Hardfacing alloy. methods and products

A hard alloy technology, applied in the field of surface hardened alloys, can solve the problems of small mechanical failures, and achieve the effects of excellent wear resistance, low friction coefficient, and excellent metal-to-metal wear resistance

Inactive Publication Date: 2006-11-22
ATT TECH LTD
View PDF9 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Although said materials have gained wide acceptance in the market, some users have expressed the need for an alloy for hardfacing of tool joints which has as little wear as possible and does not exhibit Weld cracks, to minimize the risk of mechanical failure performance

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Hardfacing alloy. methods and products
  • Hardfacing alloy. methods and products
  • Hardfacing alloy. methods and products

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0062] The preheating temperature is usually 100 to 400°C.

[0063] For tool joints of case-hardened AISI (American Iron and Steel Institute) 4137 steel, the preferred preheating temperature ranges are listed in Table 2 below.

[0064] Tool joint O.D.

[0065] * Tool joints of this size have much thinner wall thickness than standard tool joints.

Embodiment 2

[0067] For tool joints of case-hardened AISI 4145-HT steel, the preferred preheating temperature ranges are listed in Table 3 below.

[0068] Tool Joint / Drill Collar O.D.

[0069] * Tool joints of this size have much thinner wall thickness than standard tool joints.

Embodiment 3

[0071] For tool joints of case-hardened AISI 1340-HT steel, the preferred preheating temperature range is listed in Table 4 below

[0072] Tool joint O.D.

pre-heat temperature

Less than 4-3 / 4″

4-3 / 4″~6-1 / 8″

6-1 / 4″~7-1 / 4″

7-1 / 2″~7-3 / 4″

8″~8-1 / 2″(nom.)

8″~8-1 / 2″(w / 5″id.) *

150~200(66~93℃)

200~300(93~149℃)

300~400(149~204℃)

450~500(232~260℃)

600~700(316~371℃)

500~600(260~316℃)

[0073] * Tool joints of this size have much thinner wall thickness than standard tool joints.

[0074]Those of the preceding examples are representative preheat temperatures for those applications, used as examples of other preheat temperatures, depending on the size of the part to be hardfaced and the inherent properties of the matrix material, by simple Experiment OK.

[0075] The preheat temperature is preferably measured with a contact electronic pyrometer, although other temperature measurement methods...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
hardnessaaaaaaaaaa
Login to View More

Abstract

Disclosed is a hardfacing material capable of withstanding abrasion by siliceous formation particles, etc., weldable to industrial products such as drill joints and stabilizers for drilling oil and gas wells, and other industrial products without cracks alloy. The alloy for surface hardening has a low coefficient of friction and high wear resistance after welding without machining, and in the tool joint and stabilizer, the wear resistance of the tool joint and the stabilizer and the resulting casing are obtained Optimal balance between wear and tear. Other embodiments of the invention include welding hardfacing alloys (24) to the outer cylindrical surface (22) of casing and pin components of drill tool joints and welding Tool joints on stabilizing ribs of stabilizers and other industrial products; methods of manufacturing said hardfacing alloys; methods of applying said hardfacing alloys on surfaces, including preheating and post-welding treatment conditions, In order to resist wear and tear.

Description

field of invention [0001] The present invention relates to the field of hardfacing alloys having high wear resistance which can be used to increase the service life of surfaces of industrial products subject to wear, such as tool joints, drill collars used in drill strings for oil and gas drilling and stabilizers and other industrial products subject to wear and tear. Background of the invention [0002] Since nearly 95% of the surface layer of the earth's crust is composed of abrasive, siliceous materials that can cause significant wear on tool joints and stabilizer surfaces and other industrial products' abrasive surfaces, it is very important for drilling such as drilling in the earth's crust to produce There have been serious problems with oil or gas tool joints and stabilizer life. [0003] Attempts have therefore been made to provide protective hardfacing alloys suitable for welding on tool joints. For a description of prior art hardfacing for tool joints see U.S. Pa...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C21D1/70C21D9/22C21D9/08C22C38/22E21B17/00B23K9/04B23K35/30C22C38/00
CPCB23K35/308C22C38/22Y10T428/12972
Inventor R·A·达门
Owner ATT TECH LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com