Nano wave adsorption compound coating composition and its preparation and spraying method thereof

A technology of composite coatings and compositions, applied in the field of coatings, can solve the problems of limited promotion prospects, secondary electromagnetic pollution, etc., and achieve the effects of no secondary pollution, wide absorption frequency band, and high electromagnetic wave absorption rate

Inactive Publication Date: 2006-07-12
西安华捷科技发展有限责任公司
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Causes secondary electromagnetic pollution, and the prospect of promotion is restricted

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Nano wave adsorption compound coating composition and its preparation and spraying method thereof
  • Nano wave adsorption compound coating composition and its preparation and spraying method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0101] Process flow of the present invention, its steps are:

[0102] The first step, at first carry out the preparation of solvent composition 1, solvent composition is made up of methyl isobutyl ketone: ethylene glycol butyl ether: n-butanol=3.7: 2.3: 0.9 by mass ratio;

[0103] The second step, the preparation of resin solution 2:

[0104] The solvent composition and the resin form the resin solution, the mass ratio of which is solvent composition:resin=55%:45%. Add the resin to the solvent at a constant speed and slowly, heat and stir with a strong stirrer, and condense and reflux at 60°C for 30min , the resin solution should be uniform and transparent;

[0105] The 3rd step, the preparation of bottom carbon black spray composition 4: form bottom carbon black spray composition by resin solution, carbon black, its mass ratio is that the composition of 75%: 25% stirs and is mixed with bottom carbon black spray coating Solution, sealed for use;

[0106] The fourth step, th...

Embodiment 2

[0118] The first step, at first carry out the preparation of solvent composition 1:

[0119] The solvent composition is composed of methyl isobutyl ketone: ethylene glycol butyl ether: n-butanol=3.9: 2.1: 1.0 by mass ratio;

[0120] The second step, the preparation of resin solution 2:

[0121] The solvent composition and the resin form the resin solution, the mass ratio of which is solvent composition:resin=57%:43%. Add the resin to the solvent at a constant speed and slowly, heat and stir with a strong stirrer, and reflux at 65°C for 35min , the resin solution should be uniform and transparent;

[0122] The preparation of the 3rd step, bottom carbon black spray composition 4:

[0123] The bottom carbon black spray coating composition is composed of resin solution and carbon black, the mass ratio of which is 78%:22%, which is evenly stirred to prepare the bottom carbon black spray coating solution, which is sealed for use;

[0124] The fourth step, the preparation of surfa...

Embodiment 3

[0136] ① Preparation of solvent composition:

[0137] Weigh methyl isobutyl ketone according to the following mass ratio: ethylene glycol butyl ether: n-butanol=4.0: 2.2: 1.1 composition and stir to prepare solvent composition;

[0138] ② Preparation of resin solution:

[0139] The solvent composition and the resin form the resin solution, the mass ratio of which is solvent composition:resin=58%:42%. Add the resin to the solvent at a constant speed and slowly, heat and stir with a strong stirrer, and condense and reflux at 70°C for 45min , the resin solution should be uniform and transparent;

[0140] ③. Preparation of bottom carbon black spray composition:

[0141] Take by weighing resin solution by following mass ratio: carbon black=80%: the composition of 20% is stirred evenly and is mixed with bottom carbon black spray coating solution, seals up for use;

[0142] ④. Preparation of surface absorbing composite coating composition:

[0143] Take the resin solution by weig...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

A wave-absorbing composite nano-paint for military purpose, communication equipment, etc is prepared from methylisobutyl methanone, ethanediol butylether, n-butanol, resin, nano-silicon carbide, Ni nanoparticlels and carbon black through dissolving resin in solvent, preparing the bottom and surface wave-absorbing materials, mixing, stirring, and ball grinding. Its advantages are high absorptivity to electromagnetic waves, with bandwich, and low cost.

Description

technical field [0001] The invention relates to a coating, and is especially suitable for a composite nano wave-absorbing coating composition and a preparation and spraying method thereof. Background technique [0002] my country has invested a lot of manpower and funds in absorbing materials, and achieved certain results, but there is still a big gap between my country and foreign developed countries in the fields of military and aerospace, and there is an urgent need to solve the problem of absorbing materials with excellent performance. [0003] The research on absorbing materials has developed rapidly abroad. From the 1970s to 1980s, the United States, the former Soviet Union and other countries have invested a lot of energy in this research and achieved remarkable results. Since the 1990s, developed countries have also regarded their technology as a new technology with priority in their competitive strategy. [0004] The demand in the field of electromagnetic wave prot...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C09D5/32
Inventor 高建中
Owner 西安华捷科技发展有限责任公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com