Austenitic stainless steels
What is Al technical title?
Al technical title is built by PatSnap Al team. It summarizes the technical point description of the patent document.
A kind of austenitic, stainless steel technology, applied in lighting and heating equipment, printing, heat exchange equipment and other directions, can solve the problems of broken into two parts, insufficient workability, rising and so on
Inactive Publication Date: 2004-10-27
NIPPON STEEL CORP
View PDF5 Cites 42 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
[0006] However, none of these steels have improved the hot workability very well, especially the workability at high temperatures above 1200°C
Generally, when using materials with poor thermal processing properties to manufacture jointless pipes, hot extrusion is often used to make pipes, but due to the heat generated by processing, the temperature inside the material will rise further relative to the heating temperature, so if it is above 1200°C Insufficient workability, will break in two or produce internal defects
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Examples
Experimental program
Comparison scheme
Effect test
Embodiment
[0103] In a high-frequency vacuum melting furnace, the steel having the chemical composition shown in Table 1 and Table 2 was melted to produce a 50 kg steel ingot with an outer diameter of 180 mm. In addition, 1 to 38 in the table are steels of the present invention, and A to O are comparative steels.
[0104] Minute
[0105] Note: "Al" refers to sol.Al (acid soluble Al)
[0106] Each of "P upper limit, "Al upper limit" and "O upper limit" is a value obtained from formula (1), formula (2) and formula (3).
[0107] Minute
[0108] Note: "Al" refers to sol.Al (acid soluble Al). Each of "P upper limit, "Al upper limit" and "O upper limit" is a value obtained from formula (1), formula (2) and formula (3).
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More
PUM
Property
Measurement
Unit
thickness
aaaaa
aaaaa
diameter
aaaaa
aaaaa
diameter
aaaaa
aaaaa
Login to View More
Abstract
An austenitic stainless steel excellent in high temperature strength, high temperature ductility and hot workability, consisting of, by mass %, C: more than 0.05% to 0.15%, Si: 2% or less, Mn: 0.1 to 3%, P: 0.04% or less, S: 0.01% or less, Cr: more than 20% to less than 28%, Ni: more than 15% to 55%, Cu: more than 2% to 6%, Nb: 0.1 to 0.8%, V: 0.02 to 1.5%, sol. Al: 0.001 to 0.1%, but sol.Al<=0.4xN, N: more than 0.05% to 0.3% and O (Oxygen): 0.006% or less, but O<=1 / (60xCu), and the balance Fe and impurities. The austenitic stainless steel may contain at least one of Co, Mo, W, Ti, B, Zr, Hf, Ta, Re, Ir, Pd, Pt and Ag, and / or at least one of Mg, Ca, Y, La, Ce, Nd and Sc.
Description
technical field [0001] The present invention relates to austenitic stainless steels used as steel pipes for power generation boilers, chemical industry equipment, etc., steel plates for heat-resistant and pressure-resistant parts, bar steel, forged steel products, etc., and particularly relates to creep strength, creep Austenitic stainless steel with excellent fracture ductility and hot workability. Background technique [0002] In the past, 18-8 series austenitic stainless steel such as SUS304H, SUS316H, SUS321H, SUS347H, etc. was used as the material of equipment used in boilers and chemical equipment used in high-temperature environments. However, in recent years, the operating conditions of devices in such a commercial temperature environment have become more and more harsh, and the requirements for the properties of materials used have also become stricter. Therefore, the high-temperature strength, especially the creep strength, of the previously used 18-8 series auste...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).
Invalid Date:Actual expiry date is based on effective date or publication date of legal transaction data of invalid patent.