°C, add emulsified wax and stir to mix evenly, then add styrene-acrylate copolymer emulsion, vinyl acetate-ethylene copolymer Mix the product emulsion evenly, then add glycerin, sodium benzoate, and water, stir and mix evenly at room temperature, and set aside.

[0044] Coating material for intermediate coating: polyvinyl alcohol solution: 30.98%, styrene-acrylate copolymer emulsion: 12%, vinyl acetate-ethylene copolymer emulsion: 22%, glycerin: 0.01%, sodium benzoate For: 0.01%, for water: 35%; mix polyvinyl alcohol so...

Embodiment 3

[0051] Production technology step of the present invention is as follows:

[0052] 1. Preparation of coating materials for bottom, middle and overcoat coatings:

[0053] Undercoat material: take polyvinyl alcohol solution: 48%, styrene-acrylate copolymer emulsion: 18%, vinyl acetate-ethylene copolymer emulsion: 5%, emulsifying wax: 0.1%, glycerin: 0.1%, sodium benzoate: 0.1%, water: 30%; first heat the polyvinyl alcohol solution to 85°C, add emulsified wax and stir to mix evenly, then add styrene-acrylate copolymer emulsion, vinyl acetate-ethylene copolymer Mix the product emulsion evenly, then add glycerin, sodium benzoate, and water, stir and mix evenly at room temperature, and set aside.

[0054] Coating material for intermediate coating: polyvinyl alcohol solution: 30.4%, styrene-acrylate copolymer emulsion: 19%, vinyl acetate-ethylene copolymer emulsion: 20%, glycerin: 0.3%, sodium benzoate 0.3%, water: 30%; mix polyvinyl alcohol solution, styrene-acrylate copolymer emu...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention relates to a no-filling material polyvinyl alcohol coating layer art canvas and the producing technology. It uses polyvinyl alcohol as main raw material to make bottom, middle and covering coating material. Coating bottom layer on the bottom canvas, drying; coating middle coating layers, drying; coating covering layers, drying; and the product would be gain. The invention improves the softness, compactness and mechanical strength of the coating film, and would not cause loose by the alteration of temperature and humidity.

Description

technical field [0001] The invention relates to a non-filler polyvinyl alcohol composite coated art oil painting cloth and its production process, specifically for painting artists, suitable for oil painting, acrylic painting, gouache painting, and can also be used for decoration and decoration. It belongs to the technical field of painting supplies. Background technique: [0002] Before the present invention was made, in prior art, artist's painting usually adopts traditional white coated canvas. It is mainly to apply white coating material directly on the base fabric. The white coating material adopts polymer emulsion such as polyvinyl alcohol, ethylene acetic acid homopolymer emulsion, styrene-acrylic ester copolymer emulsion and pure acrylate copolymer emulsion as one-component or two-component emulsion as coating base A large number of fillers such as titanium dioxide, lithopone, talcum powder, calcium carbonate, zinc oxide, etc. are mixed. Then apply the coating mat...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): D06N3/00B44D2/00
Inventor 宋健宋奇宋磊
Owner 宋健
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com