A kind of sulfur-vacancy nitrogen-doped carbon-coated nickel sulfide composite electrode material and its preparation method

A nitrogen-doped carbon and composite electrode technology, which is applied in the preparation/purification of nickel sulfide, carbon, negative electrodes, etc., can solve the problems of complex process, difficult large-scale industrial production, low production efficiency, etc., and achieve the goal of improving interstitial diffusion Effect

Active Publication Date: 2022-05-17
HUAIYIN INSTITUTE OF TECHNOLOGY
View PDF22 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, these technologies generally have disadvantages such as low preparation efficiency, complicated process, and difficulty in large-scale industrial preparation.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of sulfur-vacancy nitrogen-doped carbon-coated nickel sulfide composite electrode material and its preparation method
  • A kind of sulfur-vacancy nitrogen-doped carbon-coated nickel sulfide composite electrode material and its preparation method
  • A kind of sulfur-vacancy nitrogen-doped carbon-coated nickel sulfide composite electrode material and its preparation method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0032] The preparation method of the sulfur-vacancy nitrogen-doped carbon-coated nickel sulfide composite electrode material of the present invention comprises the following steps in sequence:

[0033] S1: Dissolve 5mmol of nickel acetate in 20mL of deionized water to obtain a nickel acetate solution; dissolve 5mmol of hexamethylenetetramine in 20mL of ethanol to obtain a hexamethylenetetramine solution;

[0034] S2: Mix the nickel acetate solution and the hexamethylenetetramine solution uniformly by dropping, and then stand and grow at 100° C. for 20 hours to obtain the primary product containing the nickel-based metal organic framework template;

[0035] S3: centrifuge the primary product containing the nickel-based metal organic framework template, wash with deionized water and absolute ethanol three times respectively, to obtain a clean nickel-based metal organic framework template; figure 1 As shown, the nickel-based metal-organic framework template prepared in Example 1 ...

Embodiment 2

[0039] The preparation method of the sulfur-vacancy nitrogen-doped carbon-coated nickel sulfide composite electrode material of the present invention comprises the following steps in sequence:

[0040] S1: Dissolve 10mmol of nickel nitrate in 40mL of deionized water to obtain a nickel acetate solution; dissolve 30mmol of hexamethylenetetramine in 40mL of methanol to obtain a hexamethylenetetramine solution;

[0041] S2: The nickel nitrate solution and the hexamethylenetetramine solution were mixed uniformly by dropping, and then left to grow at 80° C. for 24 hours to obtain the primary product containing the nickel-based metal organic framework template;

[0042] S3: centrifuge the primary product containing the nickel-based metal-organic framework template, wash it with deionized water and absolute ethanol three times respectively, and obtain a clean nickel-based metal-organic framework template;

[0043] S4: After mixing the clean nickel-based metal-organic framework template ...

Embodiment 3

[0046] The preparation method of the sulfur-vacancy nitrogen-doped carbon-coated nickel sulfide composite electrode material of the present invention comprises the following steps in sequence:

[0047] S1: Dissolve 10mmol of nickel chloride in 50mL of deionized water to obtain a nickel acetate solution; dissolve 70mmol of hexamethylenetetramine in 100mL of acetone to obtain a hexamethylenetetramine solution;

[0048] S2: Mix the nickel chloride solution and the hexamethylenetetramine solution uniformly by dropping, and then stand and grow at 150° C. for 15 hours to obtain the primary product containing the nickel-based metal-organic framework template;

[0049] S3: centrifuge the primary product containing the nickel-based metal-organic framework template, wash it with deionized water and absolute ethanol three times respectively, and obtain a clean nickel-based metal-organic framework template;

[0050] S4: After mixing the clean nickel-based metal-organic framework template ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
Login to View More

Abstract

The invention relates to a sulfur-vacancy nitrogen-doped carbon-coated nickel sulfide composite electrode material and a preparation method thereof, comprising the following steps in sequence, S1: mixing inorganic nickel salt and hexamethylenetetramine according to a molar ratio of 1:(1-7 ) were dissolved in the solvent respectively to obtain inorganic nickel salt solution and hexamethylenetetramine solution; S2: mix the inorganic nickel salt solution and hexamethylenetetramine solution uniformly by dropping, and then Leave to grow for 12-50h to obtain the primary product containing the nickel-based metal-organic framework template; S3: centrifuge at 2000-4000r / min to separate the primary product containing the nickel-based metal-organic framework template, wash with deionized water and absolute ethanol for 3 Once, a clean Ni-based metal-organic framework template was obtained. The composite electrode material prepared by the invention has high energy storage specific capacity, good cycle stability, simple preparation method and low cost, and is easy to realize industrial scale application.

Description

technical field [0001] The invention relates to a sulfur-vacancy nitrogen-doped carbon-coated nickel sulfide composite electrode material, and also relates to the use of nitrogen-doped carbon-doped carbon-coated sulfur-vacancy composite electrode material to prepare circular electrodes for sodium-ion batteries, belonging to the sodium-ion battery negative electrode material technology field. Background technique [0002] Due to the excessive consumption of non-renewable energy, it is imperative to rationally develop and utilize renewable clean energy such as wind energy, solar energy, and geothermal energy. However, all kinds of renewable energy are restricted by geographical and environmental factors, and there are serious randomness and intermittency. Therefore, it is very important to realize the optimal management and large-scale storage of energy. Lithium-ion batteries have been the mainstream in the field of energy storage since they were commercialized, which greatl...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): H01M4/36H01M4/58H01M4/62H01M10/054C01B32/05C01G53/11
CPCH01M4/366H01M4/5815H01M4/625H01M4/628H01M10/054C01G53/11C01B32/05H01M2004/021H01M2004/027Y02E60/10
Inventor 高晓艳张孝杰李东洪坤张强华潘颖韬桂应梅李明鲜吉华玉
Owner HUAIYIN INSTITUTE OF TECHNOLOGY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com