Preparation method of automobile paint with high drying speed

A technology of drying speed and car, applied in the field of car paint, can solve the problems of low accuracy, high energy consumption, waste of manpower and material resources, etc., to save time, improve the proportioning speed, and improve production efficiency.

Inactive Publication Date: 2021-07-27
马玉国
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The drying condition of traditional automotive original paint is generally baked at 70°C for 50 minutes, which consumes a lot of energy, takes a long time to bake, and wastes manpower and material resources. Low cost and time-consuming and labor-intensive, it has been increasingly unable to meet the growing market demand for automotive paint, which has greatly restricted the rapid development of the domestic automotive industry.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method of automobile paint with high drying speed
  • Preparation method of automobile paint with high drying speed
  • Preparation method of automobile paint with high drying speed

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0028] Such as figure 1 As shown, a car paint with fast drying speed, the car paint includes a main agent and a curing agent, the raw materials of the main agent and the curing agent are respectively according to the volume content: main agent component: water-based epoxy resin 30 -55, pigment 15-35, anti-rust agent 1-5, anti-corrosion solvent 5-25, mica powder 5-10; curing agent components: ethylene glycol butyl ether 45-85, thickener 45-65; The volume ratio of the paint component and the curing agent component is 1-4:2.

[0029] Such as image 3 Shown, the invention discloses a kind of preparation method of automobile paint, and this method comprises the following steps:

[0030] A: Preparation of paint components:

[0031] (1) Transport 10-25 parts of water-based epoxy resin, 1-5 parts of anti-rust agent, 5-25 parts of anti-corrosion solvent, and 5-10 parts of mica powder into the mixing tank according to volume parts through a single delivery pump, and stir evenly .

...

Embodiment 2

[0043] A kind of preparation method of the car paint that drying speed is fast among the present invention comprises the following steps:

[0044] Start the controller, and set the number of parts of each component of the paint to be delivered through the controller. Each component of the paint is delivered independently through different single-part delivery pumps. The controller controls the stepping motor to start, and the stepping motor drives the drive shaft. 5 rotates, the drive shaft 5 drives the rotating cylinder 6 to rotate, and the conveying blade 8 on the rotating cylinder 6 is always in close contact with the inner wall of the housing 2 under the joint action of the elastic force of the spring 7, the gravity of the iron sand and the centrifugal force , the end of the conveying blade 8 is in sliding contact with the lower part of the housing 2 and maintains a sliding seal. An independent and airtight single-portion conveying space is formed between two adjacent conve...

Embodiment 3

[0051] A car paint with fast drying speed. The car paint includes a main agent and a curing agent. The raw materials of the main agent and the curing agent are respectively in parts by volume: main agent components: water-based epoxy resin 30-55, Pigment 15-35, anti-rust agent 1-5, anti-corrosion solvent 5-25, mica powder 5-10; curing agent components: ethylene glycol butyl ether 45-85, thickener 45-65; the paint The volume ratio of the component and the curing agent component is 1-4:2.

[0052] A preparation method for automobile paint, the method comprises the following steps:

[0053] A: Preparation of paint components:

[0054] (1) Transport 10-25 parts of water-based epoxy resin, 1-5 parts of anti-rust agent, 5-25 parts of anti-corrosion solvent, and 5-10 parts of mica powder into the mixing tank according to volume parts through a single delivery pump, and stir evenly ;

[0055] (2) Add 15-35 parts of pigment while stirring, and disperse at high speed in the mixing ta...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to a preparation method of an automobile paint with a high drying speed. The preparation method comprises the following steps: step A, preparing paint components; step B, preparing a curing agent component; and step C, preparing the automobile paint. Accurate matching of paint components is achieved through the single-part conveying pump, and the controller controls the stepping motor to complete conveying of accurate parts of paint components when a set value is reached through the counter and the controller, so that the matching of the paint components is accurately controlled, the matching speed is greatly increased, and the production efficiency is improved.

Description

technical field [0001] The invention relates to the technical field of car paint, in particular to a method for preparing a fast-drying car paint. Background technique [0002] Automobile paint occupies an increasingly important position in my country's paint production. The surface of automobiles needs to be protected and decorated by paint. The quality of paint film is an intuitive evaluation of automobile quality, which will directly affect the market competitiveness of automobiles. The development and changes of automobiles put forward high-quality, low-cost and green technology requirements for paints. It is imperative to further develop scratch-resistant, stone-resistant, corrosion-resistant, high-hardness, beautiful and colorful multifunctional automotive paints. [0003] The drying condition of traditional automotive original paint is generally baked at 70°C for 50 minutes, which consumes a lot of energy, takes a long time to bake, and wastes manpower and material re...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09D163/00C09D7/61C09D5/08C09D7/80
CPCC09D5/08C09D163/00C09D7/61C09D7/80C08K3/34
Inventor 马玉国
Owner 马玉国
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap