A kind of ceramic handicraft and preparation method thereof

A technology for ceramic handicrafts and lithium porcelain stone, which is applied in the field of ceramic products, can solve the problems of medium and low temperature ceramic color stagnation, low firing temperature and high water absorption, and achieve uniform and dense texture, lower firing temperature and low water absorption. Effect

Active Publication Date: 2022-08-05
福建省春秋陶瓷实业有限公司
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The firing temperature of medium and low temperature ceramics is low, so it consumes less energy, has low cost, and short firing time. However, medium and low temperature ceramics have the disadvantages of wood stagnation, rough porcelain, brittleness, and high water absorption.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of ceramic handicraft and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0036] A preparation of ceramic handicrafts, comprising the following steps:

[0037] S1. Green body preparation:

[0038] S11. Select the corresponding raw materials according to the green body formula, mix potassium feldspar, quartz, kaolin, wollastonite, lithium china stone, bentonite, talc, and alumina, and perform wet ball milling to pass through a 350-400 mesh sieve, and the sieve balance 0.2-0.4wt%;

[0039] S12. Then continue to add polymethyl methacrylate, calcium silicate, konjac glucomannan and lanthanum oxide, stir evenly to obtain a green body slurry, and the flow rate of the green body slurry is about 40 seconds;

[0040] S13. Shape the green body slurry to obtain a rough green body. After the appearance of the rough green body is trimmed, it is immersed in a sodium bicarbonate solution with a pH of about 8.0, and the temperature is raised to 60° C. for 25 minutes, and then taken out and air-dried to obtain a green body.

[0041] S2. Glazing: select the corresp...

Embodiment 2

[0047] A preparation of ceramic handicrafts, comprising the following steps:

[0048] S1. Green body preparation:

[0049] S11. Select the corresponding raw materials according to the green body formula, mix potassium feldspar, quartz, kaolin, wollastonite, lithium china stone, bentonite, talc, and alumina, and perform wet ball milling to pass through a 350-400 mesh sieve, and the sieve balance 0.4-0.6wt%;

[0050] S12. Then continue to add polymethyl methacrylate, calcium silicate, konjac glucomannan, and lanthanum oxide, stir evenly to obtain a green body slurry, and the flow rate of the green body slurry is about 45 seconds;

[0051] S13. Shape the green body slurry to obtain a rough green body. After the appearance of the rough green body is trimmed, it is immersed in a sodium carbonate solution with a pH of 8.5, and the temperature is raised to 65° C. for 20 minutes, and then taken out and air-dried to obtain a green body.

[0052] S2. Glazing: select the corresponding ...

Embodiment 3

[0058] A preparation of ceramic handicrafts, comprising the following steps:

[0059] S1. Green body preparation:

[0060] S11. Select the corresponding raw materials according to the green body formula, mix potassium feldspar, quartz, kaolin, wollastonite, lithium china stone, bentonite, talc, and alumina, and perform wet ball milling to pass through a 350-400 mesh sieve, and the sieve balance 0.2-0.3wt%;

[0061] S12. Then continue to add polymethyl methacrylate, calcium silicate, konjac glucomannan and lanthanum oxide, stir evenly to obtain green body slurry, and the flow rate of green body slurry is about 42 seconds;

[0062] S13. Shape the green body slurry to obtain a rough green body. After the appearance of the rough green body is trimmed, it is immersed in a sodium hydrogen phosphate solution with a pH of 8.2, and the temperature is raised to 62° C. for 22 minutes, and then taken out and air-dried to obtain a green body.

[0063] S2. Glazing: select the correspondin...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
Login to View More

Abstract

The invention discloses a ceramic handicraft, comprising a green body and a glaze layer. The green body is prepared from the following raw materials: 35-40 parts of potassium feldspar, 25-30 parts of quartz, 10-15 parts of kaolin, and 10-15 parts of wollastonite. parts, 8-12 parts of lithium porcelain stone, 8-12 parts of bentonite, 7-10 parts of calcium silicate, 6-8 parts of talc, 5-8 parts of alumina, 3-6 parts of polymethyl methacrylate, konjac grape 3-6 parts of mannan, 1-2 parts of lanthanum oxide; the glaze layer is made from the following raw materials: 25-30 parts of quartz, 10-15 parts of albite, 10-15 parts of potassium feldspar, and 15-20 parts of kaolin , 10-15 parts of diatomaceous earth, 8-12 parts of zirconium silicate, 5-8 parts of magnesium sulfate, 5-8 parts of zinc oxide, 3-5 parts of boron oxide, and 1-4 parts of coloring agent. The invention can reduce the firing temperature by optimizing the raw material component selection and content ratio of the green body and the glaze layer, and meanwhile, the ceramic products have uniform and dense texture, low water absorption rate, smooth and uniform surface of the glaze layer, and beautiful appearance.

Description

technical field [0001] The invention belongs to the technical field of ceramic products, in particular to a ceramic handicraft and a preparation method thereof. Background technique [0002] Ceramics is a general term for pottery and porcelain, and the existence of pottery was discovered as early as about 8000-2000 BC (Neolithic Age). Ceramic materials are mostly oxides, nitrides, borides and carbides. Common ceramic raw materials include clay, alumina, kaolin, etc. Since the main raw materials of ceramics are silicate minerals from nature, they belong to the same "silicate industry" as glass, cement, enamel, refractory and other industrial fields. category. The formed ceramic products generally have high hardness, but poor plasticity. In addition to the use of food utensils, utensils and decorations, ceramic products also play an important role in the development of electronic science. The preparation process of ceramics is mostly made by crushing, mixing, molding and c...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C04B35/19C04B35/622C04B35/64C04B35/636C04B41/86C03C8/00C03C1/04
CPCC04B35/19C04B35/622C04B35/64C04B35/636C04B41/86C04B41/5022C03C8/00C03C1/04C04B2235/3418C04B2235/349C04B2235/3454C04B2235/3203C04B2235/3217C04B2235/3227C04B2235/656C04B2235/6567C04B41/4539C04B41/4578C04B41/0072
Inventor 徐昌毅
Owner 福建省春秋陶瓷实业有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products