Substitution material in use for testing construction machinery for asphalt pavement, and its prodn. tech

A technology for asphalt pavement and construction machinery, which is applied in the field of substitute materials, and can solve the problems of flying mineral powder, waste of asphalt mixture, and the fact that the fluidity of dry material cannot fully and truly reflect the fluidity of hot asphalt mixture.

Inactive Publication Date: 2005-01-12
CHANGSHA UNIVERSITY OF SCIENCE AND TECHNOLOGY
View PDF0 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] (1) The hot asphalt mixture cannot be recycled, and the repeatability of the test is greatly limited
In addition, after the first experiment, the hot asphalt mixture becomes solid due to the temperature drop, and cannot be used in the second experiment, resulting in a lot of waste of asphalt mixture and greatly increasing the actual workload of the experiment (test After the completion, a large amount of solid asphalt mixture needs to be processed)
[0007] (2) Difficulty in temperature control
[0008] (3) The test site is

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0035] Example 1: Preparation of 135°C asphalt mixture (asphalt grade is Donghai brand AH-70, ore grading is AC-20I) test substitute material at room temperature (25°C).

[0036] The viscosity value of Donghai brand AH-70 bitumen at 135°C is 0.44Pa·s obtained from relevant standards. Therefore, 0.44Pa·s is taken as the target viscosity value.

[0037] Through the quasi-slump experiment on hot asphalt mixture at 135℃, the target slump value is 189mm.

[0038] According to the target viscosity value of 0.44Pa s, select a lubricating oil with the closest viscosity at 25°C, that is, select a medium-duty industrial valve with the code name N220 (that is, the ISO viscosity grade is 220) from GB 5903-1995. Type gear oil (ie L-CKC220). Actually, the lubricating oil selected may be any lubricating oil with a viscosity slightly less than 0.44 Pa·s.

[0039] Stir lubricating oil L-CKC220 and mineral material graded as AC-20I according to the oil-stone ratio of 3% to form a lubricating...

Embodiment 2

[0042] Embodiment 2: quasi-slump test.

[0043] 1. Purpose and scope of use:

[0044] 1) Measure the slump of the mixture to evaluate the workability of the mixture. If necessary, it can also be used to evaluate the change of workability of the mixture with the resting time of the mixture.

[0045] 2) It is suitable for plastic and fluid mixtures with the maximum particle size of the aggregate not exceeding 40mm and the slump of 10mm to 230mm.

[0046] 2. Instruments and equipment:

[0047] 1) Slump cylinder: made of iron sheet with a thickness of 2mm to 3mm, and the inner wall of the cylinder must be smooth;

[0048] 2) Two 300mm steel rulers, 40mm aperture sieve, charging funnel, trowel, small shovel, thermometer, etc.

[0049] 3. Experimental steps:

[0050] 1) Mix the mixture evenly. If the particle size of the aggregate exceeds 40mm, it should be removed by wet sieving, or it can be removed manually.

[0051] 2) Rinse the slump cylinder and keep it moist, put it on...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Viscosityaaaaaaaaaa
Particle sizeaaaaaaaaaa
Slumpaaaaaaaaaa
Login to view more

Abstract

This invention is a substitute materials used to the test machine for working on the pitch road surface, and its technology. This technology is: Collect mineral materials: use different proportion according to the degree of mineral pitch standard, and use the lubricating oil for different viscosity grade of mineral pitch according to different temperature standard, mix evenly both of mineral materials and lubricating oil according to the ratio of 2.5%-3.5%, to make up the mixture of lubricating oil. Under circumstances temp is 15deg.C-35deg.C, test the falling degree of intensity of the mixture materials, adjust the ratio of mineral materials and lubricated oil, to make the value of falling degree of intensity till it to practical using, then the substitute materials are formed.

Description

technical field [0001] The invention relates to a substitute material for asphalt pavement construction machinery test and its production process, in particular to hot asphalt mixture such as agitator of asphalt mixture mixing equipment, spiral agitator in transfer vehicle, and spiral distributor of paver Test substitute materials and production process of the contacted working device. Background technique [0002] Due to the many advantages of asphalt pavement, it has been widely used and is the development direction of high-grade highway pavement structure. However, the performance of the current asphalt pavement construction equipment and construction technology are not perfect enough, so that the completed asphalt pavement roads still have rework, the road life does not meet the design requirements, and premature water seepage, muddying, wrapping, rutting, cracking, and local pits Holes and other diseases; resulting in a large amount of asphalt pavement maintenance and ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C09K3/00E01C7/08
Inventor 李自光游张平何志勇李万莉朱福民颜荣庆周小峰
Owner CHANGSHA UNIVERSITY OF SCIENCE AND TECHNOLOGY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap