Antibacterial fabric as well as preparation method and application thereof

A technology of antibacterial fabrics and antibacterial materials, applied in textiles and papermaking, fiber types, fiber treatment, etc., can solve the problems of poor antibacterial effect, poor antibacterial durability, narrow application range, etc., and achieve good antibacterial and antiviral effects and antibacterial properties Better, good anti-virus effect

Active Publication Date: 2021-04-20
同曦集团有限公司
View PDF9 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the fiber raw materials of this fabric are all natural fibers, and the wear resistance is poor, so it is not suitable for products that require fabric wear resistance, and the application range is narrow
[0006]At present, most of the existing antibacterial fabrics have the problems of poor antibacterial effect, poor antibacterial durability and relatively single function

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Antibacterial fabric as well as preparation method and application thereof
  • Antibacterial fabric as well as preparation method and application thereof
  • Antibacterial fabric as well as preparation method and application thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0113] This embodiment provides an antibacterial fabric, which includes an antibacterial and wear-resistant layer, an antibacterial base cloth, and an antibacterial waterproof layer stacked in sequence.

[0114] In this embodiment, the components and parts by weight of the antibacterial fiber filaments, antibacterial wear-resistant coating, antibacterial waterproof coating and antibacterial finishing solution are shown in Table 1.

[0115] Table 1

[0116]

[0117]

[0118]

[0119] The preparation method of antibacterial fabric described in the present embodiment comprises the following steps:

[0120] (1) Mix high polymer, plasticizer and photocatalytic antibacterial material, melt and spin at 250°C to make antibacterial fiber filaments, and then weave the antibacterial fiber filaments into base fabric;

[0121] (2) Mix nano-silver, nano-zinc oxide, erbium-doped nano-titanium dioxide, silane coupling agent, dispersant and deionized water, heat to 80°C, ultrasonic e...

Embodiment 2

[0127] This embodiment provides an antibacterial fabric, which includes an antibacterial and wear-resistant layer, an antibacterial base cloth, and an antibacterial waterproof layer stacked in sequence.

[0128] In this embodiment, the components and parts by weight of the antibacterial fiber filaments, antibacterial wear-resistant coating, antibacterial waterproof coating and antibacterial finishing solution are shown in Table 2.

[0129] Table 2

[0130]

[0131]

[0132] The preparation method of antibacterial fabric described in the present embodiment comprises the following steps:

[0133] (1) Mix high polymer, plasticizer and photocatalytic antibacterial material, melt and spin at 270°C to make antibacterial fiber silk, and then weave the antibacterial fiber silk into base fabric;

[0134] (2) Mix nano-silver, nano-zinc oxide, erbium-doped nano-titanium dioxide, silane coupling agent, dispersant and deionized water, heat to 100°C, ultrasonic emulsify at constant t...

Embodiment 3

[0140] This embodiment provides an antibacterial fabric, which includes an antibacterial and wear-resistant layer, an antibacterial base cloth, and an antibacterial waterproof layer stacked in sequence.

[0141] In this embodiment, the components and parts by weight of the antibacterial fiber filaments, antibacterial wear-resistant coating, antibacterial waterproof coating and antibacterial finishing solution are shown in Table 3.

[0142] table 3

[0143]

[0144]

[0145]

[0146] The preparation method of antibacterial fabric described in the present embodiment comprises the following steps:

[0147] (1) Mix high polymer, plasticizer and photocatalytic antibacterial material, melt and spin at 260°C to make antibacterial fiber silk, and then weave the antibacterial fiber silk into base fabric;

[0148] (2) Mix nano-silver, nano-zinc oxide, erbium-doped nano-titanium dioxide, silane coupling agent, dispersant and deionized water, heat to 90°C, ultrasonic emulsify fo...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
antibacterial rateaaaaaaaaaa
antibacterial rateaaaaaaaaaa
antibacterial rateaaaaaaaaaa
Login to View More

Abstract

The invention provides an antibacterial fabric as well as a preparation method and application thereof. The antibacterial fabric comprises an antibacterial and wear-resistant layer, antibacterial base cloth and an antibacterial and waterproof layer which are sequentially laminated. The preparation method comprises the following steps of spinning antibacterial fiber yarns into base cloth, putting the base cloth into an antibacterial mixed solution containing antibacterial finishing liquid and fabric finishing liquid, and performing padding and drying to obtain the antibacterial base cloth; and preparing antibacterial and wear-resistant paint from raw materials of the antibacterial and wear-resistant layer, preparing antibacterial and waterproof paint from preparation raw materials of the antibacterial and waterproof layer, and spraying the antibacterial and wear-resistant paint and the antibacterial and waterproof paint to two sides of the antibacterial base cloth respectively to obtain the antibacterial fabric. The three layers of structures of the antibacterial fabric all have the antibacterial effects, the overall antibacterial performance of the fabric is achieved, the waterproof and self-cleaning functions are achieved, and the strength of the fabric is relatively high, so that the fabric is suitable for preparation of luggage fabrics; and the preparation process is scientific and efficient, and the application value is extremely high.

Description

technical field [0001] The invention belongs to the technical field of luggage fabrics, and in particular relates to an antibacterial fabric and its preparation method and application. Background technique [0002] With the advancement of science and technology, people have higher and higher requirements for luggage fabrics. At present, the improvement of luggage fabrics mainly focuses on the improvement of physical properties of fabrics, such as improving the wear resistance and comfort of fabrics, but the multifunctionality of fabrics There are relatively few improvements. [0003] In the prior art, most luggage fabrics are prepared by textile technology. The porous shape of textile fabrics and the chemical structure of high molecular polymers in textile raw materials are conducive to the attachment and reproduction of microorganisms, polluting fibers and causing adverse effects on human health. . Antibacterial fabrics can keep fabrics hygienic, prevent bacteria and othe...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): D06M15/564D06M15/248D06M11/48D06M11/83D06M11/44D06M11/46D06M15/03D06M101/32
Inventor 陈广川于红光吴新磊
Owner 同曦集团有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com